Polymer cement waterproof paint having good adhesion performance

A technology of waterproof coatings and polymers, applied in the direction of anti-corrosion coatings, coatings, etc., can solve problems such as difficult, complicated process, labor-intensive, etc., and achieve high elongation, high bonding strength, good water and alkali resistance and weather resistance Effect

Inactive Publication Date: 2016-03-02
ANHUI YOUYANG WATERPROOF TECH CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Even so, in actual construction projects, these methods are often difficult to operate due to the complex process, time-consuming, labor-intensive, and strong technical aspects, and there are too many human interference factors, making it difficult to control the quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer cement waterproof paint having good adhesion performance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A polymer cement waterproof coating with good adhesion is made of the following components in mass percentage: 60% of pure acrylic emulsion, 5% of modified polymer powder, 0.5% of rare earth light-changing agent, 0.5% of defoamer, Polyether polyol 4%, polyurethane thickener 6%, preservative 0.2%, hydroxyethyl cellulose 1%, sodium dodecylsulfonate 0.8%, propylene benzene emulsion 3%, dispersant 0.4%, balance is deionized water;

[0019] The above-mentioned modified polymer powder is made of the following components by mass percentage: 80% of nano-silicon dioxide, 5% of nano-silicon carbide, 5% of kaolin powder, 5% of nano-boron carbide, and 5% of fly ash; the preparation method as follows:

[0020] 1) Bake nano-silica, nano-silicon carbide, kaolin powder, nano-boron carbide and fly ash in a baking equipment at a temperature of 86-95°C for 30-40 minutes, then quickly cool to room temperature, and pulverize through 60 mesh Sieve, get the mixed powder for later use;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to polymer cement waterproof paint having good adhesion performance. The polymer cement waterproof paint having good adhesion performance comprises the following raw materials by mass percentage: 60% of a pure acrylic emulsion, 5% of modified polymer powder, 0.5% of a rare earth light conversion agent, 0.5% of an antifoaming agent, 4% of polyether polyol, 6% of a polyurethane thickening agent, 0.2% of an antiseptic, 1% of hydroxyethyl cellulose, 0.8% of sodium dodecanesulphonate, 3% of a phenylpropane emulsion, 0.4% of a dispersant, and the balance of deionized water. The prepared high built crack-resistant polymer cement waterproof paint has the advantages of large elongation percentage, high bonding strength, good water resistance, good alkali resistance and good weatherability, can be directly applied on bases without obvious water, and can be widely applied for watertightness of the bases with small activity such as kitchen, toilet, balcony and basement.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a polymer cement waterproof coating with good adhesion. Background technique [0002] At present, the bonding interface of some building components used in the construction field at home and abroad often has surface cracking, falling off, and even damage to the component body due to the influence of various factors, resulting in doubled building safety hazards. The specific manifestations are as follows: 1. In the external wall thermal insulation project and its decoration project, the pasted thermal insulation board and decorative board (brick) often appear to fall off from the external wall of the building; 2. The wall cement plastering of the building envelope Surface cracking, hollowing, and cracking will occur in the layer, thermal insulation leveling layer, finishing layer, roof concrete waterproof layer, etc.; , caulking materials, caulking materials, potting materials, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D7/12C09D5/08
Inventor 王赏
Owner ANHUI YOUYANG WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka