Treatment process for copper smelting smoke dust

A treatment process, copper smelting technology, applied in the field of copper smelting fume treatment process, can solve problems such as difficult to handle, reduce conversion rate, pollute the environment, etc., achieve the effect of improving capacity and solving open circuit problems

Active Publication Date: 2016-05-04
YANGGU XIANGGUANG COPPER
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the characteristics of such materials as complex components, difficult to handle, and polluting the environment, there is no mature and reliable technology in the world that can comprehensively recycle the above materials together.
At present, the method of copper smelting dust blending and returning to smelting has the following problems: the actual processing capacity of copper concentrate is ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Treatment process for copper smelting smoke dust
  • Treatment process for copper smelting smoke dust
  • Treatment process for copper smelting smoke dust

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0079] See Table 1-1 for the composition of copper smelting dust, which contains high arsenic and low copper; see Table 1-2 for the composition of waste acid.

[0080] Table 1-1 Composition of copper smelting dust

[0081] Element As Cu Fe Pb Zn Sb Bi content ％ ％ ％ ％ ％ ％ ％ soot 9.883 8.390 12.249 5.366 2.962 0.099 0.493

[0082] Table 1-2 Composition of waste acid

[0083] As Cu Fe Pb Zn Sb Bi h 2 SO 4 g / L g / L g / L g / L g / L g / L g / L g / L 0.32 0.1 0.099 0.0098 0.023 0.003 0.003 186

[0084] 1. Pickling

[0085] Prepare the waste acid into an acid solution with an acid mass concentration of 12.5%, and prepare the solution according to the solid-to-liquid ratio of smoke and acid solution at a ratio of 1:4, add it to the reaction kettle, heat it to 80°C, and react for 3.5 hours. After 3.5 hours, it will be solid-liquid Separation and leaching results are shown in Table 1...

Embodiment 2

[0119] The composition of copper smelting dust is shown in Table 2-1, and the dust contains high arsenic and low copper; the composition of waste acid is shown in Table 2-2.

[0120] Table 2-1 Composition of copper smelting dust

[0121] Element As Cu Fe Pb Zn Sb Bi content ％ ％ ％ ％ ％ ％ ％ soot 20.035 9.125 13.351 2.281 3.621 0.121 0.651

[0122] Table 2-2 Composition of waste acid

[0123] As Cu Fe Pb Zn Sb Bi h 2 SO 4 g / L g / L g / L g / L g / L g / L g / L g / L 0.12 0.105 0.086 0.001 0.035 0.004 0.004 136

[0124] 1. Pickling

[0125] Prepare the waste acid so that the acid concentration is 165g / l, make liquid according to the solid-to-liquid ratio of dust and acid liquid mass 1:6, add it to the reaction kettle, heat to 70°C, react for 5 hours, and separate the solid and liquid after 5 hours, see the leaching results Table 2-3.

[0126] Table 2-3 Leaching results

[0127] ...

Embodiment 3

[0160] The composition of copper smelting dust is shown in Table 3-1, the dust contains high arsenic and low copper; the composition of waste acid is shown in Table 3-2.

[0161] Table 3-1 Composition of copper smelting dust

[0162] Element As Cu Fe Pb Zn Sb Bi content ％ ％ ％ ％ ％ ％ ％ soot 15.314 7.951 11.382 4.655 4.210 0.101 0.750

[0163] Table 3-2 Composition of waste acid

[0164] As Cu Fe Pb Zn Sb Bi h 2 SO 4 g / L g / L g / L g / L g / L g / L g / L g / L 0.510 0.135 0.132 0.013 0.041 0.003 0.004 170

[0165] 1. Pickling

[0166] Prepare the waste acid into an acid solution with an acid mass concentration of 130g / l, and prepare the solution according to the solid-to-liquid ratio of smoke dust and acid solution at a ratio of 1:4.5, add it to the reaction kettle, heat to 80°C, and react for 3.5 hours. After 3.5 hours, it will solidify Liquid separation, leaching results are ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a treatment process for copper smelting smoke dust. The treatment process comprises the following steps that 1, after the copper smelting smoke dust is subjected to acid leaching, acid leaching liquor and acid leaching residues are obtained; 2, after the acid leaching liquor obtained in the step 1 is subjected to copper depositing through metal replacement, filter liquor with copper being deposited is obtained; 3, after the filter liquor with the copper being deposited in the step 2 neutralizes and oxidizes with alkali, ferric arsenate and filter liquor with arsenic being deposited are obtained; 4, after the filter liquor with arsenic being deposited in the step 3 is subjected to the secondary copper depositing through metal replacement, filter liquor being subjected to the secondary copper depositing and copper residues are obtained; and 5, after the filter liquor being subjected to the secondary copper depositing in the step 4 is subjected to zinc depositing through vulcanization, filter liquor with zinc being deposited and zinc residues are obtained. According to the treatment process for the copper smelting smoke dust provided by the invention, particularly, a treatment process for high-arsenic low-copper smoke dust, the harmless treatment of arsenic in the high-arsenic low-copper smoke dust is achieved; meanwhile, valuable metal copper, zinc, lead, bismuth and the like in the high-arsenic low-copper smoke dust are recovered comprehensively, and gradient recycle and comprehensive utilization of the impurities of the smoke dust are achieved.

Description

technical field [0001] The invention belongs to the technical field of copper smelting, and in particular relates to a treatment process for copper smelting smoke. Background technique [0002] Copper smelting technology refers to the process of obtaining refined copper from copper ore through various process steps. The copper smelting industry is a basic industry in the national economy, especially in my country, which is in the stage of industrialization, and the demand for copper maintains a high-speed growth. The status of the smelting industry in the national economy has been continuously improved. At present, the copper smelting industry has entered a new round of industrial upgrading period, and the copper smelting industry is becoming increasingly collectivized, specialized, large-scale and internationalized. The development of copper smelting technology has gone through a long process, but so far copper smelting is still dominated by pyrometallurgy, and its output a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B7/02C22B15/00C22B19/30C22B30/04
CPCC22B7/007C22B7/02C22B15/0067C22B15/0091C22B19/30C22B30/04Y02P10/20
Inventor 周松林谢祥添葛哲令王永明
Owner YANGGU XIANGGUANG COPPER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka