A preparation method of heteroatom-doped graphene-based material loaded noble metal nanoparticles

A graphene-based, nano-particle technology, applied in the field of materials science, can solve the problems of high catalyst price and low catalytic activity, and achieve the effect of simple preparation process and high economic value

Active Publication Date: 2018-08-28
SHANGHAI UNIVERSITY OF ELECTRIC POWER
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the above-mentioned technical problems in the prior art, the present invention provides a preparation method of heteroatom-doped graphene-based material-loaded noble metal nanoparticles, the heteroatom-doped graphene-based material-loaded noble metal nanoparticles The preparation method solves the technical problems of high price and low catalytic activity of direct alcohol fuel cell catalysts in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of heteroatom-doped graphene-based material loaded noble metal nanoparticles
  • A preparation method of heteroatom-doped graphene-based material loaded noble metal nanoparticles
  • A preparation method of heteroatom-doped graphene-based material loaded noble metal nanoparticles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A Pd / B, N-G boron-nitrogen-doped graphene-supported palladium nanoparticle material contains Pd, C, B, N, H and O elements.

[0026] The above-mentioned boron-nitrogen-doped graphene-supported palladium nanoparticle material preparation method specifically comprises the following steps:

[0027] (1) Preparation of graphene

[0028] Graphene oxide is obtained from graphite flakes through an improved oxidation method. Add 1-3g of graphite flakes to 1-5g of potassium persulfate and 1-5g of phosphorus pentoxide, then add 100-200ml of concentrated sulfuric acid (98%), oxidize at a high temperature of 50-100°C, and then use 1-10g of potassium permanganate is oxidized, and graphene is obtained through several times of centrifugal cleaning.

[0029] (2) Heteroatom-doped graphene materials

[0030] After 20-40mg of graphene is ultrasonically treated, add 1-100g of heteroatom precursors of boric acid and urea with a mass ratio of 1:1, and carry out B and N co-doping in a hydro...

Embodiment 2

[0043] A Pt / N-G of nitrogen-doped graphene-supported platinum nanoparticle material, containing Pt, C, N, H and O elements.

[0044] The above-mentioned preparation method of nitrogen-doped graphene-supported platinum nanoparticle material specifically comprises the following steps:

[0045] (1) Graphene Preparation

[0046] Graphene oxide is obtained from graphite flakes through an improved oxidation method. Add 1-3g of graphite flakes to 1-5g of potassium persulfate and 1-5g of phosphorus pentoxide, then add 100-200ml of concentrated sulfuric acid, oxidize at a high temperature of 50-100°C, and then use 1-10g of high-temperature Potassium manganate is oxidized, and graphene is obtained through several times of centrifugal cleaning.

[0047] (2) Preparation of nitrogen-doped graphene

[0048] After 20-40 mg of graphene-based material is ultrasonically treated, 1-10 g of urea heteroatom precursor is added, and N doping is carried out in a hydrothermal kettle at a high tempe...

Embodiment 3

[0052] A Pt / P, N-G material of phosphorus and nitrogen doped graphene supported platinum nanoparticles, containing Pt, C, P, N, H and O elements.

[0053] The above-mentioned preparation method of phosphorus-nitrogen-doped graphene-supported platinum nanoparticle material specifically comprises the following steps:

[0054] (1) Preparation of graphene

[0055] Graphene oxide is obtained from graphite flakes through an improved oxidation method. Add 1-3g of graphite flakes to 1-5g of potassium persulfate and 1-5g of phosphorus pentoxide, then add 100-200ml of concentrated sulfuric acid (98%), oxidize at a high temperature of 50-100°C, and then use 1-10g of potassium permanganate is oxidized, and graphene is obtained through several times of centrifugal cleaning.

[0056] (2) Preparation of phosphorus and nitrogen doped graphene

[0057] After 20-40mg of graphene is ultrasonically treated, the heteroatom precursors of sodium hypophosphite and urea with a mass ratio of 1:1 are...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of heteroatom doped graphene-based material supported noble metal nanoparticles. The preparation method comprises steps as follows: preparation of a heteroatom doped graphene-based material: a graphene-based material is subjected to ultrasonic treatment, a heteroatom precursor is added, heteroatom doping is performed in a hydrothermal kettle at the temperature of 150-200 DEG C, and the heteroatom doped graphene-based material is obtained; preparation of the heteroatom doped graphene-based material supported noble metal nanoparticles: the heteroatom doped graphene-based material is dissolved in deionized water and subjected to ultrasonic treatment, a stabilizer and a metal precursor are added, metal in the metal precursor is platinum, palladium, gold or silver, the mixture is continuously stirred, pH is adjusted to range from 8 to 14, a reduction agent is added, the mixture is continuously stirred, and the heteroatom doped graphene-based material supported noble metal nanoparticles are obtained after vacuum drying. The synergistic effect of the heteroatom and the carrier on noble metal is used, the activity and the stability of a catalyst are effectively improved, and a preparation process is simple and suitable for industrial production and has higher economic value.

Description

technical field [0001] The invention belongs to the field of materials science, and relates to a fuel cell anode catalyst material, in particular to a preparation method of a heteroatom-doped graphene-based material loaded with noble metal nanoparticles. Background technique [0002] With the continuous development of the current era, direct alcohol fuel cells have become a suitable substitute for resource and energy crisis power generation due to their advantages such as high energy density and non-polluting products. As we all know, electrocatalyst is the core of fuel cells, which is also the key to limit the commercialization of fuel cells. The catalysts of direct alcohol fuel cells are mainly noble metals, but noble metals are expensive, have low reserves and are easily poisoned by the reaction intermediate CO. In this way, noble metals are usually combined with carbon-based materials, such as activated carbon, carbon spheres, mesoporous carbon, carbon nanotubes, graphe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/88H01M4/92B82Y30/00B82Y40/00
CPCB82Y30/00B82Y40/00H01M4/8817H01M4/8825H01M4/926Y02E60/50
Inventor 徐群杰刘其林艳吴桐范金辰蔡文斌
Owner SHANGHAI UNIVERSITY OF ELECTRIC POWER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com