A low-smoke halogen-free flame-retardant cable

A flame-retardant cable and wire core technology, applied in the direction of insulated cables, cables, circuits, etc., can solve the problem of strong resistance, and achieve the effects of good ozone resistance, low smoke, halogen-free oil resistance, and good comprehensive performance.

Active Publication Date: 2017-12-22
海悦电缆制造有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

2. Not resistant to strong polar solvents and strong acid and alkali media

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A low-smoke halogen-free flame-retardant cable

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment 1: as figure 1 As shown, the low-smoke halogen-free flame-retardant cable includes four wire cores, a polypropylene mesh tape filling layer 5 wrapped around the wire cores, a synthetic mica tape wrapping layer 6 wrapped outside the polypropylene mesh tape filling layer 5, and extruded The rubber inner sheath 7 outside the cladding layer 6 wrapped by the synthetic mica tape, the corrugated aluminum sheath 8 extruded outside the rubber inner sheath 7, and the rubber outer sheath 9 extruded outside the corrugated aluminum sheath 8. The wire core consists of a stranded tinned copper wire conductor 1, an aluminum-plastic composite tape wrapped around the stranded tinned copper wire conductor 1 and a shielding layer 2 wrapped around it, and a rubber extruded and wrapped around the aluminum-plastic composite tape wrapped around the shielding layer 2 The insulating layer 3 is composed of a tinned copper braided network pipe shielding layer 4 wrapped around the rubber...

Embodiment 2

[0025] Embodiment 2: The structure of a low-smoke, halogen-free, flame-retardant cable is the same as in Embodiment 1, except that the rubber used for the rubber insulating layer, the rubber inner sheath and the rubber outer sheath are all made by the following method:

[0026] (1) Add 1 kg of isomeric alcohol polyoxyethylene ether (EH-9) to 20 times the weight of pure water, and then add 2 kg of nano-strontium titanate with an average particle size of 40nm and nano-boron nitride with an average particle size of 600nm3 kg; Stir with a magnetic stirrer for 5 minutes, ultrasonically oscillate for 200 minutes at 85°C; then dry in an oven at 90°C for 24 hours;

[0027] (2) Nanjing Nengde Chemical Co., Ltd. (KH-792) N-2-aminoethyl-3-aminopropyltrimethoxysilane 1 kg, sec-butyl acetate 3 kg, diethylene glycol monobutyl ether 3 kg kg, mixed evenly;

[0028](3) 6 kilograms of average particle diameter 20um hydroxyapatite, 10 kilograms of average particle diameter 4um silicon dioxide, ...

Embodiment 3

[0031] Embodiment 3: The structure of a low-smoke, halogen-free, flame-retardant cable is the same as in Embodiment 1, except that the rubber used for the rubber insulation layer, the rubber inner sheath and the rubber outer sheath are all made by the following method:

[0032] (1) Add 1.5 kg of isomeric alcohol polyoxyethylene ether (EH-9) to 20 times the weight of pure water, then add 2.5 kg of nano-strontium titanate with an average particle size of 40nm, and 3.5 kg of nano-boron nitride with an average particle size of 600nm kg; Stir with a magnetic stirrer for 5 minutes, ultrasonically oscillate for 200 minutes at 85°C; then dry in an oven at 90°C for 24 hours;

[0033] (2) Nanjing Nengde Chemical Co., Ltd. (KH-792) 1.5 kg of N-2-aminoethyl-3-aminopropyltrimethoxysilane, 4 kg of sec-butyl acetate, 4 kg of diethylene glycol monobutyl ether kg, mixed evenly;

[0034] (3) 8 kilograms of average particle diameter 20um hydroxyapatite, 12 kilograms of average particle diameter...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
electrical resistivityaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-smoke halogen-free flame-retardant cable, and the cable comprises a cable core, a filling layer wrapping the cable core, a wrapping layer wrapping the filling layer, an inner sheath wrapping the wrapping layer in an extruding manner, an aluminum sheath wrapping the inner sheath in an extruding manner, and an outer sheath wrapping the aluminum sheath in an extruding manner The cable core consists of a conductor, a wrapping shielding layer wrapping the conductor, an insulating layer wrapping the wrapping shielding layer, and a shielding layer wrapping the insulating layer. The cable provided by the invention employs a special structure design, especially employs a novel rubber material, is low in smoke, is halogen-free, is excellent in resistance to oil and aging and mechanical performances, is good in resistance to ozone, flame and low temperature and insulation performances, is excellent in shielding effect, is good in integrated performance, and is suitable for the fields of petroleum, chemical and oceanographic engineering and rail traffic.

Description

technical field [0001] The invention relates to a cable, in particular to a low-smoke halogen-free flame-retardant cable. Background technique [0002] The wire and cable industry is the second largest industry in China after the automobile industry, and the product variety satisfaction rate and domestic market share both exceed 90%. Worldwide, China's wire and cable output has surpassed that of the United States, becoming the world's largest producer of wire and cable. With the rapid development of China's wire and cable industry, the number of new enterprises has been increasing, and the overall technical level of the industry has been greatly improved. The continuous and rapid growth of China's economy has provided a huge market space for cable products. The strong temptation of the Chinese market has made the world focus on the Chinese market. In just a few decades of reform and opening up, China's cable manufacturing industry The huge production capacity formed has im...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01B7/17H01B7/28H01B7/29H01B7/295H01B3/28
CPCH01B3/28H01B7/17H01B7/28H01B7/2806H01B7/2813H01B7/29H01B7/295
Inventor 李洪楼潘笑东李维维肖龙军陈兆元
Owner 海悦电缆制造有限公司