Method for preparing pyrite phase iron disulfide thin film
A technology of iron disulfide and pyrite, which is applied in the field of photoelectric materials and new energy materials, can solve the problems such as difficult to obtain iron disulfide film of pyrite phase, and achieve the effect of solving the problem of sulfur vacancy and overcoming sulfur vacancy
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032] (1) Add 1.39g of ferrous sulfate heptahydrate and 0.83g of polyvinylpyrrolidone into 20ml of deionized water, stir for half an hour and add 0.76g of thiourea; transfer the above solution to the inner lining of the autoclave, and add 0.64g of sulfur powder , add an appropriate amount of ethanol to make the liquid volume reach about 80% of the volume of the autoclave lining. The autoclave was placed in a box furnace and heated at 200°C for 24 hours. After the temperature is cooled to room temperature, the liquid in the autoclave lining is poured out, washed with ethanol, deionized water, and carbon disulfide in sequence, and finally the powder is dried in an oven for use. figure 2 It is the scanning electron micrograph of this embodiment product; Figure 5 Be the X-ray diffraction result of this embodiment product; Image 6 It is the Raman result of the product of this example.
[0033] (2) Add 0.1 g of iron disulfide powder to 5 ml of ethanol, add 0.1 g of terpineol ...
Embodiment 2
[0038] (1) Add 10ml of oleylamine to a three-necked bottle protected by nitrogen, add 0.20g of ferrous chloride tetrahydrate, and keep the temperature at 120°C for 1 hour to obtain solution A; in another container protected by nitrogen, add 0.19g Dissolve sulfur powder in 5ml of diphenyl ether, react at 70°C for 1 hour to obtain solution B; inject solution B into solution A through a needle, react at 220°C for 24 hours, then cool to room temperature. Rinse with absolute ethanol and chloroform several times, and finally dry the powder in an oven for use. image 3 It is the scanning electron micrograph of this embodiment product; Figure 5 Be the X-ray diffraction result of this embodiment product; Image 6 It is the Raman result of the product of this example.
[0039] (2) Add 0.1 g of iron disulfide powder to 5 ml of ethanol, add 0.1 g of terpineol and 0.4 g of ethyl cellulose, and stir magnetically for one day.
[0040] (3) ultrasonically clean the FTO conductive glass and...
Embodiment 3
[0044] (1) Add 1.39g of ferrous sulfate heptahydrate and 0.83g of polyvinylpyrrolidone into 20ml of deionized water, stir for half an hour and add 0.76g of thiourea; transfer the above solution to the inner lining of the autoclave, and add 0.64g of sulfur powder , add an appropriate amount of ethanol to make the liquid volume reach about 80% of the volume of the autoclave lining. The autoclave was placed in a box furnace and heated at 200°C for 39 hours. After the temperature is cooled to room temperature, the liquid in the autoclave lining is poured out, washed with ethanol, deionized water, and carbon disulfide in sequence, and finally the powder is dried in an oven for use. Figure 4 It is the scanning electron micrograph of this embodiment product; Figure 5 Be the X-ray diffraction result of this embodiment product; Image 6 It is the Raman result of the product of this example.
[0045] (2) Add 0.1 g of iron disulfide powder to 5 ml of ethanol, add 0.1 g of terpineol ...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com