Microcrystalline graphite powder for carbonic refractory material and preparing method of microcrystalline graphite powder

A technology of microcrystalline graphite powder and refractory materials, which is applied in the field of microcrystalline graphite powder for carbon-containing refractory materials and its preparation, which can solve the problems of high-temperature mechanical performance decline of refractory materials, high impurity content of natural microcrystalline graphite, and difficulty in process control, etc. problems, to achieve the effects of improving high temperature mechanical properties, good thermal shock stability and slag erosion resistance, improving resource utilization and product added value

Inactive Publication Date: 2016-01-06
JIAOZUO JINXIN HENGTUO REFRACTORIES
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, natural microcrystalline graphite has a high content of impurities, and these impurities will form a large amount of liquid phase under high temperature conditions, resulting in a decrease in the high temperature mechanical properties of refractory materials
In order to solve this problem, microcrystalline graphite is purified by high-temperature alkali calcination in the prior art. Although this measure reduces the content of impurities in microcrystalline graphite, the production steps are complicated, and the high-temperature alkali calcination process requires high equipment. , the process control is difficult, and greatly increases the production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The present invention will be further described below in combination with specific embodiments, which are not intended to limit the protection scope thereof.

[0020] In order to avoid repetition, the technical parameters involved in this specific embodiment are now described in a unified manner as follows, and will not be repeated in the implementation:

[0021] The phenolic resin is liquid, wherein: the phenolic resin is an aminophenolic resin with a carbon residue rate ≥ 51.3%.

[0022] Alcohol is anhydrous alcohol, wherein: the mass fraction of ethanol ≥ 99.7%.

[0023] The particle size of the microcrystalline graphite powder is 3-500 μm, and the carbon content in the microcrystalline graphite powder is ≥90wt%.

[0024] Implementation column 1

[0025] A microcrystalline graphite powder for carbon-containing refractory materials and a preparation method thereof. Dissolve 20~25wt% phenolic resin in 30~35wt% alcohol, mix with 40~45wt% microcrystalline graphite mag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
carbon residual rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses microcrystalline graphite powder for a carbonic refractory material and a preparing method of the microcrystalline graphite powder. The preparing method comprises the preparing steps that firstly, 5-35wt% of phenolic resin is dissolved into 10-35wt% of alcohol, 40-80wt% of microcrystalline graphite is added, magnetic stirring is conducted for 2-10 minutes, and paste is obtained; secondly, the paste is put into an oven to be processed for 8-24 hours at the medium and low temperature, and a cured product is obtained after cooling; thirdly, the cured product is subjected to ball milling and then passes through a 325-mesh screen, and ball-milled powder is obtained; fourthly, the ball-milled powder is subjected to high-temperature carbonization for 1-4 hours under the condition of isolated air, and the microcrystalline graphite powder for the carbonic refractory material is obtained after cooling. The microcrystalline graphite powder is simple in technology and low in cost, the utilization rate of the microcrystalline graphite is increased, the added value of the product is increased, and the dilemma of resource exhaustion of crystalline flake graphite is relieved; in addition, the carbonic refractory material produced through the microcrystalline graphite powder prepared through the method has the good thermal shock stability and slag corrosion resisting performance, and can meet the use requirement.

Description

technical field [0001] The invention belongs to the technical field of graphite powder, and in particular relates to a microcrystalline graphite powder for carbon-containing refractory materials and a preparation method thereof. Background technique [0002] Carbon-containing refractory materials refer to refractory products made of carbon or carbon compounds, and the main component is carbon. Carbon-containing refractories are widely used in the iron and steel industry because of their excellent high temperature resistance, corrosion resistance and thermal shock resistance. At present, the production of carbon-containing refractories generally uses flake graphite with low impurity content as the carbon source. However, with the massive consumption of flake graphite, flake graphite is facing the problem of resource depletion. For another domestic microcrystalline graphite resource with abundant reserves and low price, if it can be developed as a carbon source for the produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66C04B35/628
Inventor 薛鸿雁许兴堂黄江文白晓吕宝丰彭德江周超李强
Owner JIAOZUO JINXIN HENGTUO REFRACTORIES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products