Ceramic and production process thereof

A production process and ceramic technology, applied in the field of ceramics and its production process, can solve the problems affecting artistic beauty and appreciation value, unstable structure, uneven coloring, etc., and achieve high artistic appreciation value, cost saving, uniform color and luster. Effect

Inactive Publication Date: 2016-11-23
长沙市望城区铜官窑承林陶艺有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the products fired in the prior art are easily damaged during the firing process, and the structure is unstable and the coloring is uneven, which wastes a lot of resources and also affects the aesthetics and appreciation value of its art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A ceramic and its production process. The embryo body is made of the following raw materials: 10g lead-boron frit, 8g material soil, 15g calcite, 30g albite feldspar, 10g potassium feldspar, 10g quartz, 5g iron red, 1g Titanium, lead-boron frit, material soil, calcite, albite, potassium feldspar, quartz, iron red, titanium are pulverized in a pulverizer, then ground by a ball mill, and then iron is removed by a magnet, and electrolyte is added to stir Slurrying, grouting molding, drying, hanging embryo, and drying to obtain the embryo body, after biscuit firing, glaze application, and then firing at 1210°C for 8 hours to obtain the finished product.

Embodiment 2

[0012] A ceramic and its production process. The embryo body is made of the following raw materials: 20g lead-boron frit, 15g material soil, 28g calcite, 40g albite feldspar, 20g potassium feldspar, 20g quartz, 12g iron red, 5g Titanium, lead-boron frit, material soil, calcite, albite, potassium feldspar, quartz, iron red, titanium are pulverized in a pulverizer, then ground by a ball mill, and then iron is removed by a magnet, and electrolyte is added to stir Slurrying, grouting molding, drying, hanging, and drying to obtain the embryo body, then biscuit firing, glaze application, and then firing at 1210°C for 10 hours to obtain the finished product.

Embodiment 3

[0014] A ceramic and its production process. The embryo body is made of the following raw materials: 15g lead-boron frit, 12g soil, 15-28g calcite, 35g albite, 15g potassium feldspar, 15g quartz, 8g iron red , 3g of titanium, lead-boron frit, material soil, calcite, albite, potassium feldspar, quartz, iron red, titanium are pulverized in a pulverizer, then ground through a ball mill, and the iron is removed by a magnet, and then added The electrolyte is stirred into a slurry, cast into a slurry, dried, hanged, and dried to obtain an embryo body. After biscuit firing and glaze application, it is fired at a high temperature of 1210°C for 9 hours to obtain a finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses ceramic and a production process thereof. A blank is made from, by weight, 10-20 g of lead boron frit, 8-15 g of material soil, 15-28 g of calcite, 30-40 g of albite, 10-20 g of potassium feldspar, 10-20 g of quartz, 5-12 g of iron oxide red and 1-5 g of titanium. The production process includes: smashing the lead boron frit, the material soil, calcite, albite, potassium feldspar, quartz, iron oxide red and titanium in a smasher, and grinding through a ball grinder; using a magnet to remove iron therein, adding an electrolyte, stirring to form grout, and performing slip casting; drying, blank hanging, and drying to obtain the blank; biscuiting, glazing, and firing for 8-10h at high temperature of 1210 DEG C to obtain a finished product. The ceramic and the production process have the advantages that the finished product obtained through the formula and the process is stable in structure, less prone to breakage and uniform in color and luster; resource waste is avoided greatly, and cost saving of enterprises is facilitated; the product has high art appreciation value as artware, so that added value of the product is increased.

Description

technical field [0001] The invention relates to the technical field of ceramic production, in particular to a ceramic and a production process thereof. Background technique [0002] Ceramics is the general term for pottery and porcelain. The Chinese invented pottery as early as about 8000-2000 BC (Neolithic Age). Ceramic materials are mostly oxides, nitrides, borides and carbides. Common ceramic materials are clay, alumina, kaolin and so on. Ceramic materials generally have higher hardness, but poor plasticity. In addition to the use of tableware and decoration, it also plays an important role in the development of science and technology. The raw material of ceramics is obtained by quenching the earth's original large resource clay. The nature of clay is tough, it can be molded when exposed to water at room temperature, it can be carved when it is slightly dry, and it can be ground when it is completely dry; it can be made into pottery and can hold water when it is fire...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/02C04B33/13C04B33/24C04B33/34
Inventor 刘术军
Owner 长沙市望城区铜官窑承林陶艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products