A light-curing coating and low surface energy technology, which is applied in antifouling/underwater coatings, coatings, paints containing biocides, etc., can solve problems such as limited performance, poor curing of coatings, and prone to oxygen resistance effects, etc. Achieve the effects of eliminating oxygen resistance effect, improving uniformity and mechanical properties, and promoting connection strength

Inactive Publication Date: 2017-02-08
CHENGDU NASHUO TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, a significant disadvantage of light-cured coatings is that the curing process is prone to oxygen resistance effect, resulting in poor curing of the coating and limited performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] (1) Stir and mix 10 parts of trimethylolpropane triacrylate, 3 parts of hydroxypropyl methacrylate, and 0.04 parts of α-hydroxyalkyl phenone at 10°C;

[0013] (2) Add 3 parts of nano-silica with a particle size of 50nm and 0.01 part of nano-silver particles with a particle size of 20nm into toluene, use ultrasonic dispersion for 10min, and then add 1 part of mercaptopropylmethyldimethoxysilane , heat up to 110°C and reflux for 30 minutes, then continue to heat up and concentrate the liquid to 1 / 4 volume, add 2 parts of hydroxypropyl methacrylate when the temperature drops to 30°C, and stir evenly;

[0014] (3) Mix the liquid obtained in step (1) with the liquid obtained in step (2), add 0.01 part of dibutyltin dilaurate and 0.06 part of isophorone diisocyanate, and stir evenly;

[0015] (4) Add 1 part of polylactic acid with a molecular weight of 5,000 to 15,000 to the mixture obtained in step (3), knead at 250°C for 1 hour, and store the product in the dark to obtain t...

Embodiment 2

[0017] (1) Stir and mix 15 parts of trimethylolpropane triacrylate, 8 parts of hydroxypropyl methacrylate, and 0.4 parts of α-hydroxyalkyl phenone at 20°C;

[0018] (2) Add 0.05 part of nano-silica part with a particle size of 100nm and silver particles with a particle size of 30nm in toluene, use ultrasonic dispersion for 30min, then add 3 parts of mercaptopropylmethyldimethoxysilane, and heat up Reflux at 100°C for 60 minutes, then continue to heat up and concentrate the liquid to 1 / 4 volume, add 2 parts of hydroxypropyl methacrylate when the temperature drops to 40°C, and stir evenly;

[0019] (3) Mix the liquid obtained in step (1) with the liquid obtained in step (2), add 0.1 part of dibutyltin dilaurate and 0.6 part of isophorone diisocyanate, and stir evenly;

[0020] (4) Add 3 parts of polylactic acid with a molecular weight of 5,000 to 15,000 to the mixture obtained in step (3), knead at 150°C for 3 hours, and store the product in the dark to obtain the low-surface an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an antibacterial photocureable coating with low surface energy. The coating comprises the following ingredients: trimethylolpropane triacrylate, hydroxypropyl methacrylate, 3-mercaptopropylmethyldimethoxysilane, dibutyltin dilaurate, nano-silica, a photoinitiator, polylactic acid and silver nano-particles. There exists no oxygen inhibition during curing, and curing is complete. The coating of the invention has excellent mechanical properties and low surface energy, and has dustproof and antibacterial effects.

Description

technical field [0001] The present invention relates to the field of photocurable coatings. Background technique [0002] Photocurable coatings, also known as photosensitive coatings, are usually obtained by using ultraviolet light as the energy source to trigger the reaction of coating components. Photocurable coatings do not need to be heated when used, and can be used on flammable substrates such as paper, plastic, leather and wood. It can quickly solidify into a film, and its curing time is short, the curing temperature is low, and the volatile matter is low, which can save a lot of energy and resources, and is pollution-free and high-efficiency. However, a significant disadvantage of photocurable coatings is that the oxygen resistance effect is prone to occur during the curing process, resulting in poor curing of the coating and limited performance. Contents of the invention [0003] The object of the present invention is to propose a photocurable coating with good c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D7/12C09D5/14
CPCC09D4/06C09D5/14C08F283/02
Inventor 黄波
Owner CHENGDU NASHUO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap