Blended yarn spinning method
A technology of blended yarn and blended yarn, applied in the field of spinning, can solve the problems of easy generation of static electricity, uneven cashmere, affecting the wearing performance of clothing, etc., and achieve the effect of increasing twist, reducing damage and falling down.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] A method for spinning blended yarns. The blended yarns are composed of cashmere, synthetic fibers and viscose fibers. The spinning is completed through the steps of manual mixing, cleaning, carding, drawing and roving. The specific spinning steps are as follows:
[0018] The first step is the selection of raw materials: the mass ratio of cashmere to blended yarn is 4%, the mass ratio of synthetic fiber to blended yarn is 25%, and the mass ratio of viscose fiber to blended yarn is 61%;
[0019] The second step is manual mixing: the cashmere and viscose fiber, viscose fiber and synthetic fiber are mixed by hand;
[0020] The third step, carding: In the carding process, use the FA201 carding machine, set the speed of the cylinder in the carding machine at 240r / min, the speed of the licker-in roller at 760r / min, and the speed of the cover plate at 72.3 mm / min; the doffer speed is controlled at 20r / min, and the five-point spacing between the cylinder and the cover plate is 0...
Embodiment 2
[0025] A method for spinning blended yarns. The blended yarns are composed of cashmere, synthetic fibers and viscose fibers. The spinning is completed through the steps of manual mixing, cleaning, carding, drawing and roving. The specific spinning steps are as follows:
[0026] The first step is the selection of raw materials: the mass ratio of cashmere to blended yarn is 10%, the mass ratio of synthetic fiber to blended yarn is 30%, and the mass ratio of viscose fiber to blended yarn is 60%;
[0027] The second step is manual mixing: the cashmere and viscose fiber, viscose fiber and synthetic fiber are mixed by hand;
[0028] The third step, carding: in the carding process, use the FA201 carding machine, set the speed of the cylinder in the carding machine at 330r / min, the speed of the licker-in roller at 820r / min, and the speed of the cover plate at 100mm / min; the doffer speed is controlled at 28r / min, and the five-point distance between the cylinder and the cover plate is ...
Embodiment 3
[0033] A method for spinning blended yarns. The blended yarns are composed of cashmere, synthetic fibers and viscose fibers. The spinning is completed through the steps of manual mixing, cleaning, carding, drawing and roving. The specific spinning steps are as follows:
[0034] The first step, the selection of raw material: the mass ratio of cashmere accounting for blended yarn is 7%, the mass ratio of synthetic fiber accounting for blended yarn is 26%, and the mass ratio of viscose fiber accounting for blended yarn is 67%;
[0035] The second step is manual mixing: the cashmere and viscose fiber, viscose fiber and synthetic fiber are mixed by hand;
[0036] The third step, carding: in the carding process, use the FA201 carding machine, set the speed of the cylinder in the carding machine at 290r / min, the speed of the licker-in roller at 780r / min, and the speed of the cover plate at 91mm / min; the doffer speed is controlled at 26r / min, and the five-point distance between the c...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com