Antibiotic environmentally-friendly film and production method thereof

An antibacterial environmental protection film and antibacterial layer technology, applied in the field of antibacterial environmental protection film and its preparation, can solve the problems of easy water absorption and deterioration, poor environmental protection performance, short antibacterial time, etc., achieve good sterilization and antivirus effects, good durability, and long service life Effect

Active Publication Date: 2016-09-07
广东保特信新材料科技有限公司
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although existing inorganic metal antibacterial coatings have antibacterial properties, such as using nano-silver as a bactericidal component, the antibacterial time is short, prone to oxidation and loss, and is easy to be stained with dust, easy to absorb water and deteriorate, low in hardness, easy to damage, easy to fall off, and Environmental performance is poor
Traditional fungicides usually contain toxic substances, and formaldehyde, a carcinogen, will be produced after coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibiotic environmentally-friendly film and production method thereof
  • Antibiotic environmentally-friendly film and production method thereof
  • Antibiotic environmentally-friendly film and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of antibacterial environmental protection film, described antibacterial environmental protection film is PET layer, antibacterial layer, PE layer, bactericidal coating successively from inside and outside, wherein, the thickness of PET layer and PE layer is 25 μ m, the difference between bactericidal coating and antibacterial layer The thicknesses are all 50 μm.

[0035] The coating that described antibacterial layer is used is to be formulated by the raw material of following weight part:

[0036]

[0037] The used coating of described antibacterial agent layer is prepared by the following method:

[0038] (1) Preparation of pre-emulsion

[0039] Polylactic acid, hydroxypropyl acrylate, emulsifier, initiator, trifluoropropylmethyldichlorosilane, vinyl triisopropoxysilane, polyvinyl alcohol and 1 / 2 weight part of deionized mixed with water, pre-emulsified to obtain a pre-emulsion;

[0040] (2) Emulsion polymerization

[0041] The hydroxypropyl methylcellul...

Embodiment 2

[0048] An antibacterial environmental protection film, the antibacterial environmental protection film is a PET layer, an antibacterial layer, a PE layer, and a bactericidal coating in sequence from the inside to the outside, wherein the thickness of the PET layer is 22 μm, the thickness of the antibacterial layer is 50 μm, and the thickness of the PE layer is 25 μm , The thickness of the bactericidal coating is 53μm.

[0049] The coating that described antibacterial layer is used is to be formulated by the raw material of following weight part:

[0050]

[0051] The used coating of described antibacterial agent layer is prepared by the following method:

[0052] (1) Preparation of pre-emulsion

[0053] Polylactic acid, hydroxypropyl acrylate, emulsifier, initiator, trifluoropropylmethyldichlorosilane, vinyl triisopropoxysilane, polyvinyl alcohol and 3 / 4 weight part of deionized mixed with water, pre-emulsified to obtain a pre-emulsion;

[0054] (2) Emulsion polymerizati...

Embodiment 3

[0063] An antibacterial environmental protection film, the antibacterial environmental protection film is a PET layer, an antibacterial layer, a PE layer, and a bactericidal coating in sequence from the inside to the outside, wherein the thickness of the PET layer is 30 μm, the thickness of the antibacterial layer is 55 μm, and the thickness of the PE layer is 24 μm , The thickness of the bactericidal coating is 60μm. .

[0064] The coating that described antibacterial layer is used is to be formulated by the raw material of following weight portion:

[0065]

[0066]

[0067] The used coating of described antibacterial agent layer is prepared by the following method:

[0068] (1) Pre-emulsion preparation

[0069] Polylactic acid, hydroxypropyl acrylate, emulsifier, initiator, trifluoropropylmethyldichlorosilane, vinyl triisopropoxysilane, polyvinyl alcohol and 3 / 5 parts by weight of deionized mixed with water, pre-emulsified to obtain a pre-emulsion;

[0070] (2) Em...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antibiotic environmentally-friendly film and a production method thereof. The antibiotic environmentally-friendly film sequentially comprises a PET layer, an antibiotic layer, a PE layer and a sterilization coating layer from inside to outside, wherein the antibiotic layer is produced from polylactic acid, hydroxypropyl acrylate, acryloyl chloride, trifluoropropylmethyldichlorosilane, vinyltriisopropoxysilane, hydroxypropyl methyl cellulose, chitosan, eugenol, polyvinyl alcohol, an emulsifier, an initiator and deionized water, and the sterilization coating layer is produced from ethanol, polyethylene glycol, deionized water, cinnamaldehyde, beta-cyclodextrin, a titanate coupling agent, nanometer titanium dioxide, organosilicone resin, a dispersant and an antifoaming agent. The antibiotic environmentally-friendly film produced in the invention has the advantages of good sterilization and antivirus effects, good durability, long service life and no pollution to environment.

Description

technical field [0001] The invention belongs to the technical field of films, in particular to an antibacterial and environment-friendly film and a preparation method thereof. Background technique [0002] With the advancement of science and technology and the rapid development of modern industry, environmental problems are becoming more and more serious. As people pay more attention to health and gradually increase their awareness of environmental protection, the demand for antibacterial and air-purifying architectural glass films is becoming increasingly urgent. Although existing inorganic metal antibacterial coatings have antibacterial properties, such as using nano-silver as a bactericidal component, the antibacterial time is short, prone to oxidation and loss, and is easy to be stained with dust, easy to absorb water and deteriorate, low in hardness, easy to damage, easy to fall off, and Environmental performance is poor. Traditional fungicides usually contain toxic s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D151/08C09D7/12C09D5/14B32B27/36B32B27/08B32B27/32B32B33/00
CPCB32B27/08B32B27/32B32B27/36B32B33/00B32B2250/246B32B2255/10B32B2255/26B32B2307/7145B32B2323/04B32B2367/00C08K2003/2241C08K2201/011C08K2201/014C08L2201/08C08L2205/02C08L2205/025C08L2205/035C08L2205/16C09D5/14C09D7/63C09D7/65C09D151/08C09D183/04C08L1/284C08L5/08C08L29/04C08K5/00C08K5/54C08L71/02C08L5/16C08K13/02C08K2003/2237C08K5/05C08K5/0058C08K5/5419C08K3/22C08K5/13C08L83/04C08K5/07
Inventor 张佳斌
Owner 广东保特信新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com