Tobacco-stem-powder plastic with tobacco smell and preparation method thereof

A tobacco rod powder and plastic technology, which is applied in the field of plastic products, can solve problems such as safety hazards and environmental pollution, and achieve the effects of reduced use, simple operation, and long service life

Inactive Publication Date: 2016-08-31
JIANGSU JINHE HI TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Tobacco is one of the main economic plants in Yunnan. After the tobacco is harvested, a large amount of tobacco stalks become agricultural waste. Usually, they are simply incinerated, which pollutes the environment and creates safety hazards.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The method for preparing tobacco rod powder plastic raw materials provided by the invention has low cost, simple operation, stable performance of raw material particles, and convenient production.

[0032] The invention provides a cigarette rod powder plastic with tobacco smell, which comprises the following raw materials in parts by weight: 6-10 parts of talcum powder, 4-6 parts of diatomaceous earth, 40-60 parts of high molecular polymer, plastic additives 4 to 5 parts and 25 to 35 parts of tobacco rod powder.

[0033] In a preferred solution, the tobacco rod powder plastic includes the following raw materials in parts by weight: 6-9 parts of talcum powder, 5-6 parts of diatomaceous earth, 45-55 parts of high molecular polymer, and 4-5 parts of plastic additives. 30-35 parts of tobacco rod powder.

[0034] In an optimal solution, the tobacco rod powder plastic includes the following raw materials in parts by weight: 9 parts of talcum powder, 5 parts of diatomaceous e...

Embodiment 1

[0046] This embodiment provides a method for preparing tobacco rod powder plastic, and the required raw materials are tobacco rod powder, talcum powder, diatomaceous earth, high molecular polymer and plastic additives. The above raw materials were weighed in the following parts by weight: 30 parts of tobacco rod powder, 6 parts of talcum powder, 4 parts of diatomaceous earth, 56 parts of high molecular polymer and 4 parts of plastic additives. Wherein, the high-molecular polymer is high-density polyethylene, the plastic additive is a titanate coupling agent, and the particle size of the tobacco stalk powder is 300 mesh.

[0047] Its specific production process is as follows:

[0048] 1. Mix tobacco rod powder, talcum powder, diatomaceous earth and plastic additives and heat up to 80°C to obtain mixture A;

[0049] 2. Add the high molecular polymer to the mixture A, then raise the temperature to 120°C for water removal treatment, and then transfer to the mixture B;

[0050] 3. ...

Embodiment 2

[0053] This embodiment provides a method for preparing tobacco rod powder plastic, and the required raw materials are tobacco rod powder, talcum powder, diatomaceous earth, high molecular polymer and plastic additives. The above raw materials were weighed in the following parts by weight: 35 parts of tobacco rod powder, 10 parts of talcum powder, 6 parts of diatomaceous earth, 40 parts of high molecular polymer and 5 parts of plastic additives. Wherein, the high molecular polymer is low-density polyethylene, the plastic additive is stearic acid, and the particle size of the tobacco rod powder is 350 mesh.

[0054] Its specific production process is the same as in Example 1, and will not be repeated here.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides tobacco-stem-powder plastic with tobacco smell and a preparation method thereof and relates to the field of plastic products. The tobacco-stem-powder plastic comprises, by weight, 6-10 parts of talcum powder, 4-6 parts of diatomite, 40-60 parts of high-molecular polymer, 4-5 parts of plastic additives and 25-35 parts of tobacco stem powder. The preparation method includes: mixing the tobacco stem powder with the fineness being 300-350 meshes with the talcum powder, the diatomite, the high-molecular polymer and the plastic additives to obtain raw materials, and using a double-screw mixer-extruder to performing extrusion granulation to form the raw material granules for preparing the tobacco-stem-powder plastic. The tobacco-stem-powder plastic has the advantages that the tobacco-stem-powder plastic is prepared by using tobacco stems as the raw material, the agricultural waste tobacco stems are processed in a harmless manner, a new tobacco stem processing method is provided, the traditional processing method using incineration is abandoned, environment pollution caused by the incineration is reduced, waste recycling of the tobacco stems is achieved, and the economic value of the tobacco stems is increased.

Description

technical field [0001] The invention relates to the field of plastic products, in particular to tobacco rod powder plastics with tobacco smell and a preparation method thereof. Background technique [0002] With the great development of the plastics industry and a large number of applications of plastics, the problem of waste plastics is becoming more and more serious. Traditional plastics cannot be naturally degraded after being discarded and cause serious pollution to soil, groundwater and air. Direct recycling is half the effort and inefficient. The resulting white pollution has become a global problem, and the pressure on environmental protection is extremely huge. [0003] Tobacco is one of the main economic plants in Yunnan. After the tobacco is harvested, a large amount of tobacco stalks become agricultural waste. Usually, they are simply incinerated, which pollutes the environment and creates safety hazards. [0004] The inventors of the present application creativ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/12C08L97/02C08L51/06C08K13/02C08K3/34
CPCC08L23/06C08L23/12C08L2205/035C08L97/02C08K3/34C08K3/346C08L51/06C08K13/02
Inventor 殷正福
Owner JIANGSU JINHE HI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap