A high-aluminum self-flowing iron trough castable

A high-alumina technology for iron trough castables, which is applied in the field of metal smelting and high-alumina self-flowing iron trough castables, can solve the problems of affecting the punctual tapping of blast furnaces and inconvenient production of blast furnaces, and achieve excellent thermal shock resistance, Enhanced fluidity and excellent flexural strength at room temperature

Active Publication Date: 2018-02-09
CHANGXING MINGTIAN FURNACE CHARGE
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It often affects the punctual tapping of the blast furnace, which brings inconvenience to the blast furnace production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Example 1: brown corundum or dense corundum: 40 parts, andalusite: 10 parts, silicon carbide: 10 parts, composite micropowder: 19 parts, carbon material: 3 parts, binder 10, composite water reducing agent: 2 parts .

Embodiment 2

[0024] Example 2: brown corundum or dense corundum: 45 parts, andalusite: 15 parts, silicon carbide: 12 parts, composite micropowder: 18 parts, carbon material: 4 parts, binder 10, composite water reducing agent: 4 parts .

Embodiment 3

[0025] Example 3: brown corundum or dense corundum: 50 parts, andalusite: 20 parts, silicon carbide: 14 parts, composite micropowder: 20 parts, carbon material: 4 parts, binder 10, composite water reducer: 4 parts .

[0026] The present invention mainly uses brown corundum or dense corundum, silicon carbide, silicon micropowder, etc. as main raw materials, andalusite is added to the product to replace part of brown corundum, andalusite decomposes and transforms into high melting point, low expansion coefficient and high temperature Mullite with better mechanical properties and thermal shock resistance makes the product have a good application effect in the tapping channel with high requirements for thermal shock resistance and high temperature strength; the introduction of composite micropowder in the product, α-Al2O3 micropowder and SiO2 When the amount of micropowder added is 4%, and combined with the addition of composite water reducing agent, its fluidity is the best. At t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-alumina self-flowing iron trough castable, which comprises the following components and the ratio of each component is: brown corundum or dense corundum: 40-50 parts, andalusite: 10-20 parts, silicon carbide: 10-20 parts 15 parts, composite micropowder: 10-20 parts, carbon material: 3-5 parts, binder 10-15 parts, composite water reducer: 2-4 parts. The present invention adds andalusite to replace part of brown corundum, andalusite decomposes and transforms into mullite with high melting point, low expansion coefficient, high temperature mechanical properties and thermal shock resistance during use, so that the product can resist thermal shock It has a good application effect in the iron trough that requires high performance and high temperature strength; when the introduction of composite micropowder in the product, the addition of α-Al2O3 micropowder and SiO2 micropowder is 4%, and the addition of composite water reducer, its The fluidity is the best. At this time, the system generates a large number of primary mullite phases at high temperatures, and the acicular mullite phases are interspersed between the corundum skeletons, so that the room temperature flexural strength and thermal shock resistance of the material are optimal.

Description

technical field [0001] The invention relates to the technical field of metal smelting, in particular to the technical field of a high-aluminum self-flowing iron trough castable. Background technique [0002] The tapping trough of blast furnace is a passage for guiding high temperature molten iron and slag and fully separating them. The service life of the refractories used in it directly affects the normal production of blast furnace. At present, the tap channel has loose structure, anti-oxidation slag, and low iron flow rate. The tap channel is repaired for a minor repair in three days and a major repair for five days. The number of repeated trench repairs is high, the labor intensity of the workers is high, and the service time of the tap channel is short. It often affects the punctual tapping of the blast furnace, which brings inconvenience to the blast furnace production. With the continuous improvement of blast furnace intensified smelting and blast furnace operation t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66
Inventor 佘亚锋金金佘凤娅佘成明王娇章亚
Owner CHANGXING MINGTIAN FURNACE CHARGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products