Method for manufacturing composite non-woven fabric collar interlining

A non-woven, composite technology, applied in clothing, clothing, applications, etc., can solve the problems of high cost, low stiffness and complex preparation process of bamboo charcoal fiber and far-infrared polyester, and achieve good hardness, low price, cost reduction effect

Inactive Publication Date: 2015-10-28
CHANGXING HONGBO TEXTILE
View PDF8 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the weak point of this invention is: the fabric after finishing is comparatively soft, and stiffness is not high enough, if used as collar lining not crisp enough
But its disadvantage is that the cost of bamboo charcoal fiber and far-infrared polyester is relatively high, it is not suitable for use as the base fabric of fusible interlining, and the preparation process is relatively complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A method for preparing a composite non-woven fabric collar lining is carried out as follows:

[0043] Among them, the preparation process of the non-woven fabric base fabric is as follows:

[0044] (1) Preparation of non-woven fabric: take 8 parts of natural fragrance and add it to 1000 parts of water to disperse evenly, then add 12 parts of halloysite powder to the solution to obtain a mixed solution, and leave the mixed solution to stand for 4 hours under vacuum After centrifugation and drying, halloysite powder loaded with natural flavor is obtained.

[0045] The particle size of the halloysite powder is 0.3-1 micron; the natural flavor is a mixture of sandalwood powder and camphor leaf powder, and the particle size of the natural flavor is 50-80 nanometers; the relative molecular weight of the polyethylene oxide is 800,000 -1200000; The dispersant is polypropylene wax.

[0046] In addition, take 7 parts of halloysite powder, 7 parts of aluminum chloride, 1 part of polyethy...

Embodiment 2

[0054] (1) Preparation of non-woven fabric: take 8 parts of natural fragrance and add it to 1000 parts of water to disperse evenly, then add 12 parts of halloysite powder to the solution to obtain a mixed solution, and leave the mixed solution to stand for 4 hours under vacuum After centrifugation and drying, halloysite powder loaded with natural flavor is obtained.

[0055] After the halloysite powder is loaded with natural flavor, take peppermint essential oil and heat it under reduced pressure in a closed container. Place the halloysite powder loaded with natural flavor on top of the peppermint essential oil in the closed container, and take it out after fumigation for 3 hours.

[0056] The preparation method of the peppermint essential oil is as follows: take the peppermint stems and leaves and grind them, after passing 200 meshes, take 12 parts of peppermint stems and leaves powder and add to 100 parts of ethanol aqueous solution with a concentration of 70wt%, and then add pepp...

Embodiment 3

[0066] (1) Preparation of non-woven fabric: take 5 parts of natural fragrance and add it to 1000 parts of water to disperse evenly, then add 10 parts of halloysite powder to the solution to obtain a mixed solution, and let the mixed solution stand for 3 hours under vacuum After centrifugation and drying, halloysite powder loaded with natural flavor is obtained.

[0067] After the halloysite powder is loaded with natural flavors, take peppermint essential oil and heat it under reduced pressure in a closed container, place the halloysite powder loaded with natural flavors on top of the peppermint essential oil in the closed container, and take it out after the fumigation treatment for 4 hours.

[0068] The preparation method of the peppermint essential oil is as follows: take the peppermint stems and leaves and grind them, after 200 meshes, take 10 parts of peppermint stems and leaves powder and add to 100 parts of ethanol aqueous solution with a concentration of 60wt%, and then add p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of non-woven fabric adhesive interlinings, and discloses a method for manufacturing a composite non-woven fabric collar interlining. Composite non-woven fabrics serve as the grey cloth. The method comprises following steps: (1) manufacturing the non-woven fabrics; (2) preprocessing the grey cloth; (3) dispensing the non-woven fabrics; and (4) baking the non-woven fabrics so as to obtain the composite non-woven fabric collar interlining. Compared with a conventional collar interlining, the composite non-woven fabric collar interlining is high in hygroscopicity and air permeability, stiff in texture and low in cost, can give out fragrance, and has a simple manufacturing process.

Description

Technical field [0001] The invention relates to the field of non-woven fabric adhesive interlinings, in particular to a method for preparing a composite non-woven fabric collar interlining. Background technique [0002] Fusible lining is a kind of lining coated with hot melt adhesive, which is one of the auxiliary materials often used in fabric production. The fusible interlining is heated and ironed, and the hot-melt adhesive coating on the fusible interlining is heated and melted, thereby attaching to the back of the fabric. When the fabric needs to express its stiffness and thickness, it can be reflected by adding fusible interlining, or the fabric is too thick. When it is too soft and slippery to operate, adding a fusible interlining can make the fabric smooth and obedient. [0003] Fusible interlining can be divided into: [0004] 1. Woven Fusible Interlining: Interlining made of woven fabric. [0005] 2. Knitted Fusible Interlining: Interlining fabric made of woven fabric. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A41D27/02D01F1/10D04H1/4291
Inventor 杨俊波杨志德
Owner CHANGXING HONGBO TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap