Wire rod for high-carbon steel cut wire shot and production method thereof

A technology of high-carbon steel wire and production method, which is applied in the field of iron and steel product production, can solve the problems such as no reports on the production method of high-carbon steel wire cutting shot wire, and achieve good social and economic benefits, high purity, and cleaning performance Good results

Inactive Publication Date: 2015-10-28
武钢集团有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In the retrieved literature, there is no report on the wire rod for high carbon steel wire cutting shot and its production method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A high-carbon steel wire rod for cutting shots, wherein the weight percentage of each component is: C: 0.70%, Mn: 0.90%, Si: 0.35%, Cr: 0.016%, V: 0.006%, P: 0.011%, S : 0.009%, Cu: 0.04%, N: 0.0056%, and the rest are Fe and unavoidable impurities.

[0020] The method for producing the above-mentioned wire rod for cutting high-carbon steel wire, comprising the following steps: blast furnace smelting molten iron → molten iron desulfurization → converter smelting → argon blowing → LF refining → VD degassing → continuous steel casting → billet cleaning → billet heating → high wire Rolling→Stelmo controlled cooling→Coil collection→P / F line transportation→Bundling. Among them, the tapping temperature in the converter smelting step is 1665°C, and the carbon content of the tapping is 0.06%. Refining processes such as argon blowing at the bottom of the furnace, LF refining, VD degassing and soft blowing can adjust and uniform the chemical composition in the steel, reducing incl...

Embodiment 2

[0023] A high-carbon steel wire rod for cutting shots, wherein the weight percentage of each component is: C: 0.86%, Mn: 0.50%, Si: 0.15%, Cr: 0.136%, V: 0.019%, P: 0.009%, S : 0.006%, Cu: 0.04%, N: 0.0052%, and the rest are Fe and unavoidable impurities.

[0024] The method for producing the above-mentioned wire rod for cutting high-carbon steel wire, comprising the following steps: blast furnace smelting molten iron → molten iron desulfurization → converter smelting → argon blowing → LF refining → VD degassing → continuous steel casting → billet cleaning → billet heating → high wire Rolling→Stelmo controlled cooling→Coil collection→P / F line transportation→Bundling. Among them, the tapping temperature in the converter smelting step is 1660 °C, and the carbon content of the tapping is 0.083%. The refining processes such as argon blowing at the bottom of the furnace, LF refining, VD degassing and soft blowing can adjust and uniform the chemical composition in the steel, reducin...

Embodiment 3

[0027] A high-carbon steel wire rod for cutting shots, wherein the weight percentage of each component is: C: 0.84%, Mn: 0.71%, Si: 0.23%, Cr: 0.326%, V: 0.005%, P: 0.011%, S : 0.010%, Cu: 0.04%, N: 0.0043%, and the rest are Fe and unavoidable impurities.

[0028] The method for producing the above-mentioned wire rod for cutting high-carbon steel wire, comprising the following steps: blast furnace smelting molten iron → molten iron desulfurization → converter smelting → argon blowing → LF refining → VD degassing → continuous steel casting → billet cleaning → billet heating → high wire Rolling→Stelmo controlled cooling→Coil collection→P / F line transportation→Bundling. Among them, the tapping temperature in the converter smelting step is 1671°C, and the carbon content of the tapping is 0.070%. Refining processes such as argon blowing at the bottom of the furnace, LF refining, VD degassing and soft blowing can adjust and uniform the chemical composition in the steel, reducing inc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The present invention discloses a wire rod for high-carbon steel cut wire shot, and the wire rod is characterized by comprising the following components by weight: 0.70-0.86% of C, 0.50-0.90% of Mn, 0.15-0.35% of Si, no more than 0.40% of Cr, no more than 0.05% of V, no more than 0.020% of P, no more than 0.015% of S, no more than 0.20% of Cu, no more than 0.0065% of N, and the balance of Fe and unavoidable impurities. The invention also provides a production method of the wire rod for high-carbon steel cut wire shot. The wire rod for high-carbon steel cut wire shot and production method thereof can meet the technical requirements of wire product industry on new product; the wire rod for high-carbon steel cut wire shot has the characteristics of high purity, uniform composition and tissue and the good cleaning rod performance, has good social and economic benefits, and is worthy of promotion.

Description

technical field [0001] The invention relates to the technical field of iron and steel product production, in particular to a wire rod for high-carbon steel wire cutting shots and a production method thereof. Background technique [0002] Shot peening of metal surface is a method of using mechanical centrifugal or pneumatic equipment to inject abrasives at high speed, impacting the surface of transmission parts to cause surface deformation and produce compressive stress, plastic deformation, and surface deformation strengthening method, which can improve And improve the surface properties of parts and fatigue strength, among which high carbon steel wire cutting shot is an ideal metal abrasive for shot blasting. [0003] At present, shot peening cleaning and strengthening are more and more widely used in industrial production. The annual consumption of various metal abrasives in China reaches about 500,000 tons. Among the abrasives used for shot peening strengthening, steel wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/04C22C38/12C22C38/16C22C38/18C22C38/20C22C38/24C21D8/06
Inventor 覃之光夏艳花李建华周勇桂江兵任安超吴超徐志东罗德信
Owner 武钢集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap