A kind of preparation method of bismaleimide block polymer containing carbon nanotube

A technology of bismaleimide block and bismaleimide, which is applied in the field of preparation of bismaleimide block polymers, can solve problems such as easy agglomeration and limit the application of carbon nanotubes, and achieve Easy curing, good toughness, excellent dispersion performance

Inactive Publication Date: 2011-12-07
TONGJI UNIV
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the extremely high surface energy of CNTs, the huge van der Waals force between the tubes makes them easy to agglomerate, and they are almost insoluble in any solvent, so it is difficult to disperse in the composite matrix, which limits the application of carbon nanotubes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of bismaleimide block polymer containing carbon nanotube
  • A kind of preparation method of bismaleimide block polymer containing carbon nanotube

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Example 1: Multi-walled carbon nanotubes (OD<8nm) prepared by the arc discharge method were used as the initial raw material. Diphenylmethane (BDM) undergoes Michael addition reaction to obtain a 4,4'-bismaleimidodiphenylmethane block polymer containing multi-walled carbon nanotubes.

[0026] Step (1): In the 200ml single-necked round-bottomed flask equipped with agitator, add 6g of dry multi-walled carbon nanotube raw material and 100mL, 20% weight concentration nitric acid solution, process 100 hours under 1kHz ultrasonic wave, then Heat to 100°C, react for 1 hour, filter with ψ0.8μm polytetrafluoroethylene microfiltration membrane, wash with deionized water 2-8 times until neutral, and vacuum dry at 20°C for 48 hours to obtain purified carbon nano Tube;

[0027] Step (2): In the 200mL single-necked round bottom flask that stirrer has been housed, add the carbon nanotube raw material 5g and 100mL of the purification that obtains in step (1), 60% weight concentration ...

Embodiment 2

[0032] Example 2: The single-walled carbon nanotubes (OD<8nm) prepared by chemical vapor deposition were used as the initial raw material, after purification, acidification, acyl chloride, and amination, and N-methylphthalimide The Michael addition reaction is carried out to obtain the N-methylphthalimide block polymer containing single-walled carbon nanotubes.

[0033] Step (1): In the 500ml single-necked round bottom flask that magnetic stirring rotor has been housed, add 6g single-walled carbon nanotube raw material and 200mL, the sulfuric acid of 30% weight concentration, use 60kHz ultrasonic treatment for 18 hours, then heat to 70 ℃, reacted for 12 hours, filtered with ψ0.8μm polyvinylidene fluoride microfiltration membrane, washed repeatedly with deionized water until neutral, and vacuum dried at 100℃ for 24 hours to obtain purified carbon nanotubes;

[0034] Step (2): In the 250mL single-necked round-bottomed flask equipped with a magnetic stirring rotor, add the purifi...

Embodiment 3

[0040] Example 3: The single-walled carbon nanotubes (OD<8nm) prepared by the laser evaporation method are used as the initial raw material, after purification, acidification, acyl chloride, and amination, Michael Addition reaction, the diphenyl ether-based bismaleimide block polymer containing carbon nanotubes is obtained.

[0041] Step (1): In a 500ml single-neck round bottom flask equipped with mechanical stirring, add 6g of single-walled carbon nanotube raw material and 300mL of 50% weight concentration sulfuric acid solution, use 100kHz ultrasonic treatment for 1 hour, then heat and Stir and reflux, react for 100 hours, filter with ψ0.8μm polytetrafluoroethylene microfiltration membrane, wash repeatedly with deionized water 2-8 times until neutral, and dry in vacuum at 200°C for 1 hour to obtain purified single-walled carbon nanotube;

[0042] Step (2): In a 500mL single-neck round bottom flask equipped with a magnetic stirring rotor, add 5g of purified carbon nanotube r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of nanometer materials, and in particular relates to a preparation method of a bismaleimide block polymer containing carbon nanotubes. In the present invention, after surface quantitative carboxylation and acid chlorination of the purified carbon nanotubes, long-chain diamines or polyamines with characteristic structures are introduced into the purified carbon nanotubes, and the entire carbon nanotubes become diamines or polyamines. The aminated carbon nanotubes are regarded as polymer chains, and then the aminated carbon nanotubes are used to carry out Michael addition reaction with bismaleimide to generate bismaleimide resin linear blocks containing carbon nanotubes Polymers, carbon nanotubes become part of the bismaleimide resin system. This type of carbon nanotube modified bismaleimide resin can make full use of the strength and toughness of carbon nanotubes to strengthen and toughen bismaleimide, and can also improve its heat resistance and wear resistance. The application of imide resin in the field of high-performance composite materials such as aerospace and aviation has laid a foundation.

Description

technical field [0001] The invention belongs to the technical field of nanometer materials, and in particular relates to a preparation method of a bismaleimide block polymer containing carbon nanotubes. Background technique [0002] Bismaleimide (BMI) is a bifunctional compound with maleimide (MI) as the active terminal group. Bismaleimide resin (BMI) is known for its excellent heat and humidity resistance, low moisture absorption, radiation resistance, flame retardancy, excellent mechanical properties and dimensional stability, good electrical insulation, easy molding and processing, molecular structure Easy to design and other features, it is widely used in aerospace, machinery and electronics and other industrial fields. However, the cured and crosslinked bismaleimide has insufficient toughness and high brittleness, which limits its application range. Therefore, it needs to be modified in application. In recent years, the modification of bismaleimide (BMI) by researche...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G83/00
Inventor 邱军王宗明
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com