A kind of acenaphthyl polyphenyl copolymerized allyl phenolic reactive diluent resin and preparation method thereof

A polyphenyl-copolymerized allyl phenolic and reactive dilution technology, applied in the field of resin and its preparation, can solve the problems of complex modification process, cost reduction, long reaction time and the like

Active Publication Date: 2018-05-15
SHENYANG INSTITUTE OF CHEMICAL TECHNOLOGY
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Researchers have made a lot of efforts on phenolic modification, but there are still some problems, such as complex modification process, long reaction time, low efficiency, limited cost reduction, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of acenaphthyl polyphenyl copolymerized allyl phenolic reactive diluent resin and preparation method thereof
  • A kind of acenaphthyl polyphenyl copolymerized allyl phenolic reactive diluent resin and preparation method thereof
  • A kind of acenaphthyl polyphenyl copolymerized allyl phenolic reactive diluent resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Add 100g of phenol solution and sodium hydroxide solution into the reaction kettle at about 65°C in sequence, then add 65g of paraformaldehyde into the reaction kettle in 3 times within half an hour, stir at high speed to mix evenly, react for 30min, and take 5 Slowly raise the temperature to 90°C at the rate of ℃ / min, stir at constant temperature for 1.5h, then cool to room temperature, neutralize the resin liquid with acetic acid, and then evaporate the small molecules in the system under reduced pressure until no liquid is discharged, and the viscous liquid is obtained as Phenolic Resin.

[0020] The synthesized phenolic resin is reacted with allyl chloride to generate allyl ether phenolic resin, and the resin undergoes Claisen rearrangement reaction at high temperature to generate allyl phenolic resin. At the same temperature, add 3g of acenaphthene-type cyclopentadienone and allyl resin to undergo Diels-Alder reaction, and finally obtain acenaphthene-type polypheny...

Embodiment 2

[0022] Add 100g of phenol solution and sodium hydroxide solution into the reaction kettle at about 65°C in sequence, then add 65g of paraformaldehyde into the reaction kettle in 3 times within half an hour, stir at high speed to mix evenly, react for 30min, and take 5 Slowly raise the temperature to 90°C at the rate of ℃ / min, stir at constant temperature for 1.5h, then cool to room temperature, neutralize the resin liquid with acetic acid, and then evaporate the small molecules in the system under reduced pressure until no liquid is discharged, and the viscous liquid is obtained as Phenolic Resin.

[0023] The synthesized phenolic resin is reacted with allyl chloride to generate allyl ether phenolic resin, and the resin undergoes Claisen rearrangement reaction at high temperature to generate allyl phenolic resin. At the same temperature, add 6g of acenaphthene-type cyclopentadienone and allyl resin to undergo Diels-Alder reaction, and finally obtain acenaphthene-type polypheny...

Embodiment 3

[0025] Add 100g of phenol solution and sodium hydroxide solution into the reaction kettle at about 65°C in sequence, then add 65g of paraformaldehyde into the reaction kettle in 3 times within half an hour, stir at high speed to mix evenly, react for 30min, and take 5 Slowly raise the temperature to 90°C at the rate of ℃ / min, stir at constant temperature for 1.5h, then cool to room temperature, neutralize the resin liquid with acetic acid, and then evaporate the small molecules in the system under reduced pressure until no liquid is discharged, and the viscous liquid is obtained as Phenolic Resin.

[0026] The synthesized phenolic resin is reacted with allyl chloride to generate allyl ether phenolic resin, and the resin undergoes Claisen rearrangement reaction at high temperature to generate allyl phenolic resin. At the same temperature, add 9g of acenaphthene-type cyclopentadienone and allyl resin to undergo Diels-Alder reaction, and finally obtain acenaphthene-type polypheny...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

An acenaphthene-type polyphenyl copolymerized allyl phenolic active dilution resin and a preparation method thereof, relating to a resin and a preparation method thereof, the phenolic resin synthesized by the present invention reacts with allyl chloride to generate an allyl ether phenolic resin, and the resin is used in Claisen rearrangement reaction occurs at high temperature, and then allyl phenolic resin is generated; at the same temperature, acenaphthyl cyclopentadienone is added to undergo Diels-Alder reaction with allyl resin, and finally acenaphthyl polyphenyl copolymerized allyl The phenolic reactive diluting resin replaces the phenolic hydroxyl hydrogen in the phenolic resin with an allyl group, and the resulting resin has a relatively low viscosity, which can be used as a reactive diluting resin to reduce the resin viscosity. The acenaphthene-type polyphenyl condensed ring structure with larger molecular groups is introduced, and under specific conditions, Diels-Alder reaction occurs with the double bond in the allyl phenolic resin, and multiple benzene ring groups are introduced to make the synthesized resin It has high temperature resistance and thermo-oxidative stability.

Description

technical field [0001] The invention relates to a resin and a preparation method thereof, in particular to an acenaphthene-type polyphenyl copolymerized allyl phenolic active dilution resin and a preparation method thereof. Background technique [0002] Phenolic resin has been widely used as a high-performance thermosetting resin. However, during the curing process of phenolic resin, small molecular substances such as condensation water or ammonia are released, and pressure is often required during molding. Moreover, the formed phenolic resin material is brittle and has pores. , The performance is not high, thus hindering the high-performance development of phenolic resin materials. [0003] The Chinese patent No. 200310113965.3 proposes to use chemical toughening method to manufacture closed-cell phenolic foam. The Chinese patent No. CN200710127849.5 uses cashew nut oil to modify phenolic resin to improve the toughness of phenolic resin and is used to prepare copper plates...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08G8/30
CPCC08G8/30
Inventor 葛铁军王佳王成城徐志华唐恺鸿
Owner SHENYANG INSTITUTE OF CHEMICAL TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap