A kind of cold-heat-resistant water-soluble self-drying acrylic resin and preparation method thereof

An acrylic resin, hot water soluble technology, applied in the direction of coating, etc., can solve the problems of poor water resistance, slow drying speed, and reduced adhesion, and achieve the effect of superior cold and heat resistance, fast drying speed, and good toughness

Active Publication Date: 2019-01-01
YINGDE BOTE CHEM INDAL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing single-component acrylic resins are generally high molecular compounds formed by polymerization of conventional acrylic monomers and initiators at a certain temperature. The synthesis process is easy to implement, the amount of raw materials is easy to obtain, and the cost is suitable; The impact on performance is more prominent. Under colder conditions, many one-component paints are brittle, and the flexural toughness of the paint film is insufficient, and some even crack naturally, and the adhesion is greatly reduced; The scratch resistance of the surface is not good; in this way, its decoration, protection and other functions are greatly reduced under the change of cold and hot conditions, and the application area is narrowed, which cannot meet people's use needs
In addition, the conventional water-based one-component acrylic resin has a slow drying speed due to the fact that water is used as a solvent, which affects the working efficiency of the coating. Acrylic resin application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cold-heat-resistant water-soluble self-drying acrylic resin and preparation method thereof
  • A kind of cold-heat-resistant water-soluble self-drying acrylic resin and preparation method thereof
  • A kind of cold-heat-resistant water-soluble self-drying acrylic resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0052] A kind of hot and cold water-resistant self-drying type acrylic resin preparation step comprises as follows:

[0053] 1) Put material A into the reactor and heat up to reflux;

[0054] 2) Add material B evenly and at a constant speed, and the common dropping time is 4 hours;

[0055] 3) After the dropwise addition, keep the reflux reaction for 3 hours;

[0056] 4) Add C material, and keep warm for 3.5 hours;

[0057] 5) Remove 402Kg of 60% solvent under reduced pressure and increase temperature, then lower the temperature to below 80°C, add material D neutralizing agent to neutralize evenly, so that the pH value is 7-8;

[0058] 6) Add material E co-solvent and deionized water to dilute, disperse evenly, filter and pack.

[0059] Main technical indicators of a cold and hot water soluble self-drying acrylic resin:

[0060] Appearance: transparent or slightly opalescent viscous liquid;

[0061] Color (Fe-Co colorimetric): ≤2;

[0062] Solid content: 55±2%;

[0063]...

specific Embodiment 2

[0068] A kind of hot and cold water-resistant self-drying type acrylic resin preparation step comprises as follows:

[0069] 1) Put material A into the reactor and heat up to reflux;

[0070] 2) Add material B evenly and at a constant speed, and the common dropping time is 4 hours;

[0071] 3) After the dropwise addition, keep the reflux reaction for 3 hours;

[0072] 4) Add C material, and keep warm for 3.5 hours;

[0073] 5) Remove 365Kg of 55% solvent under reduced pressure and increase temperature, then lower the temperature to below 80°C, add material D neutralizing agent to neutralize evenly, so that the pH value is 7-8;

[0074] 6) Add material E co-solvent and deionized water to dilute, disperse evenly, filter and pack.

[0075] Main technical indicators of a cold and hot water soluble self-drying acrylic resin:

[0076] Appearance: transparent or slightly opalescent viscous liquid;

[0077] Color (Fe-Co colorimetric): ≤2;

[0078] Solid content: 50±2%;

[0079]...

specific Embodiment 3

[0084] A kind of hot and cold water-resistant self-drying type acrylic resin preparation step comprises as follows:

[0085] 1) Put material A into the reactor and heat up to reflux;

[0086] 2) Add material B evenly and at a constant speed, and the common dropping time is 4 hours;

[0087] 3) After the dropwise addition, keep the reflux reaction for 3 hours;

[0088] 4) Add C material, and keep warm for 3.5 hours;

[0089] 5) Remove 435Kg of 65% solvent under reduced pressure and increase temperature, then lower the temperature to below 80°C, add material D neutralizing agent to neutralize evenly, so that the pH value is 7-8;

[0090] 6) Add material E co-solvent and deionized water to dilute, disperse evenly, filter and pack.

[0091] Main technical indicators of a cold and hot water soluble self-drying acrylic resin:

[0092] Appearance: transparent or slightly opalescent viscous liquid;

[0093] Color (Fe-Co colorimetric): ≤2;

[0094] Solid content: 60±2%;

[0095]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing heat and cold resisting water-soluble air-drying acrylic resin. A monometer-phase solution B is prepared from 5-15 wt% of functional monomer, 7-15 wt% of acrylic acid or methacrylic acid, 20-45 wt% of hard monomer, 8-20 wt% of hard tenacity monomer, 15-45 wt% of soft monomer, 0.3-2 wt% of organic siloxane organosilicone monomer, 0.3-2 wt% of fluorine acrylic acid monomer, and 0.5-3 wt% of double-ethylenic-bond monomer, and the total percentage of the monomers is 100%. By the adoption of the method, the heat and cold resisting water-soluble air-drying acrylic resin is provided, and the problems that existing single-component water-soluble acrylic resin paint becomes crispy under the refrigeration condition and becomes tacky and liable to contamination under heating to cause poor membrane surface scratch resistance, dryness is insufficient, and water resistance is low are solved.

Description

technical field [0001] The present invention relates to a method for synthesizing and preparing an environment-friendly polymer compound, in particular to a one-component water-based acrylic resin paint. After the paint is coated, the paint film has superior performance under the conditions of cold and heat changes. The cold and hot water-resistant self-drying acrylic resin with the characteristics of small change, and the preparation method of the resin. Background technique [0002] With the enhancement of people's awareness of environmental protection and the improvement of environmental protection regulations, the use of volatile organic compounds (VOC) and harmful air pollutants (HAP) in traditional solvent-based coatings has become more and more restricted, and water-based coatings are increasingly being used by people. focus on. Copolymers synthesized with vinyl monomers such as acrylate, methacrylate and styrene as the main raw materials are called acrylic resins, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/06C08F220/14C08F220/18C08F220/26C08F222/10C08F230/08C08F212/08C08F220/58C08F212/12C08F220/22C09D133/08C09D125/08
CPCC08F212/08C08F220/14C09D125/08C09D133/08C08F220/18C08F220/1808C08F220/06C08F220/26C08F222/102C08F230/08C08F220/22C08F220/1804C08F220/58C08F222/1063
Inventor 戴竹先
Owner YINGDE BOTE CHEM INDAL