Waterborne paint with camouflage decorative effect and preparing method of waterborne paint

A decorative effect, water-based coating technology, applied in the field of decorative coatings, can solve the problems that camouflage decorative coatings have not yet been used, and achieve the effect of being suitable for promotion, simple preparation method, and large specific surface area

Inactive Publication Date: 2016-11-23
泉州市合创涂料科技有限公司
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, methacrylate copolymers, vinyl acetate/methacrylate copolymers, and styrene/methacrylate copolymer emulsions are widely used. Among them, acrylate polymer emulsions have strong adhesion, Superior elasticity, water and alkali resis

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Dark green water-emulsion polymer camouflage decorative paint, including: acrylate emulsion 49g, water 10g, iron oxide black 4.7g, chrome oxide green 21.4g, iron oxide brown 3.9g, diatomaceous earth 5.8g, sodium polyacrylate 2.2g , Silicone defoamer 1.1g.

[0022] Finely grind iron oxide black, chromium oxide green, iron oxide brown, and diatomaceous earth separately to make them finer than 50 microns, and then add them together with sodium polyacrylate and silicone defoamer to acrylate emulsion and The water-emulsion polymer camouflage decorative paint of the present invention can be prepared by fully stirring in the water mixture. The prepared water-emulsion polymer camouflage decorative paint is sealed and preserved, and can be used at any time when needed.

[0023] In non-rainy weather with a temperature above 0°C, the prepared water-emulsion polymer camouflage decorative paint is evenly brushed on the surface of engineering buildings to form a good camouflage ...

Embodiment 2

[0025] Light green water-emulsion polymer camouflage decorative paint, including: acrylate emulsion 50g, water 11g, chromium oxide green 25g, chrome yellow 6.1g, diatomaceous earth 6.2g, sodium polyacrylate 1.8g, silicone defoamer 0.9g .

[0026] Finely grind chromium oxide green, chrome yellow, and diatomaceous earth separately to make them finer than 50 microns, and then add them together with sodium polyacrylate and silicone defoamer to the mixture of acrylate emulsion and water Fully stirred, the water-emulsion polymer camouflage decorative paint of the present invention can be prepared. The prepared water-emulsion polymer camouflage decorative paint is sealed and preserved, and can be used at any time when needed.

[0027] The prepared water-emulsion polymer camouflage decorative coating is mechanized sprayed on the surface of engineering buildings in non-rainy weather with a temperature above 0°C to form a good camouflage coating. The camouflage coating has good vi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a waterborne paint with a camouflage decorative effect and a preparing method of the waterborne paint. Every 100 parts of the paint by weight is prepared from, by weight, 59-61 parts of a base material, 30-32 parts of pigment, 5.8-6.2 parts of filler and 2.7-3.3 parts of an assistant. The base material is prepared from acrylate emulsion and water, and kieselguhr serves as the filler. The preparing method of the waterborne paint comprises the steps that the pigment and the filler are finely ground, the finely-ground pigment, the finely-ground filler, the base material and the assistant are fully stirred at the room temperature, and the waterborne paint can be obtained. When the waterborne paint is used, a paint film is formed on the surface of a target with the method of rolling coating or brush coating or mechanical spraying or the like, and the needed camouflage painting or decorating effect can be obtained after drying. The paint has good camouflage performance and high adhesion, water resistance, acid-base resistance and weather fastness, is nontoxic, harmless and free of foreign smells, belongs to environment-friendly type camouflage decorative paint and is suitable for permanent camouflage painting needs of military engineering facilities and other targets, and also capable of being used for beautifying or individualized decorating coating of civil or commercial buildings.

Description

technical field [0001] The invention relates to a decorative coating, more specifically, the invention relates to a water-based coating with a camouflage decorative effect and a preparation method thereof. Background technique [0002] Camouflage decorative coatings are generally used for camouflage of military targets, and are also commonly used for landscaping or personalized decoration of civil or commercial buildings. Camouflage camouflage has certain special technical requirements for its camouflage decorative coatings. Generally, it should have good camouflage performance, strong adhesion performance and environmental adaptability. Existing camouflage decorative coatings, especially camouflage decorative coatings for engineering buildings, have many disadvantages, such as fading, peeling or cracking, etc., which are easy to occur on the camouflage decorative coatings on the surface of buildings. Performance is unstable. [0003] In recent years, water-based camou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/04C09D5/30
Inventor 陈昕雄王珊珊
Owner 泉州市合创涂料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap