Container

A container and box technology, applied in coatings, anti-corrosion coatings, polyester coatings, etc., can solve the problems of anti-oxidation and weather resistance of metal boxes that need to be improved, affecting the long-term use of containers, etc., and achieve excellent anti-rust effect.

Inactive Publication Date: 2017-02-15
SUZHOU FANRONG SPECIAL CONTAINER
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] For existing containers, the antirust, corrosion resistance, oxidation resistance, and weather resistance of the metal box need to be improved, which affects the long-term use of the container

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The container includes a metal box body, the surface of the metal box body is coated with a protective paint, and the protective paint is prepared through the following steps:

[0022] 1) Put 1 to 2 parts by weight of benzotriazole, 1.5 parts by weight of maleic anhydride, 1.6 parts by weight of fatty alcohol polyoxyethylene polyoxypropylene ether, 2.1 parts by weight of polyethylene glycol, and 9 parts by weight of white latex into 26 parts by weight part deionized water, stir evenly;

[0023] 2) Add 13 parts by weight of water-based alkyd resin, 1.3 parts by weight of diethylenetriamine, 0.8 parts by weight of ammonium dodecyl trimethyl ammonium sulfate, 0.8 parts by weight of sodium benzoate, and 2.6 parts by weight of acrylic acid, and continue to stir until fully Mix evenly to prepare a protective paint.

Embodiment 2

[0025] The container includes a metal box body, the surface of the metal box body is coated with a protective paint, and the protective paint is prepared through the following steps:

[0026] 1) 1 part by weight of benzotriazole, 1.5 parts by weight of maleic anhydride, 1.6 parts by weight of fatty alcohol polyoxyethylene polyoxypropylene ether, 2.1 parts by weight of polyethylene glycol, and 9 parts by weight of white latex are sequentially dropped into 26 parts by weight to remove In ionized water, stir evenly;

[0027] 2) Add 13 parts by weight of water-based alkyd resin, 1.3 parts by weight of diethylenetriamine, 0.8 parts by weight of ammonium dodecyl trimethyl ammonium sulfate, 0.8 parts by weight of sodium benzoate, and 2.6 parts by weight of acrylic acid, and continue to stir until fully Mix evenly to prepare a protective paint.

Embodiment 3

[0029] The container includes a metal box body, the surface of the metal box body is coated with a protective paint, and the protective paint is prepared through the following steps:

[0030] 1) 2 parts by weight of benzotriazole, 1.5 parts by weight of maleic anhydride, 1.6 parts by weight of fatty alcohol polyoxyethylene polyoxypropylene ether, 2.1 parts by weight of polyethylene glycol, and 9 parts by weight of white latex are successively dropped into 26 parts by weight to remove In ionized water, stir evenly;

[0031] 2) Add 13 parts by weight of water-based alkyd resin, 1.3 parts by weight of diethylenetriamine, 0.8 parts by weight of ammonium dodecyl trimethyl ammonium sulfate, 0.8 parts by weight of sodium benzoate, and 2.6 parts by weight of acrylic acid, and continue to stir until fully Mix evenly to prepare a protective paint.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a container. The surface of a metal box body of the container is coated with protective paint, and the protective paint is prepared through the following steps: 1) sequentially adding 1-2 parts of benzotriazole, 1.5 parts of maleic anhydride, 1.6 parts of fatty alcohol polyoxyethylene polyoxypropylene ether, 2.1 parts of polyethylene glycol and 9 parts of white latex into 26 parts of deionized water, and uniformly stirring; 2) then sequentially adding 13 parts of water-based alkyd resin, 1.3 parts of diethylenetriamine, 0.8 part of dodecyl trimethyl ammonium sulfate, 0.8 part of sodium benzoate, 2.6 parts of acrylic acid, continuing stirring till sufficient and uniform mixing to obtain the protective paint. The surface of the metal box body of the container is coated with the protective paint, so that long-time use of the container can be guaranteed.

Description

technical field [0001] The invention relates to a container. Background technique [0002] The anti-rust, anti-corrosion, anti-oxidation and weather resistance of the metal box of the existing container need to be improved, which affects the long-term use of the container. Contents of the invention [0003] The purpose of the present invention is to provide a container, the surface of the metal box is coated with protective paint, so that the metal box has excellent rust resistance, corrosion resistance, oxidation resistance, and weather resistance, thereby ensuring the long-term use of the container. [0004] In order to achieve the above object, the technical solution of the present invention is to design a container, including a metal box, the surface of the metal box is coated with a protective paint, and the protective paint is prepared by the following steps: [0005] 1) Put 1 to 2 parts by weight of benzotriazole, 1.5 parts by weight of maleic anhydride, 1.6 parts ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D5/08C09D7/12
CPCC08L2201/08C08L2205/025C08L2205/035C09D5/08C09D167/08C08L71/02C08K5/3475C08K5/098
Inventor 李学军
Owner SUZHOU FANRONG SPECIAL CONTAINER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com