A kind of marine biological control coating and preparation method thereof

A technology for the prevention and control of marine organisms, applied in the field of coatings, can solve problems that affect human health, fail to function, and endanger the marine environment, and achieve the effects of being conducive to popularization and application, long antifouling period, and stable process

Active Publication Date: 2017-08-04
广东天朗化工实业有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, organotin coatings have good antifouling effects, but also have adverse effects on non-target organisms in the marine environment, endangering the marine environment, and affecting human health through the enrichment process of the food chain
In 2001, the International Maritime Organization (IMO) passed a resolution requiring that starting from January 1, 2008, paints containing organic tin compounds such as TBT should be banned on a global scale; while other products that replace TBT such as copper base paint and It also shows some limitations in practical application, and has toxic effects on oysters, algae and various aquatic organisms
However, in practical applications, diketopiperazine compounds such as cyclic (proline-alanine) need to be used in combination with coating base materials, otherwise they will be lost with seawater and cannot function
But, existing paint base material raw material is numerous, and base material type, proportioning, effective dosage etc. all can exert influence on the performance of control effect, therefore, it is necessary to seek a kind of suitable coating system, to play ring (proline) Acid-alanine) and other diketopiperazine compounds to achieve efficient, broad-spectrum, environmentally friendly, non-toxic prevention and control of marine organisms for marine artificial facilities such as ships

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of marine biological control coating and preparation method thereof
  • A kind of marine biological control coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment 1, marine biological control coating and preparation thereof of the present invention

[0025] Formula: chlorinated rubber 70kg, rosin 45kg, cycloproline-3-hydroxy-2-aminobutyric acid 100kg, zinc 50kg, iron oxide red 160kg, zinc oxide 280kg, barium carbonate 3kg, magnesium oxide 1kg, trimethyl phosphate 50kg of phenol ester, 5kg of organic bentonite and 140kg of solvent; the solvent is a mixture of butyl acetate and xylene, and the weight ratio of butyl acetate and xylene is 1:5.

[0026] Preparation:

[0027] S1. Take the formula quantity of chlorinated rubber, rosin and solvent and put them into the reactor for mixing, and stir for 20min at a speed of 100r / min; then add the formula quantity of cycloproline-3-hydroxy-2-aminobutyric acid, continue Stir for 20 minutes, heat up and keep warm at 50°C for 1 hour, take it out into a dispersion tank, and cool to room temperature;

[0028] S2, then add the formula amount of Zinc, red iron oxide, zinc oxide, barium...

Embodiment 2

[0029] Embodiment 2, marine biological control coating of the present invention and its preparation

[0030] Formula: chlorinated rubber 80kg, rosin 60kg, cycloproline-3-hydroxy-2-aminobutyric acid 120kg, zinc zinc 70kg, iron oxide red 180kg, zinc oxide 320kg, barium carbonate 10kg, magnesium oxide 5kg, trimethyl phosphate 60kg of phenol ester, 15kg of organic bentonite and 160kg of solvent; the solvent is a mixture of butyl acetate and xylene, and the weight ratio of butyl acetate and xylene is 1:7.

[0031] Preparation:

[0032]S1. Take the formula quantity of chlorinated rubber, rosin and solvent and put them into the reactor for mixing, and stir for 40min at a speed of 150r / min; then add the formula quantity of cycloproline-3-hydroxy-2-aminobutyric acid, continue Stir for 40 minutes, heat up and keep warm at 55°C for 1.5 hours, take it out into a dispersion tank, and cool to room temperature;

[0033] S2, then add the formula amount of Zinc, red iron oxide, zinc oxide, b...

Embodiment 3

[0034] Embodiment 3, marine biological control coating of the present invention and its preparation

[0035] Formula: chlorinated rubber 76kg, rosin 55kg, cycloproline-3-hydroxy-2-aminobutyric acid 110kg, zinc zinc 60kg, iron oxide red 170kg, zinc oxide 300kg, barium carbonate 5kg, magnesium oxide 2kg, trimethyl phosphate 55kg of phenol ester, 10kg of organic bentonite and 150kg of solvent; the solvent is a mixture of butyl acetate and xylene, and the weight ratio of butyl acetate and xylene is 1:6.

[0036] Preparation:

[0037] S1. Take the formula quantity of chlorinated rubber, rosin and solvent and put them into the reaction kettle for mixing, and stir for 30min at a speed of 120r / min; then add the formula quantity of cycloproline-3-hydroxy-2-aminobutyric acid, continue Stir for 30 minutes, heat up and keep warm at 55°C for 1 hour, take it out into a dispersion tank, and cool to room temperature;

[0038] S2, then add the formula amount of Zinc, red iron oxide, zinc oxi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of coatings, and particularly discloses a marine biocontrol coating and a preparation method thereof. The coating is prepared from, by weight, 70-80 parts of chlorinated rubber, 45-60 parts of rosin, 100-120 parts of diketopiperazine compounds, 50-70 parts of zineb, 160-180 parts of iron oxide red, 280-320 parts of zinc oxide, 1-10 parts of barium carbonate, 1-5 parts of magnesium oxide, 50-60 parts of tricresyl phosphate, 5-15 parts of organic bentonite and 140-160 parts of solvent. The coating has high adhesion and is excellent in antifouling property, long in antifouling period, capable of effectively preventing and killing off marine fouling organisms such as barnacles, mussels and algae, efficient, poisonless and environmentally friendly.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a marine biological control coating and a preparation method thereof. Background technique [0002] Marine fouling organisms refer to the general term for animals, plants and microorganisms that adhere to or inhabit the surface of ships and various underwater objects in the marine environment and have adverse effects on human activities. They are one of the important factors affecting the safety and service life of marine facilities. First, it is also a difficult problem encountered by human beings when they started to engage in maritime activities, and its occurrence process is completely a natural phenomenon. [0003] my country has a long coastline, and the ocean environment is complex from south to north. A large number of ships sail in the harsh ocean environment. The bottom part of the ship has been soaked in seawater for a long time, and it is seriously fouled...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D115/02C09D193/04C09D5/16C09D5/08C09D7/12
CPCC09D5/08C09D5/1625C09D5/1687C09D115/02C08L93/04C08K13/06C08K2003/2272C08K2003/2296C08K5/521C08K3/346C08K5/39
Inventor 黄立吴民汤治中刘水泉李孙文
Owner 广东天朗化工实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products