Preparation method of thermal-insulation external tile

A technology for thermal insulation of external walls and adobes, which is applied in the field of ceramic tile manufacturing, which can solve the problems of poor cold resistance and thermal insulation of ceramic tiles, and achieve the effects of excellent anti-seepage performance, stable heating performance, and not easy to be oxidized

Inactive Publication Date: 2016-09-28
岑溪市新建球陶瓷有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a method for preparing thermal insulation exterior wall tiles, so as to solve the problem of poor cold-proof and thermal insulation of tiles prepared by existing methods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A method for preparing thermal insulation exterior wall bricks, comprising the following raw materials in parts by weight: quartz powder: 500 kg, clay: 150 kg, expanded perlite: 50 kg, cement: 70 kg, feldspar powder: 30 kg, zircon powder: 20 kg;

[0022] Specific steps are as follows:

[0023] A, according to the weight of above-mentioned each raw material, take raw material respectively and carry out batching;

[0024] B, put the raw material of step A into the ball mill, add water of 80% of the total weight of the raw material, and the ball milling time is 5 hours;

[0025] C, after removing the iron from the sludge obtained in step B, spray it into powder, put the powder into the powder tank and stale for 22 hours;

[0026] D. The aged powder is pressed into bricks with a brick press; the pressed bricks are put into a drying kiln for drying at a temperature of 180°C for 5 hours;

[0027] E. Put the adobe obtained in step D into a firing kiln and sinter at a temper...

Embodiment 2

[0029] A method for preparing thermal insulation exterior wall bricks, comprising the following raw materials in parts by weight: quartz powder: 600 kg, clay: 200 kg, expanded perlite: 80 kg, cement: 100 kg, feldspar powder: 50 kg, zircon powder: 30 kg;

[0030] Specific steps are as follows:

[0031] A, according to the weight of above-mentioned each raw material, take raw material respectively and carry out batching;

[0032] B, put the raw material of step A into the ball mill, add water of 90% of the total weight of the raw material, and the ball milling time is 6 hours;

[0033] C. Spray powder after removing iron from the sludge obtained in step B, and put the powder into the powder tank to stale for 32 hours;

[0034] D. The aged powder is pressed into bricks with a brick press; the pressed bricks are put into a drying kiln for drying at a temperature of 260°C for 7 hours;

[0035] E. Put the adobe obtained in step D into a firing kiln and sinter at a temperature of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing thermal insulation exterior wall tiles, which relates to the technical field of ceramic tile manufacturing, and comprises the following raw materials in parts by weight: quartz powder: 50-60 parts, clay: 15-20 parts, expanded perlite: 5 parts ~ 8 parts, cement: 7 ~ 10 parts, feldspar powder: 3 ~ 5 parts, zircon powder: 2 ~ 3 parts; the preparation steps are as follows: A. Weigh each raw material for batching; B. Put the prepared raw materials in Put it into a ball mill for ball milling; C, spray powder, and make the powder stale; D, press it into bricks, put them into a drying kiln for drying; E, put the bricks into a firing kiln for sintering. Compared with the prior art, the thermal insulation exterior wall brick prepared by the present invention has excellent anti-seepage performance, stable thermal performance, not easy to be oxidized, sound insulation and heat insulation, has the function of cold and heat preservation, and is used for decoration and protection of building exterior walls. To achieve the effect of heat preservation and energy saving.

Description

technical field [0001] The invention relates to the technical field of ceramic tile manufacture, in particular to a method for preparing thermal insulation exterior wall tiles. Background technique [0002] Exterior wall bricks are mainly used for decoration and protection of building exterior walls. They not only decorate the entire building, but also play an important role in protecting walls because of their acid and alkali resistance and stable physical and chemical properties. The ceramic tile prepared by the existing method has excellent anti-seepage performance, stable heating performance, and is not easy to be oxidized, but has poor cold-proof and heat-retaining properties, and cannot achieve the effect of heat preservation and energy saving. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a method for preparing thermal insulation exterior wall tiles, so as to solve the problem of poor cold resistance and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/16C04B33/13C04B33/04
CPCC04B33/16C04B33/04C04B33/131C04B33/1315C04B2235/3427C04B2235/3463
Inventor 文亮
Owner 岑溪市新建球陶瓷有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com