An aluminum profile oxidation coloring process
An aluminum profile oxidation and process technology, applied in electrolytic coatings, surface reaction electrolytic coatings, coatings, etc., to achieve the effects of high gloss, low dark pattern rate, and uniform coloring
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0027] 7001 aluminum profile electrolytic coloring process:
[0028] (1) Degreasing:
[0029] The degreasing process is: 18g / L alkaline degreasing agent, pH = 8, temperature 65°C, time 10min;
[0030] (2) Wash with water after removing the oxide film on the surface of the aluminum alloy parts with an acidic solution;
[0031] (3) Oxidation in an oxidation treatment solution containing 0.08 g / L of EDTA, 0.05 g / L of sodium sulfate, 0.2 g / L of sodium aluminate, and 1.0 g / L of sodium fluoride in the oxidation solution, and adjusting the pH to 1.5, with 18-19V voltage, treatment temperature 15-17 ℃, treatment 6min;
[0032] (4) Water washing: 2 times of water washing, the pH of water washing is 1.1 and 1.0 respectively, the time is 10s and 20s respectively, and the conductivity is 120ms / m;
[0033] (5) Electrolytic coloring, the process parameters are:
[0034] NiSO 4 ·6H 2 O 150 g / L
[0035] h 3 BO 3 38g / L
[0036] EDTA0.06g / L
[0037] pH 4.5
[0038] temperature 25 ...
Embodiment 2
[0046] 7009 aluminum profile electrolytic coloring process:
[0047] (1) Degreasing:
[0048] The degreasing process is: 18g / L alkaline degreasing agent, pH = 8, temperature 65°C, time 12 min;
[0049] (2) Wash with water after removing the oxide film on the surface of the aluminum alloy parts with an acidic solution;
[0050] (3) Oxidation in an oxidation treatment solution containing 0.06 g / L of EDTA, 0.05 g / L of sodium sulfate, 0.2 g / L of sodium aluminate, and 1.0 g / L of sodium fluoride in the oxidation solution, and adjusting the pH to 1.5, use 19V voltage, treatment temperature 17℃, treatment 8min;
[0051] (4) Water washing: 2 times of water washing, the pH of water washing is 1.1 and 1.0 respectively, the time is 10s and 20s respectively, and the conductivity is 120ms / m;
[0052] (5) Electrolytic coloring, the process parameters are:
[0053] NiSO 4 ·6H 2 O 150 g / L
[0054] h 3 BO 3 42g / L
[0055] EDTA0.06g / L
[0056] pH 4.5
[0057] temperature 25 ℃
[0...
Embodiment 3
[0065] 2001 Aluminum profile electrolytic coloring process:
[0066] (1) Degreasing:
[0067] The degreasing process is: 18g / L alkaline degreasing agent, pH = 8, temperature 65°C, time 10-15 min;
[0068] (2) Wash with water after removing the oxide film on the surface of the aluminum alloy parts with an acidic solution;
[0069] (3) Oxidation in the oxidation treatment solution, containing EDTA 0.05g / L, sodium sulfate 0.05g / L, sodium aluminate 0.2g / L, sodium fluoride 1.0g / L in the said oxidation solution, adjust the pH to 1.5, use 18V voltage, treatment temperature 15℃, treatment 6min;
[0070](4) Water washing: 2 times of water washing, the pH of water washing is 1.1 and 1.0 respectively, the time is 10s and 20s respectively, and the conductivity is 120ms / m;
[0071] (5) Electrolytic coloring, the process parameters are:
[0072] NiSO 4 ·6H 2 O 140g / L
[0073] h 3 BO 3 38g / L
[0074] EDTA0.06g / L
[0075] pH 4.5
[0076] temperature 22 ℃
[0077] Voltage 16V
...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com