Blended and interwoven fabric as well as preparation method thereof

A technology of interwoven fabric and base fabric layer, applied in the field of textile fabrics, can solve the problems of no preparation method, no acid and alkali resistance, antistatic, high and low temperature resistance, narrow use range, etc. Wide and versatile effect

Inactive Publication Date: 2015-12-09
定远县保尔工贸有限公司
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the interwoven fabric disclosed in this patent has the characteristics of moisture absorption, good air permeability, and good warmth retention, the interwoven fabric has no functions of acid and alkali resistance, antistatic, high and low temperature resistance, and can only be used in simple environments. The scope of use is narrow; and there is no preparation method, therefore, it is necessary to design a kind of blended interwoven fabric and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blended and interwoven fabric as well as preparation method thereof
  • Blended and interwoven fabric as well as preparation method thereof
  • Blended and interwoven fabric as well as preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] The preparation method of this blended interwoven cloth comprises the following steps:

[0047] A, take the required raw material by the weight part of above each component;

[0048] b. Add the polytetrafluoroethylene concentrated dispersion, crosslinking agent, antistatic agent and antioxidant to the mixer, stir for 5 minutes, and stir at a speed of 100r / min to prepare the finishing solution;

[0049] c. Inject the finishing liquid into the padding tank of the padding equipment, dip the base cloth layer in the padding tank 14, and process it with padding process, the padding speed is 10m / min, and the finishing liquid layer is the protective layer;

[0050] d. Put the padded base fabric layer into an oven for drying treatment at a drying temperature of 100° C. and a drying time of 10 minutes to obtain the blended interwoven fabric.

[0051] Such as figure 1 Shown, the padding equipment in step c comprises frame 1, first roller 10, second roller 12, the 3rd roller 11 a...

Embodiment 2

[0057] The preparation method of this blended interwoven cloth comprises the following steps:

[0058] A, take the required raw material by the weight part of above each component;

[0059] b. Add polytetrafluoroethylene concentrated dispersion, cross-linking agent, antistatic agent and antioxidant to the mixer, stirring time 8min, stirring speed 125r / min, prepared finishing solution;

[0060] c. Inject the finishing solution into the padding tank of the padding equipment, immerse the base cloth layer in the padding tank 14, and treat it with the padding process, the padding speed is 15m / min, and the finishing liquid layer is the protective layer;

[0061] d. Put the padded base fabric layer into an oven for drying treatment, the drying temperature is 125° C., and the drying time is 14 minutes to obtain the blended interwoven fabric.

[0062] Such as figure 1 Shown, the padding equipment in step c comprises frame 1, first roller 10, second roller 12, the 3rd roller 11 and ma...

Embodiment 3

[0068] The preparation method of this blended interwoven cloth comprises the following steps:

[0069] A, take the required raw material by the weight part of above each component;

[0070] b. Add the polytetrafluoroethylene concentrated dispersion, crosslinking agent, antistatic agent and antioxidant to the mixer, stir for 10 minutes, and stir at a speed of 150r / min to prepare the finishing solution;

[0071] c. Inject the finishing liquid into the padding tank of the padding equipment, dip the base cloth layer in the padding tank 14, and process it with the padding process, the padding speed is 20m / min, and the finishing liquid layer is the protective layer;

[0072] d. Put the padded base fabric layer into an oven for drying treatment at a drying temperature of 150° C. and a drying time of 18 minutes to obtain the blended interwoven fabric.

[0073] With this method, the protective layer is quickly fixed on the base cloth layer by padding, which replaces the previous spray...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a blended and interwoven fabric as well as a preparation method thereof, and solves the technical problems that the conventional interwoven fabric does not have the functions of resisting acids, alkalis, static electricity and high-low temperature, can only be utilized in a simple environment, is low in utilization range and has no preparation methods. The blended and interwoven fabric comprises a base fabric layer, wherein protective layers are arrange on both sides of the base fabric layer; each protective layer comprises the following components in parts by weight: 40-60 parts of a polytetrafluoroethylene concentrated dispersion solution, 2-4 parts of a cross-linking agent, 3-5 parts of an anti-static agent and 0.6-1 part of an anti-oxidant. The blended and interwoven fabric has the advantages of being wide in utilization range and high in quality.

Description

technical field [0001] The invention belongs to the technical field of textile fabrics, and relates to an interwoven fabric, in particular to a blended interwoven fabric and a preparation method thereof. Background technique [0002] At present, people require clothing fabrics to have slub yarn effects in both warp and weft directions, with well-proportioned fabrics, strong layering, and good hemp-like effects. However, the more popular clothing fabrics at home and abroad cannot meet the above requirements at the same time. [0003] After searching, for example, Chinese patent literature discloses a double-layer polyester-nylon-cotton interwoven fabric [application number: 200910186034.3; announcement number: CN101660239A]. This double-layer polyester-nylon-cotton interwoven fabric is characterized in that: the interwoven fabric is a double-layer satin structure, which consists of 65D-85D polyester DTY as the warp, 5S-15S cotton fiber and 150D-170D nylon-polyester composite ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/256D06M13/10D06M13/335D06B3/18D06B9/00D06M101/06D06M101/04D06M101/32
Inventor 蒋新明
Owner 定远县保尔工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap