Bamboo fiber lime sand brick

A bamboo fiber, lime-sand brick technology, applied in sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problem of lower raw material cost of lime-sand brick, dry shrinkage value and impermeability of lime-sand brick need to be improved , to be improved and other issues, to achieve the effect of low cost, improved heat resistance, and resource saving

Inactive Publication Date: 2016-12-14
绍兴职业技术学院
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although lime-sand bricks have many advantages, there are still shortcomings, such as: the strength index of lime-sand bricks needs to be improved (flexural strength and compressive strength); the raw material cost of lime-sand bricks needs to be reduced; the drying shrinkage of lime-sand bricks Value and impermeability need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of bamboo fiber lime-sand brick, by weight, comprises the following components:

[0027] 30 parts of fly ash,

[0028] 7 parts quicklime powder,

[0029] 50 parts of recycled fine aggregate,

[0030] 3 parts bamboo fiber,

[0031] Add 2 parts;

[0032] Among them, the admixture is a mixture of cement and brominated epoxy resin, and the mass ratio of the two is 2:1;

[0033] Its preparation method comprises the following steps:

[0034] (1) Mix fly ash, quicklime powder, regenerated fine aggregate, bamboo fiber, and admixtures to form a mixture, put it into a forced mixer and add an appropriate amount of water for the first stirring. Generally, the stirring time is controlled at 1 minute. Make the water evenly distributed in the agitator, and then let it stand for digestion for 4 hours;

[0035] (2) Add water to stir for the second time, and after stirring evenly, press to form twice, then put it at room temperature for a period of time, and then autoclave f...

Embodiment 2

[0038] A kind of bamboo fiber lime-sand brick, by weight, comprises the following components:

[0039] 40 parts of fly ash,

[0040] 13 parts quicklime powder,

[0041] 60 parts of recycled fine aggregate,

[0042] 7 parts of bamboo fiber,

[0043] Add 5 parts;

[0044] Wherein, the admixture is a mixture of cement and brominated epoxy resin, and the mass ratio of the two is 6:1;

[0045] Its preparation method comprises the following steps:

[0046] (1) Mix fly ash, quicklime powder, regenerated fine aggregate, bamboo fiber, and admixtures to form a mixture, put it into a forced mixer and add an appropriate amount of water for the first stirring. Generally, the stirring time is controlled at 5 minutes. Make the water evenly distributed in the stirrer, then let it stand for digestion for 1h;

[0047] (2) Add water to stir for the second time, and after stirring evenly, press to form twice, then put it at room temperature for a period of time, and then autoclave for curin...

Embodiment 3

[0050] A kind of bamboo fiber lime-sand brick, by weight, comprises the following components:

[0051] 33 parts of fly ash,

[0052] 8 parts quicklime powder,

[0053] 52 parts of recycled fine aggregate,

[0054] 4 parts bamboo fiber,

[0055] Add 3 parts;

[0056] Wherein, the admixture is a mixture of cement and brominated epoxy resin, and the mass ratio of the two is 3:1;

[0057] Its preparation method comprises the following steps:

[0058] (1) Mix fly ash, quicklime powder, regenerated fine aggregate, bamboo fiber, and admixtures to form a mixture, put it into a forced mixer and add an appropriate amount of water for the first stirring. Generally, the stirring time is controlled at 2 minutes. Make the water evenly distributed in the agitator, then let it stand for digestion for 2 hours;

[0059] (2) Add water to stir for the second time, and after stirring evenly, press to form twice, then put it at room temperature for a period of time, and then autoclave for cur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a bamboo fiber lime sand brick. The bamboo fiber lime sand brick comprises the following components in parts by weight: 30-40 parts of fly ash, 7-13 parts of quicklime powder, 50-60 parts of recycled fine aggregate, 3-7 parts of bamboo fiber and 2-5 parts of admixture. The bamboo fiber lime sand brick makes full use of construction wastes, so that resources can be effectively saved, the economy is good and the sustainable development of the construction industry is facilitated. The bamboo fiber is added into mortar, so that the compactness of the lime sand brick can be effectively improved, the strength of the lime sand brick is effectively improved, and the lime sand brick has good waterproof performance.

Description

Technical field: [0001] The invention relates to the technical field of building materials, in particular to a bamboo fiber lime-sand brick. Background technique: [0002] At present, the treatment of most construction wastes is generally only simple landfill treatment or directly stacked in the open air, which has caused serious damage to the ecological environment, and the recycling of construction wastes is becoming more and more urgent. Using construction waste to prepare building materials has become a trend. It can not only save a lot of cultivated land resources, but also enable effective recycling and utilization of construction waste. It can be said to kill two birds with one stone. [0003] With the rapid development of my country's economy and a large number of construction projects, the demand for building bricks is increasing. Since 2008, in order to protect the cultivated land resources, the use of clay bricks has been completely stopped nationwide. For a whil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/12C04B16/02C04B18/16C04B7/00C04B24/28
CPCC04B7/00C04B16/02C04B18/167C04B24/288C04B28/12C04B18/08Y02W30/91
Inventor 金奇亮孔爱散孙秋砚杨兵李建栋
Owner 绍兴职业技术学院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap