Textile reinforced cement matrix composite board for reinforcement of concrete flexural members and production method thereof

A fiber woven mesh and reinforced cement technology, used in building maintenance, manufacturing tools, building construction, etc., can solve the problems of fiber material peeling damage, board cracking, etc., to delay cracking, improve bearing capacity, and increase ductility. Effect

Inactive Publication Date: 2016-07-20
HUNAN UNIV
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So as to effectively solve the problem that the fiber material is prone to peeling damage an

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Textile reinforced cement matrix composite board for reinforcement of concrete flexural members and production method thereof
  • Textile reinforced cement matrix composite board for reinforcement of concrete flexural members and production method thereof
  • Textile reinforced cement matrix composite board for reinforcement of concrete flexural members and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] as attached Figure 4 As shown, a fiber braided mesh reinforced cement-based composite plate for reinforcement of concrete flexural members and a manufacturing method thereof, comprising the following steps:

[0036] 1) Lay the mold flat accurately, the mold size is 2100mm×150mm×25mm (length×width×height);

[0037] 2) Arrange 5mm thick bottom positioning strips;

[0038] 3) Prepare the steel fiber reinforced cement matrix (3), and pour it on the formwork with a thickness of 5mm as the bottom protective layer; the mix ratio of the steel fiber reinforced cement matrix (3) is: 52.5 Portland cement 800kg / m 3 , superfine fly ash 100kg / m 3 , silica fume 100kg / m 3 , 800kg / m of silica sand with a particle size of 0-0.6mm 3 , silica sand with a particle size of 0.6-1.2mm 400kg / m 3 , steel fiber 85kg / m 3 , water 286kg / m 3 , superplasticizer 2.0kg / m 3 The preparation method of the steel fiber reinforced cement matrix (3) is: put cement, fly ash, silica fume, sand, steel fi...

Embodiment 2

[0047] as attached Figure 5 As shown, a fiber braided mesh reinforced cement-based composite plate for reinforcement of concrete flexural members and a manufacturing method thereof, comprising the following steps:

[0048]1) Lay the mold flat accurately, the mold size is 2100mm×150mm×25mm (length×width×height);

[0049] 2) Arrange 3mm thick bottom positioning strips;

[0050] 3) Prepare the steel fiber reinforced cement matrix (3), and pour it on the formwork with a thickness of 3 mm as the bottom protective layer; the mix ratio of the steel fiber reinforced cement matrix (3) is: 52.5 Portland cement 800kg / m 3 , superfine fly ash 100kg / m 3 , silica fume 100kg / m 3 , 800kg / m of silica sand with a particle size of 0-0.6mm 3 , silica sand with a particle size of 0.6-1.2mm 400kg / m 3 , steel fiber 85kg / m 3 , water 286kg / m 3 , superplasticizer 2.0kg / m 3 The preparation method of the steel fiber reinforced cement matrix (3) is: put cement, fly ash, silica fume, sand, steel fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a textile reinforced cement matrix composite board for reinforcement of concrete flexural members and a production method thereof. The textile reinforced cement matrix composite board comprises a prestressed textile (1), shearing chopped steel fibers (2), a steel fiber reinforced cement matrix (3) and an ordinary cement matrix (4), wherein the shearing chopped steel fibers (2) are vertically inserted into mesh holes of the prestressed textile (1), the steel fiber reinforced cement matrix (3) is poured on protective layers at the top and the bottom of the composite board, the ordinary cement matrix (4) is poured between layers of the prestressed textile (1), and the prestressed textile (1) is a carbon textile or glass textile. When the concrete flexural members are reinforced by the composite board, the problem that fiber materials are easy to peel off during reinforcement of external bonding of FRP is solved. The composite board has the advantages of slowing down cracks, improving ductility and giving full play to high-strength characteristics of fiber materials.

Description

technical field [0001] The invention relates to the technical field of building structure reinforcement, in particular to a fiber braided mesh-reinforced cement-based composite plate for reinforcement of concrete bending members and a manufacturing method thereof. Background technique [0002] In recent years, with the rapid development of my country's economy, the loads of various buildings are increasing day by day. In addition to the aging of the buildings themselves, various natural disasters and man-made damages, existing buildings continue to produce various safety hazards. According to a conservative estimate, more than 40% of the existing reinforced concrete building area in my country needs to be identified and reinforced in stages and batches. It can be seen that the reinforcement of building structures will definitely become an important branch of the construction industry. Therefore, it is very necessary to develop and research reliable reinforcement technology f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): E04G23/02B28B23/04
CPCB28B23/043E04G23/0218
Inventor 周芬刘玲玲杜运兴
Owner HUNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap