Polycarbonate composition suitable for laser welding and preparation method thereof

A polycarbonate and laser welding technology, applied in the field of polymer materials, can solve the problems of complex process, high price, low photothermal conversion rate, etc., and achieve the effects of high efficiency, high cleanliness and narrow particle size distribution

Active Publication Date: 2015-09-23
SHANGHAI KUMHO SUNNY PLASTICS
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Currently researched gold, tungsten oxide and other composite nanomaterials can absorb near-infrared light through the surface plasmon resonance absorption effect, but these materials are expensive, complicated in process, and low in light-to-heat conversion rate, which is not conducive to popularization.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A polycarbonate composition and a preparation method thereof, the method comprising the following steps:

[0033] (1) Weigh each component by weight: PC: 67 parts, ABS: 30 parts, copper sulfide 1: 3 parts, antioxidant 1010: 0.1 parts, antioxidant 168: 0.1 parts, lubricant PETS: 0.3 parts share.

[0034] (2) Feed the raw materials from the feeding port, melt and extrude at 200-280°C, the screw extruder rotates at 500rpm, and the pressure is 2MPa, melts and extrudes, and granulates to obtain the product.

[0035] (3) The screw diameter of the extruder is 35 mm, and the aspect ratio is 32.

Embodiment 2

[0037] A polycarbonate composition and a preparation method thereof, the method comprising the following steps:

[0038] (1) Weigh each component by weight: PC: 90 parts, ABS: 9 parts, copper sulfide 1:1 part, antioxidant 1010: 0.1 part, antioxidant 168: 0.1 part, lubricant PETS: 0.3 share.

[0039] (2) Feed the raw materials from the feeding port, melt and extrude at 200-280°C, the screw extruder rotates at 500rpm, and the pressure is 2MPa, melts and extrudes, and granulates to obtain the product.

[0040] (3) The screw diameter of the extruder is 35 mm, and the aspect ratio is 32.

Embodiment 3

[0042] A polycarbonate composition and a preparation method thereof, the method comprising the following steps:

[0043] (1) Weigh each component by weight: PC: 50 parts, ABS: 45 parts, copper sulfide 1:5 parts, antioxidant 1010: 0.1 parts, antioxidant 168: 0.1 parts, lubricant PETS: 0.3 parts share.

[0044] (2) Feed the raw materials from the feeding port, melt and extrude at 200-280°C, the screw extruder rotates at 500rpm, and the pressure is 2MPa, melts and extrudes, and granulates to obtain the product.

[0045] (3) The screw diameter of the extruder is 35 mm, and the aspect ratio is 32.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to polycarbonate composition suitable for laser welding. The polycarbonate composition suitable for the laser welding is prepared by the following components including, by weight, 50-90 parts of polycarbonate resin PC, 10-50 parts of ABS, 1-5 parts of copper sulfide nanoparticles, 0.1-1 part of antioxygen and 0.1-1 part of lubricant. The invention further provides a preparation method and the application of the polycarbonate composition suitable for the laser welding. Compared with the prior art, according to the polycarbonate composition, the absorption of near-infrared light by copper sulphide is used, the copper sulphide is prepared by using an ultrasound spray method, the particle size distribution is narrow, the cleanliness is high, the efficiency of turning luminous energy into thermal energy is high, and the polycarbonate composition is suitable for the laser welding.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a polycarbonate composition suitable for laser welding and a preparation method thereof. Background technique [0002] Laser welding has become the trend of future welding due to its advantages of fast and efficient, beautiful weld seam and unlimited product shape. The principle of laser welding is to weld two polymer products by projection. One of the polymer products is projected to the near-infrared laser, and the other polymer product absorbs the laser. After absorption, the temperature rises, causing the polymer to melt and produce an interface. of welding. [0003] Most polymers have very low absorption of infrared light, and the performance of laser welding can be improved by adding infrared absorbing materials. The currently studied composite nanomaterials such as gold and tungsten oxide can absorb near-infrared light through the surface plasmon resonance abso...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L69/00C08L55/02C08K13/02C08K3/30C08K5/134C08K5/526
CPCC08K2201/003C08K2201/011C08L69/00C08L55/02C08K13/02C08K2003/3009C08K5/1345C08K5/526
Inventor柏莲桂李强罗明华辛敏琦
OwnerSHANGHAI KUMHO SUNNY PLASTICS