Agate-containing dark green glaze for ru-porcelain, processing method of glaze as well as ru-porcelain and firing method thereof

A technique of agate and Ru porcelain, applied in Ru porcelain and its firing, Ru porcelain agate blue-green glaze and its processing fields, can solve the problems such as the glaze smoothness and mechanical strength of Ru porcelain need to be improved, shorten the production cycle, and achieve a crisp sound. , smooth glaze effect

Active Publication Date: 2017-03-08
郭秀贞
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the glaze smoothness and mechanical strength of Ru porcelain using the above-mentioned Ru kiln agate glaze need to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The Ru porcelain agate cyan glaze of the present embodiment contains the following components by weight: 13 parts of Ru stone, 15 parts of agate stone, 40 parts of feldspar, 2 parts of calcite, 15 parts of wollastonite, 15 parts of chestnut wood ash, 8 parts of porphyrin 1 part, black bluestone 1 part.

[0042] The processing method of the Ru porcelain agate cyan glaze of the present embodiment may further comprise the steps:

[0043] 1) Put Ru stone and agate stone into a kiln and calcinate at 800°C for 3.5 hours, and then pulverize them respectively to obtain granular or powder Ru stone and agate stone;

[0044] 2) respectively pulverizing feldspar, calcite, wollastonite, talc, black bluestone and porphyrin to obtain granular or powdery stone;

[0045] 3) According to the weight ratio, take chestnut wood ash, the granular or powdery stone and agate stone obtained in step 1), and the granular or powdery stone materials obtained in step 2), mix them, add water ball mil...

Embodiment 2

[0048] The Ru porcelain agate cyan glaze of the present embodiment contains the following components in parts by weight: 6 parts of Ru stone, 1 part of agate stone, 70 parts of feldspar, 5 parts of calcite, 1 part of wollastonite, 2 parts of talc, and 1 part of porphyrin , 20 parts of black bluestone.

[0049] The processing method of the Ru porcelain agate cyan glaze of the present embodiment may further comprise the steps:

[0050] 1) Put Ru stone and agate stone respectively into the kiln for calcination at 850°C for 4 hours, and then pulverize them respectively to obtain granular or powder Ru stone and agate stone;

[0051] 2) respectively pulverizing feldspar, calcite, wollastonite, talc, black bluestone and porphyrin to obtain granular or powdery stone;

[0052] 3) According to the weight ratio, take the granular or powdery stones and agate stones obtained in step 1), and the granular or powdery stones obtained in step 2), mix them, add water and ball mill for 36 hours,...

Embodiment 3

[0055] The Ru porcelain agate cyan glaze of the present embodiment contains the following components by weight: 20 parts of Ru stone, 13 parts of agate stone, 10 parts of feldspar, 8 parts of calcite, 20 parts of wollastonite, 1 part of talc, and 8 parts of chestnut wood ash , 5 parts of porphyrin, 15 parts of black bluestone.

[0056] The processing method of the Ru porcelain agate cyan glaze of the present embodiment may further comprise the steps:

[0057] 1) Put the Ru stone and agate stone into the kiln for calcination at 900°C for 4 hours, and then pulverize them respectively to obtain granular or powder Ru stone and agate stone;

[0058] 2) respectively pulverizing feldspar, calcite, wollastonite, talc, black bluestone and porphyrin to obtain granular or powdery stone;

[0059] 3) According to the weight ratio, take chestnut wood ash, the granular or powdery stone and agate stone obtained in step 1), and the granular or powdery stone materials obtained in step 2), mix ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to agate-containing dark green glaze for ru-porcelain, a processing method of the glaze as well as the ru-porcelain and a firing method thereof and relates to the technical field of silicate ceramics. The agate-containing dark green glaze for the ru-porcelain is prepared from components in parts by weight as follows: 6-20 parts of ru jade, 1-15 parts of agate, 10-70 parts of feldspar, 2-8 parts of calcite, 1-20 parts of wollastonite, 0-2 parts of talc, 0-15 parts of chest wood ash, 1-8 parts of ammolite and 1-20 parts of black bluestone. The enamel of the ru-porcelain fired with the adoption of the agate-containing dark green glaze for the ru-porcelain takes dark green as a base, can present the deep and full sky blue, azure, light greenish blue, bluish white, pale blue and bright green and can present bright and transparent pea green and onion green color. The ru-porcelain adopting the agate-containing dark green glaze for the ru-porcelain has good jade sense and opalescence effects and has a smoother glaze surface, higher mechanical strength, lower water absorption rate and high firing qualification rate.

Description

technical field [0001] The invention relates to the technical field of silicate ceramics, in particular to a Ru porcelain agate green glaze and a processing method thereof, as well as a Ru porcelain and a firing method thereof. Background technique [0002] Ru kiln, named for its location in Ruzhou, was the first of the five famous kilns of Ru, Ge, Guan, Ding and Jun in the Song Dynasty in my country. Flow, its glaze is thick and full of sound, bright but not glaring", has the typical characteristics of "green as sky, beautiful as jade, cicada's wings split, full glaze wraps feet, nails burnt". However, due to historical reasons, the Ru Kiln was only fired for more than 20 years. The firing time was very short, the output was limited, and it was rarely circulated. In the Southern Song Dynasty, it was "very rare". More than ten pieces have become rare treasures. [0003] In the prior art, when firing Ru porcelain, the glaze used is generally obtained by grinding feldspar, qu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/14C03C1/04C04B41/86C04B35/622C04B35/64
CPCC03C1/04C03C8/14C04B35/622C04B41/5022C04B41/86C04B2235/658C04B2235/661C04B2235/96C04B2235/963C04B41/4535
Inventor 张天庆张颖政张颖裕郭秀贞
Owner 郭秀贞
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap