Glass fiber reinforced ASA (acrylonitrile-styrene-acrylate copolymer)/PETG (polyethylene terephthalate glycol) alloy material and preparation method thereof

A technology of alloy material and ASA resin, which is applied in the field of glass fiber reinforced ASA/PETG alloy material and its preparation, can solve the problems of poor PC processing formability, material application limitations, poor toughness of PBT resin, etc., and achieve excellent mechanical properties with a simple method easy effect

Active Publication Date: 2016-09-07
SHANGHAI KUMHOSUNNY JINSHAN PLASTICS CO LTD
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] After searching, CN104845284A discloses a modified PET / PTT / PETG composite material, but the preparation method of glass fiber reinforcement is not mentioned in the patent
CN 102911487 A discloses a glass fiber reinforced PBT / ASA alloy material and a preparation method thereof, but the toughness of PBT resin is too poor, and the application range of the material is limited
CN 104693767 A discloses a glass fiber reinforced PC alloy material and its preparation method, but PC has poor formability and the application of the material is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass fiber reinforced ASA (acrylonitrile-styrene-acrylate copolymer)/PETG (polyethylene terephthalate glycol) alloy material and preparation method thereof
  • Glass fiber reinforced ASA (acrylonitrile-styrene-acrylate copolymer)/PETG (polyethylene terephthalate glycol) alloy material and preparation method thereof
  • Glass fiber reinforced ASA (acrylonitrile-styrene-acrylate copolymer)/PETG (polyethylene terephthalate glycol) alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The components of the glass fiber reinforced ASA / PETG alloy material provided in this embodiment and the weight ratio of each component are:

[0024]

[0025] The preparation method is as follows:

[0026] (a) Add ASA resin, PETG resin, compatibilizer, antioxidant, and lubricant into the mixing mixer for 10 minutes;

[0027] (b) The mixture obtained in step a is main-fed through a twin-screw extruder, and the glass fiber is side-fed, blended and granulated to obtain a glass fiber reinforced ASA / PETG alloy material.

Embodiment 2

[0029] The components of the glass fiber reinforced ASA / PETG alloy material provided in this embodiment and the weight ratio of each component are:

[0030]

[0031] The preparation method is as follows:

[0032] (a) ASA resin, PETG resin, compatibilizer, antioxidant, lubricant are added in the mixing mixer and mixed for 15 minutes;

[0033] (b) The mixture obtained in step a is main-fed through a twin-screw extruder, and the glass fiber is side-fed, blended and granulated to obtain a glass fiber reinforced ASA / PETG alloy material.

Embodiment 3

[0035] The components of the glass fiber reinforced ASA / PETG alloy material provided in this embodiment and the weight ratio of each component are:

[0036]

[0037] The preparation method is as follows:

[0038] (a) ASA resin, PETG resin, compatibilizer, antioxidant, lubricant are added in the mixing mixer and mixed for 20 minutes;

[0039] (b) The mixture obtained in step a is main-fed through a twin-screw extruder, and the glass fiber is side-fed, blended and granulated to obtain a glass fiber reinforced ASA / PETG alloy material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a glass fiber reinforced ASA (acrylonitrile-styrene-acrylate copolymer) / PETG (polyethylene terephthalate glycol) alloy material and a preparation method thereof. The ASA / PETG alloy material is prepared from, by weight, 30-60 parts of ASA resin, 30-60 parts of PETG resin, 10-30 parts of glass fibers, 0.5-2 parts of a compatilizer, 0.1-1 part of an antioxidant and 0.1-1 part of a lubricant. The preparation method includes steps: (a) adding the ASA resin, the PETG resin, the compatilizer, the antioxidant and the lubricant into a mixer to realize mixing; (b) after side feeding of the glass fibers and main feeding of a mixture obtained at the step through a double-screw extruder, blending and granulating to obtain the material. The method is simple and feasible; by the compatilizer, the ASA, the PETG and the glass fibers are combined more steadily, and the glass fiber reinforced ASA / PETG alloy material has excellent mechanical properties, fluidity and dimensional stability and suitable for automotive complex structural interior decoration parts such as speaker covers and defogging grilles.

Description

technical field [0001] The invention belongs to the fields of polymer blending and polymer molding processing, and in particular relates to a glass fiber reinforced ASA / PETG alloy material and a preparation method thereof. Background technique [0002] ASA resin (acrylonitrile-styrene-butyl acrylate copolymer) is a thermoplastic polymer material structure with high strength, good toughness, good light resistance, and easy processing and molding. [0003] PETG is a transparent, non-crystalline copolyester. The common comonomer of PETG is 1,4-cyclohexanedimethanol, which is called polyethylene terephthalate-1,4-cyclohexanedimethanol. ester. It is a polycondensation product of three monomers of terephthalic acid (PTA), ethylene glycol (EG) and 1,4-cyclohexanedimethanol (CHDM) by transesterification. Compared with PET, it has more 1,4 -Cyclohexanedimethanol comonomer has more ethylene glycol comonomer than PCT, so the performance of PETG is quite different from PET and PCT. P...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L51/00C08L67/02C08K13/04C08K7/14C08K5/098C08K5/20
CPCC08K2201/003C08L51/003C08L67/02C08L2205/025C08L2205/03C08K13/04C08K7/14C08K5/098C08K5/20
Inventor 周中玉李强罗明华辛敏琦
Owner SHANGHAI KUMHOSUNNY JINSHAN PLASTICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com