Special crawling ladder for inspection well
A technology for inspection wells and ladders, applied in the directions of ladders, artificial islands, underwater structures, etc., can solve the problems of insufficient opening angle, personnel falling, and increasing process difficulty, so as to facilitate inspection and maintenance operations, and facilitate installation and use. , to avoid the effect of false backfill
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0045] Weight composition of plastic:
[0046] 95 parts of o-phthalic resin,
[0047] 25 parts polystyrene,
[0048] Calcium carbonate superfine powder 90 parts,
[0049] 105 pieces of glass fiber with a length of 10-15mm,
[0050] 3 parts of tert-butyl peroxy-2-ethylhexanoate,
[0051] Lubricant BYK-W966: 1 part,
[0052] Magnesium stearate 4 parts,
[0053] 2 parts of MgO powder passed through a 400 mesh sieve,
[0054] 1 part styrene,
[0055] Aluminum hydroxide superfine powder 15 parts,
[0056] 30 parts of vitrified microbead particles;
[0057] 2 parts of No. 58 paraffin.
[0058] The measured bulk density of the vitrified microbead particles is 92kg / m 3 , the surface vitrified closed porosity rate is greater than 60%; and the vinyl silane coupling agent of 3% by weight of vitrified microbeads is pretreated in advance.
Embodiment 2
[0060] Weight composition of plastic:
[0061] 100 parts of m-benzene resin,
[0062] 28 parts polystyrene,
[0063] 105 parts of calcium carbonate superfine powder,
[0064] 110 pieces of glass fiber with a length of 10-15mm,
[0065] 2 parts of tert-butyl peroxy-2-ethylhexanoate,
[0066] Lubricant BYK-W9010: 1 part,
[0068] 1 part of MgO powder passed through a 400 mesh sieve,
[0069] 2 parts styrene,
[0070] Aluminum hydroxide superfine powder 16 parts,
[0071] 35 parts of vitrified microbead particles;
[0072] 3 parts of No. 54 paraffin wax.
[0073] The measured bulk density of the vitrified microbead particles is 86kg / m 3 , the surface vitrified closed porosity rate is greater than 60%; and the vitrified microbead particle weight 2% vinyl silane coupling agent is pretreated in advance.
Embodiment 3
[0075] Weight composition of plastic:
[0076] 108 parts of o-phthalic resin, m-benzene resin mixture,
[0077] 30 parts polystyrene,
[0078] Calcium carbonate superfine powder 93 parts,
[0079] 120 pieces of glass fiber with a length of 10-15mm,
[0080] 2 parts of tert-butyl peroxy-2-ethylhexanoate,
[0081] Lubricant BYK-W966: 2 parts,
[0082] Magnesium stearate 2 parts,
[0083] 3 parts of MgO powder passed through a 400-mesh sieve,
[0084] 2 parts styrene,
[0085] 14 parts of aluminum hydroxide superfine powder,
[0086] 38 parts of vitrified microbead particles;
[0087] 4 parts of No. 58 paraffin.
[0088] The measured bulk density of the vitrified microbead particles is 95kg / m 3 , the closed cell rate of surface vitrification is greater than 60%; and pretreatment with vinyl silane coupling agent of 4% by weight of vitrified microbead particles in advance.
[0089] The processing method of three embodiments is identical:
[0090] The glass fiber is firs...
PUM
Property | Measurement | Unit |
---|---|---|
density | aaaaa | aaaaa |
density | aaaaa | aaaaa |
density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com