A technology of nano-particles and heavy metals, applied in the direction of non-active ingredient medical preparations, medical preparations containing active ingredients, pharmaceutical formulas, etc., can solve the problems of unseen preparations, and achieve simple preparation methods, good effects, and stability Good results
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] a. In the ethanol that is 2000 parts by mass, add 20 parts of dipalmitoylphosphatidylcholine, 10 parts of cholesterol, and 30 parts of phospholipids;
[0022] b. Stir magnetically at 40°C for 30 minutes until completely dissolved and no obvious lumps;
[0023] c. in the water of 2000 parts by mass, add 20 parts of acetic acid, after mixing, add 100 parts of chitosan;
[0024] d. Stir magnetically at room temperature for 12 hours until completely dissolved and no obvious particles;
[0025] e. Add the solution obtained in b to the solution obtained in d, and keep stirring at 50° C. for 60 minutes to obtain chitosan nanoparticles.
[0026] Test result: Particle size analysis is carried out after dilution, and the particle size is mainly distributed at 388nm.
Embodiment 2
[0028] a. In the ethanol that is 2000 parts by mass, add 40 parts of dipalmitoylphosphatidylcholine, 10 parts of cholesterol, and 50 parts of phospholipids;
[0029] b. Stir magnetically at 50°C for 30 minutes until completely dissolved and no obvious lumps;
[0030] c. in the water of 2000 parts by mass, add 20 parts of acetic acid, after mixing, add 100 parts of chitosan;
[0031] d. Stir magnetically at room temperature for 12 hours until completely dissolved and no obvious particles;
[0032] e. Add the solution obtained in b to the solution obtained in d, and keep stirring at 70° C. for 60 minutes to obtain chitosan nanoparticles.
[0033] Test result: Particle size analysis after dilution, the particle size is mainly distributed at 293nm.
Embodiment 3
[0035] a. In the ethanol that is 2000 parts by mass, add 80 parts of dipalmitoylphosphatidylcholine, 100 parts of cholesterol, and 10 parts of phospholipids;
[0036] b. Stir magnetically at 70°C for 50 minutes until completely dissolved and no obvious lumps;
[0037] c. in the water of 2000 parts by mass, add 40 parts of acetic acid, after mixing, add 80 parts of chitosan;
[0038] d. Stir magnetically at room temperature for 18 hours until completely dissolved and no obvious particles;
[0039] e. Add the solution obtained in b to the solution obtained in d, and keep stirring at 50° C. for 120 minutes to obtain chitosan nanoparticles.
[0040] Test result: Particle size analysis after dilution, the particle size is mainly distributed at 350nm.
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com