Warm white fluorescent powder excited by ultraviolet LED
A phosphor, warm white technology, applied in the field of rare earth luminescent materials, can solve the problems of low excitation efficiency, high cost, poor stability of phosphors, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0033] Example 1: In 0.974 Dy 0.01 Tm 0.01 Eu 0.006 NbO 4 Preparation of phosphor
[0034] Weigh 0.9701gNb 2 O 5 , 0.9869gIn 2 O 3 , 0.0136gDy 2 O 3 , 0.0141gTm 2 O 3 And 0.0077g Eu, grind in an agate mortar for 15 minutes to mix the raw materials uniformly. The mixed raw materials are placed in a corundum crucible, and the temperature is raised to 1000°C at a rate of 5°C / min in a resistance furnace for the first stage sintering, and the sintering time is 12h. Then with the furnace cooling, the sintered product was ground for 10 minutes, and then heated to 1250°C at a rate of 5°C / min for the second stage sintering, and the sintering time was 24 hours. After cooling in the furnace, grinding, you can get the composition of In 0.98 Dy 0.01 Tm 0.01 NbO 4 Of phosphors.
Example Embodiment
[0035] Example 2: In 0.98 Dy 0.01 Tm 0.01 NbO 4 Preparation of phosphor
[0036] Weigh 0.9701gNb 2 O 5 , 0.9930gIn 2 O 3 , 0.0136gDy 2 O 3 And 0.0141gTm 2 O 3 , The remaining steps are the same as in Example 1.
Example Embodiment
[0037] Example 3: In 0.97 Dy 0.01 Tm 0.01 Eu 0.01 NbO 4 Preparation of phosphor
[0038] Weigh 0.9701gNb 2 O 5 , 0.9869gIn 2 O 3 , 0.0136gDy 2 O 3 , 0.0141gTm 2 O 3 And 0.0128gEu, and the remaining steps are the same as in Example 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap