Rare earth permanent magnet material utilizing recycled waste materials and preparation method

A technology of rare earth permanent magnets and permanent magnet materials, applied in the direction of magnetic materials, magnetic objects, electrical components, etc., can solve the problem of insufficient coercive force of materials, and achieve the effects of improving magnetic properties, reducing costs, and high social value

Active Publication Date: 2016-04-13
XUZHOU NANFANG YONGCI MATERIAL
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the coercive force of the material prepared by this method is not high enough.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rare earth permanent magnet material utilizing recycled waste materials and preparation method
  • Rare earth permanent magnet material utilizing recycled waste materials and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The preparation method of the waste recycling rare earth permanent magnet material of the present invention comprises the following steps:

[0037] 1) Waste disposal:

[0038] a) Put phosphor powder waste in a roasting furnace for pretreatment at 620° C. for 2 hours, then ball mill to 20-80 microns to obtain roasted phosphor waste; mix the treated phosphor waste with Na 2 O mixed, high temperature alkali fusion treatment at 700°C for 3 hours to obtain the alkali fusion reaction product, in which Na 2 The mass ratio of O to the waste fluorescent powder after roasting treatment is 4:1.5; add 8mol / L (concentration is 6-10mol / L) hydrochloric acid to the obtained alkali fusion reaction product, the mass ratio of alkali fusion reaction product and hydrochloric acid is 1:1; put the prepared mixed solution in a 65°C constant temperature water bath and heat for 2 hours, then filter to obtain a leachate containing rare earth elements; take 130g / L oxalic acid solution and mix it ...

Embodiment 2

[0049] The preparation method of the waste recycling rare earth permanent magnet material of the present invention comprises the following steps:

[0050] 1) Waste disposal:

[0051] a) first place the phosphor waste material in a roasting furnace for pretreatment at 550° C. for 1 hour, and then ball mill it to 20-80 microns to obtain the roasted phosphor waste material; mix the processed phosphor waste material with Na 2 O mixed, high temperature alkali fusion treatment at 690°C for 2 hours to obtain alkali fusion reaction product, in which Na 2 The mass ratio of O to the roasted fluorescent powder waste was 4:1; 6mol / L hydrochloric acid was added to the resulting alkali fusion reaction product, and the mass ratio of the alkali fusion reaction product to hydrochloric acid was 1:1; Put it into a 65°C constant temperature water bath and heat it for 2 hours, then filter to obtain a leaching solution containing rare earth elements; mix 125g / L oxalic acid solution with the leachi...

Embodiment 3

[0062] In this example, the mixed rare earth permanent magnet material alloy ingot: according to the following mass percentage ingredients: Nd20%, Y8%, Eu4%, Dy4%, B4%, P0.3%, Ag0.175%, Ni0.5%, Si0.025 %, Ti0.5%, and the rest is Fe. All the other conditions and preparation process are the same as in Example 1. The mass percent content of N in the treated material is 0.050%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
widthaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention provides a rare earth permanent magnet material utilizing recycled waste materials. An alloy material is high in coercivity. The preparation method is simple in process, low in production cost and suitable for industrial production. The permanent magnet material comprises the following components in percentage by mass: 18-22% of Nd, 7.2-8.8% of Y, 3.6-4.4% of Eu, 3.6-4.4% of Dy, 2-6% of B, 0.1-0.5% of P, 0.15-0.20% of Ag, 0.45-0.60% of Ni, 0.01-0.04% of Si, 0.45-0.60% of Ti and the balance of Fe; the mass ratio of Nd to Y to Eu to Dy in the permanent magnet material is 10:4:2:2; and the permanent magnet material also comprises 0.045-0.060% of N in percentage by mass.

Description

technical field [0001] The invention belongs to the field of metal materials, and relates to a rare earth permanent magnet material recycled from scraps and a preparation method thereof. Background technique [0002] CN201410725480.8 application relates to a preparation method of rare earth permanent magnet material, the preparation method includes the following steps: respectively provide Re-Fe-B quenching powder and Ce-based quenching powder, wherein the Re-Fe-B quenching The rare earth Re in the powder is one or more of Nd, Pr, Dy, Tb, and the chemical formula of the Ce-based quenching powder is Ce x Fe (100-x-y-z) B y m z , M is selected from one or more of Ga, Co, Al, Zn, Cu, Nb and Zr, x, y and z are the mass percentages of the corresponding elements, and 28%≤x≤35%, 0.8% ≤y≤1.5%, 0%≤z≤2%; uniformly mix the Ce-based quenching powder with the Re-Fe-B quenching powder to obtain a mixed magnetic powder, wherein the Ce in the mixed magnetic powder The mass percentage...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01F1/057H01F1/059C22C38/08C22C38/02C22C38/14
CPCC22C38/001C22C38/005C22C38/007C22C38/02C22C38/08C22C38/14C22C38/32H01F1/0575H01F1/059
Inventor 张作州
Owner XUZHOU NANFANG YONGCI MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com