Stainless steel sieve plate high temperature permeability dissolving nitrogen treatment method

A stainless steel sieve and stainless steel technology, applied in the direction of coating, metal material coating process, solid diffusion coating, etc., can solve problems such as wear and sieve plate corrosion, and achieve the effect of simple process, extended service life and uniform thickness

Active Publication Date: 2015-09-09
SHANDONG UNIV OF SCI & TECH
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In order to solve the corrosion and wear problems of the sieve plate under harsh working conditions, the present invention provides a high-temperature infiltration nitrogen treatment method to improve the corrosion resistance of the stainless steel sieve plate. A high-temperature dissolved nitrogen layer of 1-2mm is obtained on the hole wall surface, and a nitrogen-containing martensite structure is obtained through the quenching process, which can significantly improve the wear resistance of the sieve plate surface and the hole wall without reducing the corrosion resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stainless steel sieve plate high temperature permeability dissolving nitrogen treatment method
  • Stainless steel sieve plate high temperature permeability dissolving nitrogen treatment method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Step 1: Surface Pretreatment

[0032] The surface of the stainless steel sieve plate is treated with a general electroless Ni plating pretreatment method, which is divided into two steps of cleaning and activation: first use alcohol or gasoline to completely remove the oil on the surface of the workpiece, and then pickle the surface to remove the oxide film on the surface of the workpiece, acid Washing temperature: 15-30°C, pickling time: 3-5min;

[0033] Step 2: Electroless Nickel Flash Plating

[0034] Immediately after pickling to remove the oxide film on the surface of the stainless steel sieve plate, immerse it in the flash nickel solution. When performing nickel flash plating, the stainless steel sieve plate should be pre-soaked in the plating tank for 10-15 minutes before being energized. After electrification, the plated parts stay in the plating tank for 3 minutes, and after nickel flash plating, they must be quickly put into the nitriding furnace after clean...

Embodiment 2

[0039] In addition to the second step of electrification, the plated parts stay in the plating tank for 5 minutes, and in the third step of high temperature dissolved nitrogen treatment, the dissolved nitrogen temperature is set to 1050 ° C, the pressure in the furnace is set to 2 bar, and the nitriding time is kept for 4 hours. Except for the parameter changes in the above two steps, all other processes and parameters are the same as in the first embodiment.

[0040] It has been tested: the martensite depth of the solid-dissolved nitrogen obtained in Example 2 reaches 1 mm, and the hardness can be increased by 1.3 times.

Embodiment 3

[0042] In addition to the second step of electrification, the plated parts stay in the plating tank for 4 minutes, and in the third step of high temperature dissolved nitrogen treatment, the dissolved nitrogen temperature is set to 1010 ° C, the pressure in the furnace is set to 1.5 bar, and the nitriding time is kept for 3 hours. Except for the parameter changes in the above two steps, all other processes and parameters are the same as in the first embodiment.

[0043] It has been tested: the martensite depth of solid-dissolved nitrogen finally obtained in Example 3 reaches 1.5 mm, and the hardness can be increased by 1.5 times.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a stainless steel sieve plate high temperature permeability dissolving nitrogen treatment method, by stainless steel sieve plate high temperature permeability dissolving nitrogen treatment, a 1-2 mm high temperature dissolving nitrogen layer is obtained on sieve hole wall surface, through the quenching process, a nitrogen-containing martensite or austenite layer is obtained on sieve plate surface and hole wall surface, on the basis of keeping corrosion resistance of stainless steel, the wear resistance of the sieve plate surface and hole wall surface is significantly increased, and the service life of a stainless steel sieve plate is prolonged.

Description

technical field [0001] The invention belongs to the field of materials, and relates to a method for improving the wear resistance of stainless steel sieve plates. Specifically, it uses high-temperature infiltration nitrogen treatment to obtain a high-temperature dissolved nitrogen layer of 1-2 mm on the wall surface of the sieve hole, and through a quenching process, The method of obtaining nitrogen-containing martensite or austenite is a technology that significantly improves the wear resistance of the surface of the sieve plate and the wall of the hole on the basis of maintaining the corrosion resistance of stainless steel. Background technique [0002] Stainless steel sieve plate has good corrosion resistance, it has high rigidity and bearing capacity, and can be made into rigid screening and filtering devices of various shapes, which are widely used in screening, filtering, dehydration, desliming, etc. in various industries effect. At present, the sieve plates used in c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C8/26C23C8/02C23C8/80C25D7/04
Inventor 崔洪芝王伟张国松宋强魏娜宋晓杰张新杰
Owner SHANDONG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com