Modified PCT resin compound and preparing method thereof

A resin composite and modification technology, applied in the field of modified PCT resin composite and its preparation, can solve the problems of poor processing fluidity, poor processing performance, unstable injection pressure, etc., and achieve improved tensile strength and good processing. Performance, simple effect of raw materials

Active Publication Date: 2016-05-25
JIANGSU WATER SPECIAL MATERIAL MFG CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a modified PCT resin compound and a preparation method thereof to solve the problems of poor processing fluidity and unstable injection pressure in the injection molding process of existing PCT resins.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified PCT resin compound and preparing method thereof
  • Modified PCT resin compound and preparing method thereof
  • Modified PCT resin compound and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] In the preparation process of the above-mentioned wholly aromatic liquid crystal polyester resin, a solution polycondensation method or a bulk polycondensation method may be used. In order to promote the polycondensation reaction, an acylating agent can be used to pretreat the raw materials during the synthesis of the wholly aromatic liquid crystal polyester prepolymer, especially an acetylating agent can be used for pretreatment.

[0033] In the above-mentioned solid-state polycondensation reaction (solid-state polycondensation reaction), it is necessary to provide appropriate heat to the wholly aromatic liquid crystal polyester prepolymer. The specific heat supply can be through methods such as heating plates, hot air, and high-temperature fluids, and in order to remove solid-state polycondensation reactions. By-products can be removed with an inert gas purge or vacuum.

[0034] In any embodiment, the first filler is at least one of glass fiber, whisker, polytetrafluo...

Embodiment 1

[0050] A modified PCT resin composite, comprising the following components in parts by weight:

[0051]

[0052] The preparation method of the modified PCT resin compound that embodiment 1 provides is as follows:

[0053]Step S01, 30 parts of PCT resin (produced by American Eastman Chemical Company), 30 parts of fully aromatic liquid crystal polyester resin (produced by Jiangsu Water Special Materials Co., Ltd.), 30 parts of titanium dioxide, and 10 parts of glass fiber were placed in Dry at 130°C for 4 hours;

[0054] Step S02, putting the dried PCT resin, glass fiber, titanium dioxide and wholly aromatic liquid crystal polyester resin into an automatic mixer and mixing evenly to obtain a mixed material;

[0055] Step S03, putting the mixture obtained in step S02 into a twin-screw extruder for melting and kneading, and then extruding, drawing, cooling, and granulating to obtain a modified PCT resin compound.

Embodiment 2

[0057] A modified PCT resin composite, comprising the following components in parts by weight:

[0058]

[0059] The preparation method of the modified PCT resin compound that embodiment 2 provides is as follows:

[0060] Step S01, 40 parts of PCT resin (produced by American Eastman Chemical Company), 20 parts of fully aromatic liquid crystal polyester resin (produced by Jiangsu Water Special Materials Co., Ltd.), 30 parts of titanium dioxide, and 10 parts of glass fiber were placed in Dry at 130°C for 4 hours;

[0061] Step S02, putting the dried PCT resin, glass fiber, titanium dioxide and wholly aromatic liquid crystal polyester resin into an automatic mixer and mixing evenly to obtain a mixed material;

[0062] Step S03, putting the mixture obtained in step S02 into a twin-screw extruder for melting and kneading, and then extruding, drawing, cooling, and granulating to obtain a modified PCT resin compound.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of polymer-based composites and particularly discloses a modified PCT resin compound and a preparing method thereof. The modified PCT resin compound is prepared from, by weight, 30-70 parts of PCT resin, 10-40 parts of liquid crystal polyester resin, 5-40 parts of first filler and 10-40 parts of second filler. The modified PCT resin compound has a large reflective rate; moreover, tensile strength is improved obviously, melt viscosity and the average change rate of injection molding pressure are reduced greatly, and finally the processability of the PCT resin compound is improved greatly.

Description

technical field [0001] The invention relates to the technical field of polymer composite materials, in particular to a modified PCT resin composite and a preparation method thereof. Background technique [0002] Because poly-1,4-cyclohexanedimethylene terephthalate (English abbreviation: PCT) has good chemical resistance, processability, dimensional stability and heat resistance, it is especially suitable for material performance requirements. strict field. In view of the characteristics of PCT, up to now, it has been widely used in industries such as automobiles, electronics and electrical industries, especially as a raw material for LED reflectors. [0003] From the perspective of the development trend of LED, with the development of LED-related fields, in order to improve the light-gathering effect, the structure of LED reflectors is becoming more and more complex, which puts forward further requirements for the processing performance of PCT raw materials for manufacturi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L67/00C08L77/00C08K7/14C08K3/22
CPCC08L67/00C08L67/02C08L77/00C08K7/14C08K2003/2241
Inventor 金东植高海燕杨云飞周小宇
Owner JIANGSU WATER SPECIAL MATERIAL MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More