A light conversion film and adhesive technology, which is applied in the direction of non-polymer organic compound adhesives, film/sheet adhesives, adhesives, etc., can solve the problems of quantum dot light conversion film failure, easy to fade, etc. , to achieve high compactness, improve stability, improve service life and stability

Active Publication Date: 2015-09-16
ZHANGJIAGANG KANGDE XIN OPTRONICS MATERIAL
View PDF4 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The main purpose of the present invention is to provide a UV curing adhesive, a quantum dot light conversion film and a white light emitting device comprising a quantum dot light conversion film, so as to solve the problem that the quantum dots are exposed to trace amounts of water vapor, oxygen and acid in the prior art. , It is easy to die out in alkali, which leads to the failure of the quantum dot light conversion film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV curing adhesive, quantum dot light conversion film and white light emitting device comprising quantum dot light conversion film
  • UV curing adhesive, quantum dot light conversion film and white light emitting device comprising quantum dot light conversion film
  • UV curing adhesive, quantum dot light conversion film and white light emitting device comprising quantum dot light conversion film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] The composition of the UV curing adhesive includes 3.0 g of low-polarity oligomers with the structure of formula (I), wherein the R of the above-mentioned oligomers 1 is a silicon atom, R 2 is a carbon atom, R 3 for SiH 3 , degree of polymerization p=7; 1.0g of acrylate monomer with formula (Ⅲ) structure, wherein, R of the above-mentioned oligomer 4 Be phenyl, degree of polymerization n=8; 1.2g of acrylate monomer of cycloalkane with structure of formula (IV), 0.5g of dipentaerythritol hexaacrylate, 0.2g of photoinitiated monomer with structure of formula (Ⅴ) agent.

[0065] According to the weight ratio of red quantum dots, green quantum dots and UV curing adhesive is 1.5:6.0:100, red and green quantum dots are added to the UV curing adhesive of the above formula and stirred to obtain a mixture; then the above mixture is coated Spread on the transparent support layer 600, the thickness of the mixture is 100 μm, and then completely cured by light to obtain a quantum...

Embodiment 2

[0068] The composition of the UV curing adhesive includes 3.0 g of low-polarity oligomers with the structure of formula (I), wherein the R of the above-mentioned oligomers 1 is a silicon atom, R 2 is a carbon atom, R 3 for SiH 3 , degree of polymerization p=7; 1.0g of acrylate monomer with formula (Ⅲ) structure, wherein, R of the above-mentioned oligomer 4 Be phenyl, degree of polymerization n=8; 1.2g of acrylate monomer of cycloalkane with structure of formula (IV), 0.5g of dipentaerythritol hexaacrylate, 0.2g of photoinitiated monomer with structure of formula (Ⅴ) agent.

[0069] The first barrier layer 100 was prepared by coating a 50 μm thick UV-curable adhesive with a low-polarity formulation without quantum dots on the transparent support layer 600 and cured completely. The structure of the transparent support layer 600 is porous. According to the weight ratio of red quantum dots, green quantum dots and UV curing adhesive is 1.5:6.0:100, red and green quantum dots ar...

Embodiment 3

[0072] The composition of the UV curing adhesive includes 3.0 g of low-polarity oligomers with the structure of formula (I), wherein the R of the above-mentioned oligomers 1 is a silicon atom, R 2 is a carbon atom, R 3 for SiH 3 , degree of polymerization p=7; 1.0g of acrylate monomer with formula (Ⅲ) structure, wherein, R of the above-mentioned oligomer 4 Be phenyl, degree of polymerization n=8; 1.2g of acrylate monomer of cycloalkane with structure of formula (IV), 0.5g of dipentaerythritol hexaacrylate, 0.2g of photoinitiated monomer with structure of formula (Ⅴ) agent.

[0073] The first barrier layer 100 was prepared by coating a 50 μm thick UV-curable adhesive with a low-polarity formula without quantum dots on the transparent support layer 600 and cured completely. The structure of the transparent support layer 600 is surface atomization. According to the weight ratio of red quantum dots, green quantum dots and UV curing adhesive is 1.5:6.0:100.0, add red and green ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a UV curing adhesive, a quantum dot light conversion film and a white light emitting device comprising the quantum dot light conversion film. The UV curing adhesive comprises a low-polarity acrylate oligomer, an active dilute monomer and a photoinitiator, wherein the low-polarity acrylate oligomer is an oligomer with a structure of formula (I) or (II); R1 and R2 in the structure of formula (I) are separately selected from silicon atom and carbon atom; R3 is SiH3, CH3 or phenyl; p is 5-10; and in the formula (II), R4 is phenyl, naphthyl or C2-C10 alkyl, and n is 5-10. The UV curing adhesive has the characteristics of low polarity, water resistance, oxygen resistance and no acid or alkali and facilitates stable dispersion of quantum dots in the UV curing adhesive, and thus a quantum dot light conversion film with relatively high light color stability and brightness stability is obtained.

Description

technical field [0001] The invention relates to the field of light emitting devices, in particular to a UV curing adhesive, a quantum dot light conversion film and a white light light emitting device comprising the quantum dot light conversion film. Background technique [0002] The color gamut is usually called a color space, which represents the specific situation of a color image that can express the color of the color space. In terms of computer monitor applications, people mostly use sRGB as the standard color gamut definition, while in audio and video, they mostly use NTSC definition, and NTSC is a set of standards developed by the National Television Standards Committee (National Television Standards Committee) in the United States. A television broadcast transmission and reception protocol that covers a wider range of colors than the sRGB standard. However, the presentation of the color gamut value mainly depends on the choice of backlight. As we all know, liquid c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/02C09J7/00H01L33/44
Inventor 时成贞吴泓辉丁清华程武
Owner ZHANGJIAGANG KANGDE XIN OPTRONICS MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap