Antibacterial flame-retardant paint and preparation method thereof

A flame retardant coating and mass fraction technology, applied in the field of coatings, can solve the problem of no antibacterial function, and achieve the effects of preventing infection, purifying the air, and having good transparency.

Inactive Publication Date: 2015-10-07
饶烨
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current industrialized products do not have antibacterial function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial flame-retardant paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The antibacterial and flame-retardant coating in the present embodiment is made up of following mass components: 6 parts of glycidyl acrylate, 15 parts of conch shell powder, 8 parts of aluminum tripolyphosphate, 10 parts of antibacterial nano-titanium dioxide, coconut oil fatty acid diethanolamide 8 parts, 4 parts of precipitated barium sulfate, 12 parts of polyvinyl butyral, 0.5 parts of ultrafine acrylate rubber powder, 0.1 part of isophorone diisocyanate, 5 parts of epoxy acrylic resin, 1 part of zinc borate.

[0029] The preparation method of above-mentioned antibacterial flame-retardant coating comprises the following steps:

[0030] (1) Add the conch shell powder of the above-mentioned parts by mass into water, then add the glycidyl acrylate, aluminum tripolyphosphate, coconut oil fatty acid diethanolamide, precipitated barium sulfate, and polyvinyl butyral in turn in the above-mentioned parts by mass. , isophorone diisocyanate, epoxy acrylic resin, zinc borate, ...

Embodiment 2

[0035] The antibacterial and flame-retardant coating in the present embodiment is made up of following mass components: 10 parts of glycidyl acrylate, 30 parts of conch shell powder, 16 parts of aluminum tripolyphosphate, 25 parts of antibacterial nano-titanium dioxide, coconut oil fatty acid diethanolamide 10 parts, 10 parts of precipitated barium sulfate, 20 parts of polyvinyl butyral, 1 part of ultrafine acrylate rubber powder, 0.5 parts of isophorone diisocyanate, 15 parts of epoxy acrylic resin, 3 parts of zinc borate.

[0036]The preparation method of above-mentioned antibacterial flame-retardant coating comprises the following steps:

[0037] (1) Add the conch shell powder of the above-mentioned parts by mass into water, then add the glycidyl acrylate, aluminum tripolyphosphate, coconut oil fatty acid diethanolamide, precipitated barium sulfate, and polyvinyl butyral in turn in the above-mentioned parts by mass. , isophorone diisocyanate, epoxy acrylic resin, zinc borat...

Embodiment 3

[0042] The antibacterial and flame-retardant coating in the present embodiment is made up of following mass components: 8 parts of glycidyl acrylate, 18 parts of conch shell powder, 12 parts of aluminum tripolyphosphate, 13 parts of antibacterial nano-titanium dioxide, coconut oil fatty acid diethanolamide 9 parts, 12 parts of precipitated barium sulfate, 16 parts of polyvinyl butyral, 0.75 parts of ultrafine acrylate rubber powder, 0.3 parts of isophorone diisocyanate, 10 parts of epoxy acrylic resin, 2 parts of zinc borate.

[0043] The preparation method of above-mentioned antibacterial flame-retardant coating comprises the following steps:

[0044] (1) Add the conch shell powder of the above-mentioned parts by mass into water, then add the glycidyl acrylate, aluminum tripolyphosphate, coconut oil fatty acid diethanolamide, precipitated barium sulfate, and polyvinyl butyral in turn in the above-mentioned parts by mass. , isophorone diisocyanate, epoxy acrylic resin, zinc bo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to antibacterial flame-retardant paint. The antibacterial flame-retardant paint consists of the following substances in parts by weight: 6 to 10 parts of glycidyl acrylate, 15 to 30 parts of trumpet shell powder, 8 to 16 parts of aluminium triphosphate, 10 to 25 parts of antibacterial nano titanium dioxide, 8 to 10 parts of coconut oil fatty acid diethanol amide, 4 to 10 parts of precipitated barium sulfate, 12 to 20 parts of polyvinyl butyral, 0.5 to 1 part of superfine acrylate rubber powder, 0.1 to 0.5 part of isophorone diisocyanate, 5 to 15 parts of epoxy acrylic resin and 1 to 3 parts of zinc borate. The antibacterial flame-retardant paint preparation process is carried out under the normal temperature and normal pressure, no novel device is needed, the process is simple, and the production cost is low. After the antibacterial flame-retardant paint is used, not only is the surface antibacterial performance of the material effectively improved, but also the flame-retardant performance is relatively good.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to an antibacterial and flame-retardant coating and a preparation method thereof. Background technique [0002] With the rapid development of the economy, people's living standards have been greatly improved, and their health awareness has been continuously enhanced. Especially in recent years, the outbreak and prevalence of various diseases have made people pay more and more attention to the impact of various infectious diseases and diseases caused by harmful bacteria on human health. serious harm caused. This type of product of industrialization does not have antibacterial function at present. With the improvement of people's living standards and the strengthening of hygiene awareness, antibacterial products will inevitably be developed. In addition, some coatings have a good effect on flame retardant, which is convenient and better flame retardant, and improves the safety of c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D129/14C09D163/10C09D7/12
Inventor 饶烨
Owner 饶烨
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com