Anti-static wear-resistant noise reduction and sound insulation material and preparation method thereof

A sound insulation material, wear-resistant technology, applied in the direction of wear-resistant fibers, fiber processing, textiles and papermaking, etc. Peeling and scattering problems, to achieve the effect of light weight, outstanding wear resistance and antistatic properties, and easy preparation

Inactive Publication Date: 2016-10-12
DONGHUA UNIV
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Currently commonly used non-woven noise-reducing materials often have the disadvantage that the fibers are easy to peel off and float away, especially in non-woven noise-reducing materials made of short fibers and ultra-short fibers
Its poor wear resistance not only shortens the service life of the material, but also reduces the noise reduction efficiency during use
In addition, chemical fiber non-woven noise-reducing materials have a high specific resistance, and the charges generated on the surface of the fabric are not easy to dissipate, and accumulate to generate high static voltage, which not only hinders the improvement of the grade of noise-reducing materials, but also limits non-woven fabrics. Expansion of application fields of woven noise reduction materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-static wear-resistant noise reduction and sound insulation material and preparation method thereof
  • Anti-static wear-resistant noise reduction and sound insulation material and preparation method thereof
  • Anti-static wear-resistant noise reduction and sound insulation material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Step (1): under the condition of continuous stirring, slowly add the graphite powder into the water-based polyurethane solution, the addition ratio is 1.0% of the water-based polyurethane solution (if the water-based polyurethane is 100ml, then add 1.0g of the graphite powder); at the same time, Add a certain amount of sodium dodecylsulfonate as a dispersing aid, and the addition ratio is 0.5% of the graphite powder mass (such as adding 1.0g of graphite powder, the amount of sodium dodecylsulfonate added is 5mg), stir After 0.5h, a mixed solution was obtained.

[0030] Step (2): Wash the nonwoven fabric substrate with distilled water to remove surface impurities; then, perform alkali reduction treatment: the concentration of the alkali solution is 2%, the alkali reduction treatment time is 60 minutes, and the temperature condition is 80°C.

[0031] Step (3): Place the nonwoven material after the alkali reduction treatment in the graphite powder water-based polyurethane ...

Embodiment 2

[0033] Step (1): under the condition of continuous stirring, the graphite powder is slowly added in the water-based polyurethane solution, and the addition ratio is 2.0% of the water-based polyurethane solution (as the water-based polyurethane is 100ml, then add 2.0g of the graphite powder); meanwhile, Add a certain amount of sodium dodecyl sulfonate as a dispersing aid, and the addition ratio is 0.5% of the graphite powder mass (such as adding 2.0 g of graphite powder, the amount of sodium dodecyl sulfonate is 10 mg), stir 2h, a mixed solution was obtained.

[0034] Step (2): Wash the nonwoven fabric substrate with acetone solution to remove surface impurities; then, carry out alkali reduction treatment, the concentration of the alkali solution is 2%, the alkali reduction treatment time is 60min, and the temperature condition is 80°C.

[0035] Step (3): Place the nonwoven material after the alkali reduction treatment in the graphite powder water-based polyurethane mixed solut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an anti-static wear-resistant noise reduction and sound insulation material and a preparation method thereof. Non-woven cloth serves as a base body of the material, waterborne polyurethane and graphite powder serve as modifying agents, and a dispersing auxiliary is used for dispersing the graphite powder. The preparation method comprises the steps that the graphite powder is added into waterborne polyurethane under the stirring condition, the dispersing auxiliary is added, stirring is conducted, and a mixed solution is obtained; the non-woven cloth base body is washed, subjected to alkali-minimization treatment, placed in the mixed solution to be soaked, subjected to roll compacting treatment, dried and cured, and then the anti-static wear-resistant noise reduction and sound insulation material is obtained. The material has the high sound transmission loss decibel and the outstanding wear resistance and static resistance; in addition, the preparation method is easy to operate, low in production cost and suitable for industrialized production.

Description

technical field [0001] The invention belongs to the field of noise-reducing and sound-insulating materials and preparation thereof, in particular to an antistatic, wear-resistant, noise-reducing and sound-insulating material and a preparation method thereof. Background technique [0002] The currently commonly used non-woven noise-reducing materials often have the disadvantage that the fibers are easy to peel off and float away, especially in the non-woven noise-reducing materials made of short fibers and ultra-short fibers. Its poor wear resistance not only shortens the service life of the material, but also reduces the noise reduction efficiency during use. In addition, chemical fiber non-woven noise-reducing materials have a high specific resistance, and the charges generated on the surface of the fabric are not easy to dissipate, and accumulate to generate high static voltage, which not only hinders the improvement of the grade of noise-reducing materials, but also limit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/564D06M11/74
CPCD06M11/74D06M15/564D06M2200/35
Inventor 晏雄唐晓宁张慧萍庄兴民
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com