Municipal sludge non-sintered ceramsite and production method thereof

A technology of municipal sludge and production method, applied in the field of building materials, can solve problems such as leakage and watermark, and achieve the effect of simple process and widening of utilization channels.

Inactive Publication Date: 2016-11-09
MAANSHAN MCC17 ENG TECH CO LTD
View PDF6 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to overcome the defects of quality problems such as leakage or large-area watermarks in the existing window walls when any violent storm invades, and to provide an anti-leakage treatment method for the window walls of the outer walls of high-rise buildings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The invention provides a municipal sludge non-burning ceramsite, which is prepared from the following raw materials according to the mass percentage: 40%~60% of municipal sludge, 20%~30% of cement, 5%~10% of fly ash, desulfurization Gypsum 3%~7%, slag powder 3%~7%, sodium silicate 4%~6%, the municipal sludge described is municipal sludge that has been deodorized, and its water content is controlled at 70%~ Between 80%, the free water content of the desulfurized gypsum is 10%~15%, the average particle size is 20μm~50μm, the remaining 5.2% is 200 mesh sieve, the loss on ignition of the slag micropowder is 1.77%, and the specific surface area after grinding is 450m2 / kg, the sodium silicate is powdery, the water-insoluble matter percentage is ≤0.04%, the water content mass percentage is ≤25%, the modulus is 2.6~2.8, and the particle size is 20~40 mesh, including the following steps: 1 ), weigh cement, fly ash, desulfurized gypsum, slag powder and sodium silicate according t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a municipal sludge non-sintered ceramsite and a production method thereof. The municipal sludge non-sintered ceramsite is produced from, by weight, 40-60% of municipal sludge, 20-30% of cement, 5-10% of fly ash, 3-7% of desulfurized gypsum, 3-7% of slag micro-powder and 4-6% of sodium silicate, wherein the municipal sludge is deodorized municipal sludge, and the content of the municipal sludge is controlled to be 70-80%; the content of free water in the desulfurized gypsum is 10-15%, the average granularity is 20-50 [mu]m, and the 200 mesh screen residue is 5.2%; the ignition loss of the slag micro-powder is 1.77%, and the specific surface area of the reduced slag micro-powder is 450 m<2>/kg; and the sodium silicate is powdery, the mass percentage of water-insoluble substances is not greater than 0.04%, the mass percentage of water is not greater than 25%, the modulus is 2.6-2.8, and the granularity is 20-40 meshes. The municipal sludge non-sintered ceramsite can digest a large amount of municipal sludge, and also can digest fly ash, slag micro-powder, desulfurized gypsum and other industrial wastes, so the utilization approach of above solid wastes is widened; and compared with a roasting technology, a non-sintering technology adopted by the above product has the advantages of energy saving, low carbon and environmental protection.

Description

technical field [0001] The invention relates to the field of building materials, in particular to municipal sludge burn-free ceramsite and a production method thereof. Background technique [0002] Ceramsite, as a lightweight aggregate for construction, has received great attention for its light weight, heat preservation, and environmental protection. At present, my country's ceramsite is mainly clay ceramsite, and the source of clay raw materials is mostly from cultivated land, which does not conform to the sustainable development strategy. Therefore, the sludge from the sewage plant is used as the main raw material, and a certain amount of auxiliary materials and admixtures are added to make lightweight ceramsite with a certain strength after decarbonization and swelling, which can consume a large amount of dewatered sludge, and not only the treatment cost is greatly reduced It is better than the incineration method, and can avoid the secondary pollution of sludge, especia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B18/02
CPCC04B18/027C04B18/021C04B18/0418C04B18/08C04B22/145C04B22/08C04B18/141
Inventor 李亚辉钱元弟王璠陈贺王孝平王慧
Owner MAANSHAN MCC17 ENG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap