Preparation method of titanium dioxide film layer without cracking due to heating

A titanium dioxide and film technology, which is applied in the field of titanium dioxide film preparation, can solve the problems of easy cracking, unstable drying performance, harsh experimental conditions for the formation of titanium dioxide film, etc., and achieves a simple and easy preparation process and stable performance at room temperature and high temperature. Effect

Active Publication Date: 2016-08-17
合肥名龙电子科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the defects in the prior art that the experimental conditions for the formation of the titanium dioxide film layer are harsh, and the obtained titanium dioxide film layer is naturally dried in the air or under heating conditions, the drying performance is unstable and easy to crack, etc., the present invention provides a titanium dioxide film that does not crack when heated. The preparation method of the film layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of titanium dioxide film layer without cracking due to heating
  • Preparation method of titanium dioxide film layer without cracking due to heating
  • Preparation method of titanium dioxide film layer without cracking due to heating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 1. Preparatory work: take the beaker, glass rod, and measuring cylinder, and dry them in an oven; soak the stirring magnet in alcohol for cleaning; soak the clean glass slices in hydrofluoric acid for 4 minutes, take them out and rinse them with deionized water, and set aside.

[0022] 2. Preparation of Sol-Gel TiO

[0023] Take 2 beakers and add 10.00mL of ethanol respectively, labeled A and B, add 1.00mL of acetic acid and 1.50mL of distilled water into beaker A with a rubber dropper, and then stir for 10 minutes at a stirring speed of 3900r / min ;Add 4.50mL n-tetrabutyl titanate to the B beaker, and then stir for 9-11 minutes at a stirring speed of 3900r / min; Add the solution in the B beaker to the A beaker drop by drop at a rate of 3 drops / second , After the dropwise addition was completed, stir with magnetic force at room temperature for 30 minutes to form a light blue solution, and let it stand for 24 hours.

[0024] 3. Hydrothermal synthesis treatment

[0025] D...

Embodiment 2

[0033] It is basically the same as that in Example 1, except that the film is formed on the surface of the phosphor powder, and the obtained film layer is uniform without cracking.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a titanium dioxide film layer without cracking due to heating. The preparation method comprises the following sequential steps: 1), preparing sol-gel titanium dioxide; 2) performing hydro-thermal synthesis; and 3) performing film forming. According to the preparation method of the titanium dioxide film layer without cracking due to heating, disclosed by the invention, a film layer with stable normal temperature and high temperature performances, uniformly and no cracking can be formed on the surfaces of fluorescent powder, glass and the like, and the preparation process is simple and feasible.

Description

technical field [0001] The invention relates to a method for preparing a titanium dioxide film that does not crack when heated, and belongs to the technical field of surface film preparation. Background technique [0002] The coating method is used to form a layer of transparent conductive material on the surface of phosphor particles, which can not only improve the conductivity, relieve the current saturation effect, but also serve as a protective layer to improve the anti-deterioration performance. There is very little research work on this aspect at home and abroad. In 2005, for EL devices, Sang-Do Han et al. used tetraisopropyl titanate as the precursor to use sol-gel method and heat treatment in nitrogen to coat TiO on the surface of ZnS:Cu,Cl. 2 , studied the relationship between photoluminescence and electroluminescence properties and experimental conditions. In 2007, Lihong Xue et al. used the sol-gel method involving the hydrolytic polymerization process of butyl ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09K11/02C03C17/23
CPCC03C17/23C03C2217/212C09K11/025
Inventor 郭萍朱宪忠曾明敏张彦娜
Owner 合肥名龙电子科技有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com