Ink repellent, negative photosensitive resin composition, partition wall and optical element

An optical element and partition wall technology, applied in the field of ink repellent, can solve the problems of reduced ink affinity of the opening, hindered uniform ink coating, difficult to remove the negative photosensitive resin composition, etc., and achieves sufficient storage stability, Good storage stability

Active Publication Date: 2018-05-25
ASAHI GLASS CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At this time, it is difficult to completely remove the negative photosensitive resin composition from the opening, and there are usually some residues in the opening.
Due to the existence of the residue of the negative photosensitive resin composition, the ink affinity of the opening is reduced, which hinders the uniform application of ink, which is a problem.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ink repellent, negative photosensitive resin composition, partition wall and optical element
  • Ink repellent, negative photosensitive resin composition, partition wall and optical element
  • Ink repellent, negative photosensitive resin composition, partition wall and optical element

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0416] Hereinafter, although this invention is demonstrated based on an Example, this invention is not limited to them. Examples 1, 2, 5-8, and Examples 10-16 are examples, and Examples 3, 4, 9, and Examples 17-19 are comparative examples.

[0417] Each measurement was performed by the following method.

[0418] [number average molecular weight (Mn), mass average molecular weight (Mw)]

[0419] The number average molecular weight (Mn) and the mass average molecular weight (Mw) were measured by gel permeation chromatography using polystyrene as a standard substance. As gel permeation chromatography, HPLC-8220GPC (manufactured by Tosoh Corporation) was used. As the column, a column obtained by connecting three Shodex LF-604 pieces was used. As a detector, an RI detector is used. As a standard substance, EasiCalPS1 (manufactured by Polymer Laboratories) was used. Furthermore, when measuring the number average molecular weight and mass average molecular weight, the column was...

example 1

[0463] (Example 1; Synthesis of Polymer (C1-1))

[0464] At 300cm equipped with a mixer 3 3.87 g of compound (cx-11), 13.30 g of compound (cx-21), 4.16 g of compound (cx-31), and 1.28 g of compound (cx-51) were added to a three-necked flask in a separate flask to obtain a hydrolyzable silane compound mixture. Next, 71.1 g of PGME was added to this mixture to prepare a raw material solution.

[0465] 6.30 g of 1% nitric acid aqueous solution was dripped at the obtained raw material solution. After the dropwise addition, it was stirred at 40° C. for 12 hours to obtain a PGME solution of the polymer (C1-1) (polymer (C1-1) concentration: 10% by mass, hereinafter also referred to as “polymer (C1-1) solution".).

[0466] It should be noted that after the completion of the reaction, the components of the reaction solution were measured using gas chromatography, and it was confirmed that each compound used as a raw material was below the detection limit.

[0467] Table 1 shows the...

example 2～4

[0468] (Examples 2-4: Synthesis of polymers (C1-2) and (Cf-1), (Cf-2))

[0469] Except that the raw material composition was set as shown in Table 1, the same procedure as Example 1 was performed, that is, PGME was added to the mixture of each silane compound shown in Table 1 to prepare a raw material solution, and the acid shown in Table 1 was added dropwise thereto. aqueous solution and stirred in the same manner as Example 1 to obtain solutions of polymer (C1-2) and (Cf-1), (Cf-2) (both compound concentration: 10% by mass, each solution is also referred to as "polymerization" hereinafter). Substance (C1-2), (Cf-1), (Cf-2) solution".).

[0470] Table 1 shows the feed amounts and molar ratios of the raw material hydrolyzable silane compounds used in the production of the polymers (C1-2) obtained above and (Cf-1) and (Cf-2). In Table 1, the silane compound means a hydrolyzable silane compound. In addition, the measurement results of the number average molecular weight (Mn), ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
particle diameteraaaaaaaaaa
amine valueaaaaaaaaaa
Login to View More

Abstract

To provide an ink repellent agent, a negative photosensitive resin composition containing the same, a partition wall having good ink repellency on the upper surface, and dots formed with high precision by uniformly applying ink to openings partitioned by the partition wall An optical element, wherein the photosensitive resin composition containing the ink repellent agent has sufficient storage stability, and the ink repellent agent can form a partition wall with good ink repellency on the upper surface and an opening with good ink affinity photosensitive resin composition. An ink repellent that imparts ink repellency to the upper surface of a partition formed in a shape that divides the surface of a substrate into a plurality of partitions for forming dots, the ink repellent It includes: a polymer having a unit containing a fluorine atom and a unit containing a blocked isocyanate group capable of generating an isocyanate group by deblocking by heating, and having a fluorine atom content of 1 to 40% by mass.

Description

technical field [0001] The present invention relates to an ink repellent, a negative photosensitive resin composition, a partition wall and an optical element. Background technique [0002] In the production of optical elements such as organic EL (Electro-Luminescence; electroluminescence) elements, a method of pattern printing by an inkjet (IJ) method using an organic layer such as a light emitting layer as dots may be used. In the above-mentioned method, a partition wall is provided along the contour of the dot to be formed, and ink containing an organic layer material is injected into a section (hereinafter also referred to as an "opening") surrounded by the partition wall to perform Drying, heating, etc., thereby forming dots of a desired pattern. [0003] In the above method, in order to prevent the mixing of ink between adjacent dots and uniformly apply ink during dot formation, it is necessary to have ink repellency on the upper surface of the partition wall, and the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01L51/50G03F7/004G03F7/075H05B33/22H05B33/12
CPCG03F7/004G03F7/075H05B33/12H05B33/22H10K50/00G03F7/027G03F7/028G03F7/0382
Inventor 山田光太郎
Owner ASAHI GLASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com