Modified graphene lubricating oil with high dispersibility and high affinity, and preparation method thereof

A high-dispersion, graphene technology, which is applied in the petroleum industry, lubricating compositions, additives, etc., can solve the problems of poor stability of lubricating oil and reduced lubricating performance of lubricating oil, so as to improve lubricating performance, improve performance and prolong service life Effect

Inactive Publication Date: 2016-12-21
CHONGQING DELING TECH
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although the use of graphene can improve the lubricating performance of the lubricating oil to a certain extent, the stability of the lubricating oil obtained is poor, and agglomerates will be formed after a long period of storage, which will reduce the lubricating performance of the lubricating oil.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified graphene lubricating oil with high dispersibility and high affinity, and preparation method thereof
  • Modified graphene lubricating oil with high dispersibility and high affinity, and preparation method thereof
  • Modified graphene lubricating oil with high dispersibility and high affinity, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The modified graphene lubricating oil with high dispersibility and affinity comprises the following components in parts by weight: 0.3 part of 3-propylaminoethoxysilanized graphene, 0.5 part of stearic acid, 0.1 part of silane coupling agent 100 parts and mineral base oil.

[0031] The preparation method of the modified graphene lubricating oil with high dispersibility and affinity comprises the steps:

[0032] (1) 3-propylaminoethoxysilanized graphene and silane coupling agent are added step by step in the mineral base oil according to the ratio, and stirred evenly to obtain a mixture;

[0033] (2) Add stearic acid to the mixture obtained in step (1), stir evenly, then mechanically stir the mixture for 1 hour, and then process it with a rubber mill to obtain a modified graphene lubricating oil with high dispersibility and affinity .

[0034] In this embodiment, the particle size of the 3-propylaminoethoxysilanized graphene is controlled to be 50-80 nm, and butadienyl...

Embodiment 2

[0036] The modified graphene lubricating oil with high dispersibility and affinity comprises the following components in parts by weight: 0.5 part of 3-propylaminomethoxysilylized graphene, 0.3 part of sodium dodecylbenzenesulfonate, titanium 2 parts of acid lipid coupling agent and 100 parts of synthetic base oil.

[0037] The preparation method of the modified graphene lubricating oil with high dispersibility and affinity comprises the steps:

[0038] (1) 3-propylaminoethoxysilanized graphene and titanate lipid coupling agent are added step by step in the synthetic base oil according to the ratio, and stirred evenly to obtain a mixture;

[0039] (2) Add sodium dodecylbenzenesulfonate to the mixture obtained in step (1) according to the proportioning ratio, stir evenly, then mechanically stir the mixture for 1.5 hours, and then process it with a rubber mill to obtain a modified compound with high dispersibility and affinity. Non-toxic graphene lubricating oil.

[0040] In t...

Embodiment 3

[0042] A modified graphene lubricating oil with high dispersibility and affinity, comprising the following components in parts by weight: 0.8 parts of N-aminoethyl-3-aminopropyl trimethoxysilylized graphene, 1.5 parts of fatty acid glycerides , 1 part of zirconate lipid coupling agent and 100 parts of vegetable oil base oil.

[0043] The preparation method of the modified graphene lubricating oil with high dispersibility and affinity comprises the steps:

[0044] (1) N-aminoethyl-3-aminopropyltrimethoxysilanized graphene and zirconate lipid coupling agent are added step by step in the vegetable oil base oil according to the ratio, and stirred evenly to obtain a mixture;

[0045] (2) Add fatty acid glycerides to the mixture obtained in step (1), stir evenly, then mechanically stir the mixture for 3 hours, and then process it with a rubber mill to obtain a modified graphene lubricating oil with high dispersibility and affinity .

[0046] In this embodiment, the particle size o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a modified graphene lubricating oil with high dispersibility and high affinity, and a preparation method thereof. The modified graphene lubricating oil comprises, by weight, 0.3-1.5 parts of modified graphene, 0.3-1.5 parts of a dispersing agent, 0.1-2 parts of an affiliation agent, and 100 parts of base oil. According to the present invention, the formula is reasonable, and the preparation method is simple; the prepared lubricating oil has advantages of good stability, good affinity and improved lubricating performance, and can form ink on a mechanical member in mechanical movement so as to reduce the movement resistance of the mechanical member, reduce the friction coefficient, provide the super strong lubricating property and wear resistance, prolong the service life of mechanical member, and achieve energy saving; and the modified graphene lubricating oil can be widely used in a variety of mechanical members, and has great market potential and broad market prospects.

Description

technical field [0001] The invention belongs to the field of macromolecule and its application, in particular to a modified graphene lubricating oil with high dispersibility and affinity, and also relates to a preparation method of the modified graphene lubricating oil. Background technique [0002] Friction and wear are ubiquitous in nature, causing more than 50% of the world's primary energy loss due to friction and wear, and wear is one of the main reasons for the scrapping of materials and equipment. In order to reduce friction and wear, people add lubricating oil between workpieces, but the economic loss of tens of billions of yuan is still caused to the country every year due to friction and wear. Therefore, reducing friction, reducing wear, reducing wear, and prolonging the life of parts are the goals that researchers in tribology, chemistry and materials are constantly pursuing. In order to improve the lubricating performance of lubricating oil, various anti-wear ad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M125/02C10M141/12C10M161/00C10M177/00C10N30/04C10N30/06
CPCC10M125/02C10M141/12C10M161/00C10M177/00C10M2201/041C10M2201/14C10M2203/1006C10M2207/026C10M2207/126C10M2207/283C10M2207/401C10M2209/104C10M2209/109C10M2219/044C10M2229/02C10M2229/041C10M2229/048C10N2020/06C10N2030/04C10N2030/06
Inventor 罗廷军
Owner CHONGQING DELING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com