Anti-cracking sulphoaluminate cement and plant fiber product and preparation method thereof

A technology of sulfoaluminate cement and cracked sulfoaluminate, applied in solid waste management, sustainable waste treatment, climate sustainability, etc., can solve the problem of low surface smoothness, poor appearance, and easy cracking of boards and other problems, to achieve the effect of simple and easy-to-operate preparation method, smooth surface and strong durability

Inactive Publication Date: 2016-03-30
ZHUODA NEW MATERIALS TECH GRP WEIHAI CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the modular production of building boards is more and more popular among people. Modular production of boards has brought a new revolutionary impact to the construction industry, which reduces construction costs and greatly shortens the time for building houses. However, modular production Due to the fast hardening speed and easy demoulding required in the production process, the cement board produced by the existing formula is easy to crack, and the surface smoothness is not high. Surface cracking not only affects the appearance, but also reduces the strength and poor durability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] (1) Weigh the required raw materials of each component according to the ratio of parts by weight: 56 parts of sulphoaluminate cement, 16 parts of melon fiber with a particle size of 80, 7 parts of silica fume, 10 parts of fly ash, glass fiber 8 parts, 30 parts of water, 2 parts of retarder, 3 parts of water-retaining agent, 3 parts of thickener, and 5 parts of anti-cracking agent. Green chips, the crude fiber obtained was dried at 60°C for 3 hours, soaked in 20% alkaline water for 12 hours, washed with clean water, dried, and cut to a length of 0.5-1mm;

[0021] (2) Add sulfoaluminate cement, sweet potato fiber, silica fume, fly ash, and glass fiber into water and stir for 2 minutes, then add water retaining agent, thickener and anti-cracking agent, stir for 1 minute, and let stand for 10 minutes;

[0022] (3) Add retarder, stir for 2 minutes, send it to the roller leveling line production workshop, enter the template filling roller leveling to produce wet plates, and s...

Embodiment 2

[0028] (1) Weigh the required raw materials of each component according to the ratio of parts by weight: 82 parts of sulphoaluminate cement, 8 parts of melon fiber with a particle size of 120, 12 parts of silica fume, 15 parts of fly ash, glass fiber 12 parts, 90 parts of water, 5 parts of retarder, 5 parts of water-retaining agent, 5 parts of thickener and 8 parts of anti-cracking agent. Among them, the fiber of sweet potato is obtained from the skin of sweet potato, which is scraped off after 5 days of exposure to the sun. Green chips, the crude fiber obtained was dried at 70°C for 3 hours, soaked in 10% alkaline water for 12 hours, washed with clean water, dried, and cut to a length of 0.5-1mm;

[0029] (2) Add sulfoaluminate cement, sweet potato fiber, silica fume, fly ash, and glass fiber into water and stir for 10 minutes, then add water retaining agent, thickener and anti-cracking agent, stir for 1 minute, and let stand for 5 minutes;

[0030] (3) Add retarder, stir for...

Embodiment 3

[0036] (1) Weigh the required raw materials of each component according to the ratio of parts by weight: 69 parts of sulfoaluminate cement, 12 parts of melon fiber with a particle size of 100, 10 parts of silica fume, 12 parts of fly ash, glass fiber 10 parts, 60 parts of water, 3 parts of retarder, 4 parts of water-retaining agent, 4 parts of thickener and 6.5 parts of anti-cracking agent. Among them, the fiber of Di Shao melon is obtained from the skin of Di Shao melon, which is scraped off after 4 days in the sun. Green chips, the crude fiber obtained was dried at 65°C for 3 hours, soaked in 15% alkaline water for 12 hours, washed with clean water, dried, and cut to a length of 0.5-1mm;

[0037] (2) Add sulfoaluminate cement, sweet potato fiber, silica fume, fly ash, and glass fiber into water and stir for 6 minutes, then add water retaining agent, thickener and anti-cracking agent, stir for 1 minute, and let stand for 7 minutes;

[0038] (3) Add retarder, stir for 2 minute...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-cracking sulphoaluminate cement and plant fiber product comprising components of raw materials in parts by weight as follows: sulphoaluminate cement, Cynanchum thesioides fibers, silica fume, fly ash, glass fibers, water, a retarder, a water retaining agent, a thickening agent and an anti-cracking agent. The preparation method of the product comprises steps as follows: (1) weighing all components of raw materials in parts by weight; (2) adding the sulphoaluminate cement, the Cynanchum thesioides fibers, the silica fume, the fly ash and the glass fibers to the water with stirring, adding the water retaining agent, the thickening agent and the anti-cracking agent with stirring, and leaving the mixture to stand; (3) adding the retarder with stirring, and sending the mixture to a roller flattening line production workshop, producing a wet plate through mold plate filling and roller flattening, and cutting and sending the plate to a curing workshop for curing. The obtained product is smooth in surface, free of cracks, high in strength and high in durability; further, raw materials of the product are easy to obtain, the cost is low, and the preparation method is simple and easy to operate.

Description

technical field [0001] The invention relates to a plant fiber product and a preparation method thereof, in particular to a crack-resistant sulphoaluminate cement plant fiber product and a preparation method thereof. Background technique [0002] At present, the modular production of building boards is more and more popular among people. Modular production of boards has brought a new revolutionary impact to the construction industry, which reduces construction costs and greatly shortens the time for building houses. However, modular production Due to factors such as fast hardening speed and easy demoulding required in the production process of high-grade cement boards, the boards produced by the existing formula are prone to cracking, and the surface smoothness is not high. Surface cracking not only affects the appearance, but also reduces strength and poor durability. [0003] The information disclosed in this Background section is only for enhancing the understanding of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/06C04B18/24
CPCC04B18/248C04B28/06C04B2111/343C04B18/146C04B18/08C04B14/42C04B2103/22C04B2103/46C04B2103/44C04B2103/0068C04B24/16C04B24/04C04B22/0093C04B24/003C04B24/383C04B22/08C04B24/129C04B22/0013C04B22/142C04B24/045C04B24/307C04B24/10C04B14/041C04B24/121C04B24/24Y02W30/91
Inventor 杨卓舒余中华孙吉利陈强邹阳陈展庆月
Owner ZHUODA NEW MATERIALS TECH GRP WEIHAI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com