Hardenable two part acrylic composition

An acrylic and composite technology, applied in tissue regeneration, surgical adhesives, surgery, etc., can solve problems such as poor repeatability, heavy work, and high cost

Active Publication Date: 2015-10-07
MITSUBISHI CHEM UK LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Furthermore, the batch-to-batch reproducibility of such processes is poor, sometimes requiring additional processing of the resulting product, such as by sieving or blending, to obtain the desired particle size distribution
[0022] This makes the industrial manufacture of PMMA with a large proportion of particles <20 microns in diameter a costly and sometimes onerous and unreliable effort

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hardenable two part acrylic composition
  • Hardenable two part acrylic composition
  • Hardenable two part acrylic composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0101] emulsion polymerization

[0102] Add 1.0 L of deionized water to a five-liter round-bottomed glass flask equipped with a nitrogen inlet, condenser, and electrically operated stainless steel paddle stirrer. At the same time with the help of an electric heating pack for 392min -1 With stirring, the water was heated to 82°C. A stream of nitrogen was passed through the vapor space of the flask above the liquid surface.

[0103] Prepared from 500 grams of methyl methacrylate (containing 5 ppm Topanol A inhibitor) and 5.0 grams of 75% active sodium dioctyl sulfosuccinate emulsifier (trade name: Aerosol TM OT) monomer mixture. These components are mixed before use.

[0104] Polymer seeding (stage 1 ) was prepared by adding 50 grams of the monomer mixture to the flask followed by 10 mL of a 2 wt % solution of potassium persulfate in deionized water at a water temperature of 82°C. After a slight temperature rise, the reaction proceeded for thirty minutes until the temper...

Embodiment 2

[0119] As Example 1, but using 14.0 grams of 70% active dibenzoyl peroxide and reducing mixer speed to 300min -1 .

Embodiment 3

[0121] As in Example 2, but about 1.0 grams of 1-dodecanethiol was added to the initial monomer mixture before starting the polymerization to cause a reduction in the molecular weight of the polymer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a hardenable two part acrylic composition, a polymer component of the two part hardenable composition and a method of producing a polymer component of the two part composition. The hardenable two part acrylic composition comprises an acrylic polymer composition first part and an acrylic monomer composition second part. The acrylic polymer composition first part comprises a first type of acrylic polymer particles characterized in that each first type of acrylic polymer particle is formed of a network of coalesced emulsion polymerized acrylic microparticles or is microporous. The acrylic polymer composition may comprise emulsion polymerised acrylic polymer particles of particle size between 10 and 2000nm. The invention also extends to the use of acrylic polymer particles formed of a network of coalesced emulsion polymerized acrylic microparticles as a dough time reduction agent in a hardenable two part acrylic composition.

Description

[0001] This application is a divisional application of the application dated August 13, 2009, the application number is 200980131088.8, and the title of the invention is "hardenable two-part acrylic composition". technical field [0002] The present invention relates to polymer compositions, and in particular, but not exclusively, to hardenable two-part acrylic compositions, polymer components of the two-part hardenable compositions, and methods of producing the polymer components of the two-part compositions. Background technique [0003] Hardenable compositions formed by mixing together acrylic polymers and monomers are useful in many applications. Particular utility is found in dental, medical, adhesives and construction applications where such materials have been used for over 40 years. [0004] Dental applications include their use in denture bases, denture bases, denture liners, denture repairs, custom trays, veneers for crowns and bridges, dentures, veneers and restor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F265/06C08F265/04C08L33/00A61L24/06
CPCC08F265/06A61L24/0036A61L24/0094A61L24/06C08F265/04C08L51/003A61L2430/02C08L2666/02C08L33/00