Sizing technology of yarn of polyester-cotton-ramie blended fabric

A technology of blended fabrics and polyester-cotton linen, applied in textiles and papermaking, plant fibers, wear-resistant fibers, etc., can solve the problems of performance improvement, etc., and achieve the advantages of increased strength, good elongation performance, and close-fitting yarn hairiness Effect

Inactive Publication Date: 2017-02-15
成路凯尔服装(苏州)有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The warp yarns of fabrics such as cotton, viscose and synthetic fibers are mostly sizing before weaving; and the performance of the existing sizing solution needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The sizing process of polyester-cotton-linen blended fabric yarn comprises the following steps:

[0026] 1) Add 1 to 2 parts by weight of fatty alcohol polyoxyethylene ether, 1.6 parts by weight of polyacrylate, 1.2 parts by weight of ethyl acrylate, 1.4 parts by weight of sodium polyacrylate, and 12 parts by weight of phosphate modified starch into 30 parts by weight of deionized water, stir well;

[0027] 2) Add 2.2 parts by weight of alkanolamide polyoxyethylene ether, 0.8 parts by weight of sodium secondary alkyl sulfate, 1.2 parts by weight of sodium acetate, and 0.9 parts by weight of Phellodendron Phellodendri extract in turn, and continue to stir until fully mixed and evenly prepared. get slurry;

[0028] 3) Dip the yarn into the size solution for sizing, press off the remaining solution, and dry.

Embodiment 2

[0030] The sizing process of polyester-cotton-linen blended fabric yarn comprises the following steps:

[0031] 1) 1 part by weight of fatty alcohol polyoxyethylene ether, 1.6 parts by weight of polyacrylate, 1.2 parts by weight of ethyl acrylate, 1.4 parts by weight of sodium polyacrylate, and 12 parts by weight of phosphate modified starch were dropped into 30 parts by weight of deionized water in sequence, Stir well;

[0032] 2) Add 2.2 parts by weight of alkanolamide polyoxyethylene ether, 0.8 parts by weight of sodium secondary alkyl sulfate, 1.2 parts by weight of sodium acetate, and 0.9 parts by weight of Phellodendron Phellodendri extract in turn, and continue to stir until fully mixed and evenly prepared. get slurry;

[0033] 3) Dip the yarn into the size solution for sizing, press off the remaining solution, and dry.

Embodiment 3

[0035] The sizing process of polyester-cotton-linen blended fabric yarn comprises the following steps:

[0036] 1) Put 2 parts by weight of fatty alcohol polyoxyethylene ether, 1.6 parts by weight of polyacrylate, 1.2 parts by weight of ethyl acrylate, 1.4 parts by weight of sodium polyacrylate, and 12 parts by weight of phosphate modified starch into 30 parts by weight of deionized water, Stir well;

[0037] 2) Add 2.2 parts by weight of alkanolamide polyoxyethylene ether, 0.8 parts by weight of sodium secondary alkyl sulfate, 1.2 parts by weight of sodium acetate, and 0.9 parts by weight of Phellodendron Phellodendri extract in turn, and continue to stir until fully mixed and uniform. get slurry;

[0038] 3) Dip the yarn into the size solution for sizing, press off the remaining solution, and dry.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a sizing technology of a yarn of a polyester-cotton-ramie blended fabric. The sizing technology comprises the following steps: (1) sequentially adding 1 to 2 parts by weight of fatty alcohol polyoxyethylene ether, 1.6 parts by weight of polyacrylate, 1.2 parts by weight of ethyl acrylate, 1.4 parts by weight of sodium polyacrylate, and 12 parts by weight of phosphate modified starch into 30 parts by weight of deionized water, and evenly stirring; (2) then sequentially adding 2.2 parts by weight of alkyl alcohol amide polyethylene oxide, 0.8 part by weight of sodium sec-alkyl sulfate, 1.2 parts by weight of sodium acetate, and 0.9 part by weight of phellodendron extract, keeping on stirring until all components are fully and evenly mixed to obtain a slurry; and (3) soaking yarns into the slurry to carry out sizing, pressing the yarns to remove residual slurry, and drying the yarns. After sizing, fine hairs of yarns are tamed, the strength of yarns is prominently improved, the wear resistant property of the yarns is strong, and the elasticity maintaining performance of the yarns is good.

Description

technical field [0001] The invention relates to a sizing process of polyester-cotton-linen blended fabric yarn. Background technique [0002] The warp yarns of fabrics such as cotton, viscose and synthetic fibers mostly pass through sizing before weaving; and the performance of existing sizing liquid needs to be improved. Contents of the invention [0003] The object of the present invention is to provide a sizing process of polyester-cotton-linen blended fabric yarn. After sizing, the hairiness of the yarn is closely aligned, the strength is significantly improved, the wear resistance is good, and the yarn has good elongation retention. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of sizing process of polyester-cotton-linen blended fabric yarn, comprising the steps: [0005] 1) Add 1 to 2 parts by weight of fatty alcohol polyoxyethylene ether, 1.6 parts by weight of polyacrylate, 1.2 parts by weight of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/11D06M15/53D06M15/263D06M13/224D06M13/262D06M13/188D06M101/32D06M101/06
CPCD06M13/188D06M13/2246D06M13/262D06M15/11D06M15/263D06M15/53D06M2101/06D06M2101/32D06M2200/35D06M2200/40
Inventor 曹叙兴
Owner 成路凯尔服装(苏州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com