Water-saving permeation tube and manufacture method thereof

A technology for permeation pipes and waste tires, which is applied in the direction of pipes, rigid pipes, pipes/pipe joints/fittings, etc., which can solve the problems of polypropylene pipes such as weak impact strength, poor aging resistance, and short life, so as to ensure seepage irrigation demand, strong impact resistance and long service life

Inactive Publication Date: 2016-11-02
ZHANGZHOU LEYNEM IND
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing permeation tubes mainly use polypropylene tubes, but polypropylene tubes have problems such as weak impact resistance, poor aging resistance, and short life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A water-saving permeation pipe is made of the following components in parts by weight:

[0024] 100 parts of polypropylene, 28 parts of waste tire rubber powder, 5 parts of calcium sulfate whisker, 6 parts of aluminum silicate ceramic fiber, 9 parts of calcium carbonate, 2 parts of graphite powder, 3-(2,3-epoxypropoxy)propane 5 parts of trimethoxysilane, 2 parts of polyethylene wax.

[0025] The mesh number of the waste tire rubber powder is 100-150 mesh. The calcium sulfate whisker has a diameter of 3-5 μm, a length of 50-80 μm, and an aspect ratio of 10-15. The mesh number of the calcium carbonate is 500-600 mesh, and the mesh number of the graphite powder is 400-500 mesh.

[0026] The above-mentioned manufacturing method of a water-saving permeation pipe comprises the following steps:

[0027] (1) Polypropylene, waste tire rubber powder, calcium sulfate whisker, aluminum silicate ceramic fiber, calcium carbonate, graphite powder, 3-(2,3-glycidyloxy)propyltrimethox...

Embodiment 2

[0031] A water-saving permeation pipe is made of the following components in parts by weight:

[0032] 100 parts of polypropylene, 25 parts of waste tire rubber powder, 7 parts of calcium sulfate whisker, 5 parts of aluminum silicate ceramic fiber, 8 parts of calcium carbonate, 2 parts of graphite powder, 3-(2,3-epoxypropoxy)propane 6 parts of trimethoxysilane, 2 parts of polyethylene wax.

[0033] The mesh number of the waste tire rubber powder is 100-150 mesh. The calcium sulfate whisker has a diameter of 3-5 μm, a length of 50-80 μm, and an aspect ratio of 10-15. The mesh number of the calcium carbonate is 500-600 mesh, and the mesh number of the graphite powder is 400-500 mesh.

[0034] The above-mentioned manufacturing method of a water-saving permeation pipe comprises the following steps:

[0035] (1) Polypropylene, waste tire rubber powder, calcium sulfate whisker, aluminum silicate ceramic fiber, calcium carbonate, graphite powder, 3-(2,3-glycidyloxy)propyltrimethox...

Embodiment 3

[0039] A water-saving permeation pipe is made of the following components in parts by weight:

[0040] 100 parts of polypropylene, 30 parts of waste tire rubber powder, 8 parts of calcium sulfate whiskers, 4 parts of aluminum silicate ceramic fiber, 10 parts of calcium carbonate, 3 parts of graphite powder, 3-(2,3-epoxypropoxy)propane 4 parts of trimethoxysilane, 3 parts of polyethylene wax.

[0041] The mesh number of the waste tire rubber powder is 100-150 mesh. The calcium sulfate whisker has a diameter of 3-5 μm, a length of 50-80 μm, and an aspect ratio of 10-15. The mesh number of the calcium carbonate is 500-600 mesh, and the mesh number of the graphite powder is 400-500 mesh.

[0042] The above-mentioned manufacturing method of a water-saving permeation pipe comprises the following steps:

[0043] (1) Polypropylene, waste tire rubber powder, calcium sulfate whisker, aluminum silicate ceramic fiber, calcium carbonate, graphite powder, 3-(2,3-glycidyloxy)propyltrimeth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
aspect ratioaaaaaaaaaa
Login to view more

Abstract

The invention provides a water-saving permeation tube and a manufacture method thereof. The permeation tube is prepared from the following ingredients (by weight): 100 parts of polypropylene, 25-30 parts of waste tire rubber powder, 5-8 parts of calcium sulfate whiskers, 4-6 parts of aluminium silicate ceramic fibre, 8-10 parts of calcium carbonate, 2-3 parts of graphite powder, 4-6 parts of 3-(2,3-epoxypropoxy) trimethoxypropylsilane and 2-3 parts of polyethylene wax. The permeation tube has strong impact resistance, aging resistance and long service life, and guarantees infiltrating irrigation requirement in agricultural production.

Description

technical field [0001] The invention relates to a water-saving permeation pipe and a manufacturing method thereof. Background technique [0002] Infiltration irrigation is an effective water-saving irrigation technology. Irrigation water seeps out through the permeable holes on the wall of the permeable pipe buried in the ground, and diffuses to the surrounding under the action of water head pressure and capillary suction, which has the advantages of water saving, energy saving and labor saving. , increase production, improve the quality of agricultural products, improve soil environmental conditions and other advantages. [0003] Existing permeation tubes mainly use polypropylene tubes, but polypropylene tubes have problems such as weak impact resistance, poor aging resistance, and short life. Contents of the invention [0004] The invention provides a water-saving permeation pipe, which has strong impact resistance and aging resistance, and also provides a manufacturing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L21/00C08L23/06C08K13/04C08K7/10C08K7/08C08K3/26C08K3/04C08K5/5435F16L9/12
CPCC08L23/12C08L2203/18C08L2205/02C08L2205/03F16L9/12
Inventor 郭文礼
Owner ZHANGZHOU LEYNEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap