Water permeable brick prepared from sulfuric acid waste residue and preparation method of water permeable brick

A technology of sulfuric acid waste slag and permeable bricks, which is applied in applications, household appliances, clay products, etc., can solve the problems of unsatisfactory water permeability and strength, uneven pores, etc., achieve good ecological and environmental protection performance, good water permeability, and reduce energy consumption Effect

Inactive Publication Date: 2017-03-15
阳泉市鑫盛瓷业有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the technical problems that existing permeable bricks have mostly closed or semi-closed pores, uneven pores, unsatisfactory water permeability and strength, and provide a permeable brick prepared by using sulfuric acid waste slag and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A permeable brick prepared by using sulfuric acid waste residue in this embodiment is made of the following raw materials in parts by weight: 60 parts of sulfuric acid waste residue pellets with a particle size of 6-30 mesh, sulfuric acid waste residue particles with a particle diameter of 30-60 mesh 35 parts of material, 10 parts of clay and 5 parts of sintering agent.

[0015] A kind of method utilizing sulfuric acid waste residue to prepare described permeable brick, comprises the following steps:

[0016] 1) Raw material screening: use a vibrating sieve to screen the sulfuric acid waste residue to obtain pellets with a particle size of 6-30 mesh and 30-60 mesh; process the clay into a powder with a particle size of less than 180 mesh;

[0017] 2) Mixing: Stir and mix 60 parts of sulfuric acid waste slag pellets with a particle size of 6-30 mesh, 35 parts of sulfuric acid waste slag pellets with a particle diameter of 30-60 mesh, 10 parts of clay powder and 5 parts o...

Embodiment 2

[0021] A permeable brick prepared by using sulfuric acid waste slag in this embodiment is made of the following raw materials in parts by weight: 65 parts of sulfuric acid waste slag pellets with a particle size of 6-30 mesh, sulfuric acid waste slag particles with a particle size of 30-60 mesh 40 parts of material, 20 parts of clay and 10 parts of sintering agent.

[0022] A kind of method utilizing sulfuric acid waste residue to prepare described permeable brick, comprises the following steps:

[0023] 1) Raw material screening: use a vibrating sieve to screen the sulfuric acid waste residue to obtain pellets with a particle size of 6-30 mesh and 30-60 mesh; process the clay into a powder with a particle size of less than 180 mesh;

[0024] 2) Mixing: Stir and mix 65 parts of sulfuric acid waste slag pellets with a particle size of 6-30 mesh, 40 parts of sulfuric acid waste slag pellets with a particle diameter of 30-60 mesh, 20 parts of clay powder and 10 parts of sintering...

Embodiment 3

[0028] A permeable brick prepared by using sulfuric acid waste residue in this embodiment is made of the following raw materials in parts by weight: 62 parts of sulfuric acid waste residue pellets with a particle diameter of 6-30 mesh, sulfuric acid waste residue pellets with a particle diameter of 30-60 mesh 38 parts of material, 16 parts of clay and 7 parts of sintering agent.

[0029] A kind of method utilizing sulfuric acid waste residue to prepare described permeable brick, comprises the following steps:

[0030] 1) Raw material screening: use a vibrating sieve to screen the sulfuric acid waste residue to obtain pellets with a particle size of 6-30 mesh and 30-60 mesh; process the clay into a powder with a particle size of less than 180 mesh;

[0031] 2) Mixing: Stir and mix 62 parts of sulfuric acid waste slag pellets with a particle size of 6-30 mesh, 38 parts of sulfuric acid waste slag pellets with a particle diameter of 30-60 mesh, 16 parts of clay powder and 7 parts...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention specifically relates to a water permeable brick prepared from sulfuric acid waste residue and a preparation method of the water permeable brick. The water permeable brick, meeting the standard of GB / T28993-2010, is prepared from the locally abundant sulfuric acid waste residue and a local clay sintering agent through the working procedures of sieving, mixing, forming, drying, sintering and the like. The particles of the sulfuric acid waste residue in the raw materials are in the range of 6 to 120 meshes, so that the working procedure of breaking is not needed, the water permeable brick can be directly used after sieving, the energy consumption is reduced, the production cost is reduced, and the sintered clinker is extremely suitable for producing the water permeable brick by adopting a particle stacking method, the waste residue is fully utilized, and the environmental pollution is reduced. The water permeable brick prepared from the sulfuric acid waste residue is high in strength, high in water permeable performance, antifreeze and skid-resistant, and has high ecological environmental protection performance. The water permeable brick can be widely applied to the buildings such as plazas, urban roads, residential districts and parking lots. The construction of sponge cities is proposed by our country at present, and a large quantity of water permeable bricks are needed, so that the market prospect is wide.

Description

technical field [0001] The invention belongs to a permeable brick and a preparation method thereof, in particular to a permeable brick prepared by using sulfuric acid waste residue and a preparation method thereof. Background technique [0002] Permeable brick is a new century environmental protection building material product that was born to solve urban surface hardening, create a high-quality natural living environment, and maintain urban ecological balance. This product has the characteristics of maintaining the water permeability and moisture retention of the ground, non-slip, high strength, cold resistance, weather resistance, noise reduction, and sound absorption. It uses slag waste and waste ceramics as raw materials and is molded twice, which is a green and environmentally friendly product. [0003] At present, there are two methods of producing sintered permeable bricks at home and abroad: one is the method of adding pore-forming agents, which uses carbon particle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B38/00
CPCC04B33/132C04B38/0003Y02P40/60
Inventor 郑晋贤
Owner 阳泉市鑫盛瓷业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap