Soft stone paint template and preparation method

A coating and colored stone technology, which is applied in the field of soft stone coating templates and its preparation, can solve the problems of poor impact resistance, inconvenient carrying, and large size, and achieve the effects of strong impact resistance, saving manpower and tools, and small size

Inactive Publication Date: 2016-01-27
SHANDONG HORIZON BUILDING ENERGY EFFICIENCY TECH CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional method of coating formwork is sprayed on rectangular tiles or insulation material boards, which is heavy in texture, large in size, inconvenient to carry, and poor in impact resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) Add 121.2 kg of water in the above parts by weight into the dispersion tank.

[0022] (2) Adjust the speed of the disperser to 600 rpm, add preservative F2030.6kg, defoamer NXZ0.75kg, cellulose HS300001.35kg in sequence, and disperse for 15 minutes.

[0023] (3) Adjust the dispersion speed to 900 rpm and add AMP-950.3kg, and disperse for 15 minutes until HS30000 is completely dissolved

[0024] (4) Keep the speed of the disperser at 1 minute / 900 rpm, add film-forming aid T-124.8kg, and disperse for 5 minutes.

[0025] (5) Keep the speed of the disperser at 1 minute / 900 rpm, add 988A66kg and 9389105kg, disperse and stop for 5 minutes, and pack for later use.

[0026] (6) Put 1.2kg of the material in the above step (5) into the dispersing tank and then add 2.8kg of the above-mentioned base material. After stirring evenly, take an appropriate amount and pour it into a fixture with a length of 2.44m, a width of 1.22m and a thickness of 2.2mm. Spread a layer of glass f...

Embodiment 2

[0029] (1) Add 12.12 kg of water with the above weight kg into the dispersion tank.

[0030] (2) Adjust the speed of the disperser to 600 rpm, add preservative F2030.06kg, defoamer NXZ0.075kg, cellulose HS300000.135kg in sequence, and disperse for 15 minutes.

[0031] (3) Adjust the dispersion speed to 900 rpm and add AMP-950.3kg, and disperse for 15 minutes until HS30000 is completely dissolved.

[0032] (4) Keep the speed of the disperser at 1 minute / 900 rpm, add film-forming aid T-120.48kg, and disperse for 5 minutes.

[0033] (5) Keep the speed of the disperser at 1 minute / 900 rpm, add 988A6.6kg and 938910.5kg, stop the machine for 5 minutes and pack it for later use.

[0034] (6) Put 1.2kg of the material in the above step (5) into the dispersing tank and then add 2.8kg of the above-mentioned base material. After stirring evenly, take an appropriate amount and pour it into a fixture with a length of 2.44m, a width of 1.22m and a thickness of 2.2mm. Spread a layer of gla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses ceramic color stone paint, which comprises the following raw materials in parts by weight: 160.95 parts of water, 3 parts of hydroxyethyl cellulose, 0.3 part of antibacterial preservative HF-1, 0.6 part of fast and easy dispersant Orotan, 0.6 part of defoamer Foamaster NXZ, 6 parts of propylene glycol, 6 parts of coalescent Texanol, 0.6 part of ammonia water, 0.3 part of preservative Acticide Rs, 0.45 part of preservative Acticide EPW, 120 parts of emulsion BJL-881, 1.2 parts of and leveling agent Acrysol RM-2020NPR and 700 parts of sintering sand. The beneficial effects are that: the use amount per unit area is small, the ceramic color stone paint does not blur, has a natural real natural color, is not easy to fade, inconsistent in producing color, easy to construct, easy to clean and easy to renovate, saves labor, and has excellent adhesion and perfect hiding power, and good flexibility and alkali and impact resistance.

Description

Technical field: [0001] The invention relates to a paint template, in particular to a soft stone paint template and a preparation method thereof. Background technique: [0002] In order to meet the requirements of the overall appearance of people's buildings, one side coating needs to be sprayed on the outer surface of the building, such as thin exterior wall paint, multi-layer pattern paint, colored sand paint, thick quality paint. In order for people to choose different exterior wall paints that they like, according to the different properties of the paint, people are equipped with different ingredients and colorants to make templates with various colors and different performances for people to choose. The traditional paint formwork is sprayed on rectangular tiles or insulation material boards, which is heavy in texture, large in size, inconvenient to carry, and poor in impact resistance. Invention content: [0003] The purpose of the present invention is to provide a s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/02C04B14/06C04B24/38
Inventor 王丽萍王宝群
Owner SHANDONG HORIZON BUILDING ENERGY EFFICIENCY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap