Preparation method of bimetallic composite plate
A bimetallic and composite plate technology, applied in chemical instruments and methods, lamination devices, lamination auxiliary operations, etc., can solve the problems of weak diffusion ability of metal atoms, low melting point of magnesium alloy, low interface strength, etc., and achieve the goal of inhibiting element Long-range diffusion, high interfacial bonding strength, and the effect of improving interfacial bonding strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0024] The preparation method of the high-strength bimetal composite board of the present invention includes the following steps:
[0025] Ⅰ. Raw material pretreatment: the base material and composite material are processed and flattened separately, and polished to remove burrs and flashes;
[0026] Ⅱ. Coating of release agent: coat release agent on one side of the composite material;
[0027] Ⅲ. Coating of permeation agent: Coat at least one of the surface of the base material and the side of the composite material that is not coated with the permeation agent;
[0028] Ⅳ. Assembling blanks: symmetrically group blanks in the manner of base material-composite material-composite material-base material or base material-metal transition layer-composite material-composite material-metal transition layer-base material, and then weld the sides of the blank Combine and evacuate to obtain a composite blank; wherein the two sides of the composite material coated with a release agent are attache...
Example Embodiment
[0040] Example 1
[0041] The titanium steel composite board with nickel as the intermediate layer is prepared, and the preparation method is as follows:
[0042] ⅠThe Q235 steel base material and TA2 titanium composite material are processed and smoothed on a lathe respectively, and polished to remove burrs and flashes. Leveling and cleaning the nickel metal transition layer. The thickness of Q235 steel substrate is 10mm, the thickness of TA2 titanium composite is 3mm, and the thickness of nickel transition layer is 1mm.
[0043] Ⅱ Coat a release agent on one side of two TA2 titanium composites.
[0044] Ⅲ Coat the osmotic agent on the side of the TA2 titanium composite that is not coated with the release agent. Osmotic agent is 5% Y 2 O 3 , 2% NaF and 1.5% NH 4 It is composed of Cl, 40% metal titanium powder and 51.5% nickel powder.
[0045] Ⅳ According to the Q235 steel base material-nickel transition layer-TA2 titanium composite material-TA2 titanium composite material-nickel tra...
Example Embodiment
[0050] Example 2
[0051] The preparation method of aluminum-magnesium composite board is as follows:
[0052] ⅠThe AZ31B magnesium alloy and 5052 aluminum alloy are processed and flattened on a lathe respectively, and polished to remove burrs and flashes. The thickness of 5052 aluminum alloy is 5mm, and the thickness of AZ31B magnesium alloy is 2mm.
[0053] Ⅱ Coat one side of two AZ31B magnesium alloy with release agent.
[0054] Ⅲ Coat the permeating agent on the side of the AZ31B magnesium alloy without the release agent. Osmotic agent is 2% Y 2 O 3 ,1%LaCl 3 , 2.5% NaF and 0.5% NH 4 It is composed of Cl, 47% magnesium powder and 47% aluminum powder.
[0055] Ⅳ The billet is symmetrically assembled in the manner of 5052 aluminum alloy-AZ31B magnesium alloy-AZ31B magnesium alloy-5052 aluminum alloy magnesium alloy. Then weld and evacuate the four sides of the blank to obtain a combined blank. The vacuum degree of 0.1Pa exceeds the claim and is less than 1×10 -2 The range of Pa. W...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap