Imitated activated pigment printing adhesive copolymer and preparation method thereof

A pigment printing and adhesive technology, which is applied in dyeing, textiles and papermaking, etc., can solve the problems affecting product stability and use effect, hard hand feeling, hydrolysis, etc., and achieve excellent rubbing fastness, hand feeling, and stability Good resistance, not easy to hydrolyze

Inactive Publication Date: 2017-03-15
SHANGHAI ARGUS NEW MATERIAL CO LTD
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the heat resistance, solvent resistance and weather resistance of the polyacrylate coating film are poor, and there are disadvantages such as high hardness, cold and brittle hot stickiness, etc. The fabric treated with this type of adhesive has poor rubbing fastness, hard hand feeling, Formaldehyde release and other issues
[0004] In order to solve the shortcomings of polyacrylate adhesives, many researchers have carried out organosilicon modification, as disclosed in the publication number CN105601799 A core / shell type organosilicon modified acrylate emulsion and its preparation method and application. The organosilicon monomer used is γ-methacryloxypropyltrimethoxysilane. The organosilicon monomer has a small molecular weight, which can make up for the structural shortcomings of polyacrylate to a certain extent, but it does not help to improve the feel. In addition, the Si-O-C bond in this structure is easily hydrolyzed, which affects product stability and use effect
Publication No. CN 103526595 A discloses an imitation active pigment printing adhesive and its preparation method. The silane coupling agent KH-570 used is easily hydrolyzed after being polymerized with acrylate. The modification of methacrylamide improves the hydrolysis of acrylate, but the Si-O-C in the product will still be hydrolyzed, affecting the stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Imitated activated pigment printing adhesive copolymer and preparation method thereof
  • Imitated activated pigment printing adhesive copolymer and preparation method thereof
  • Imitated activated pigment printing adhesive copolymer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] In a more preferred embodiment, the preparation method of imitation reactive pigment printing binder copolymer of the present invention comprises following preferred steps:

[0026] 1) Combine organosilicon containing unsaturated carbon-carbon double bonds, soft monomers containing unsaturated carbon-carbon double bonds, hard monomers containing unsaturated carbon-carbon double bonds, functional monomers capable of bonding with cellulose, and Stir the organic carboxylic acid with saturated carbon-carbon double bond evenly at room temperature, add the emulsifier with a weight fraction of 50-70% (to the weight of the whole emulsifier), and the deionized water with a weight fraction of 50% (to the weight of the whole deionized water) to mix , and heated to 50-60°C, emulsified for 30 minutes to obtain pre-emulsion A;

[0027] 2) the cross-linking monomer containing three or four-C=C-double bond structure, the weight fraction is 10% (to all deionized water weight) deionized ...

Embodiment 1

[0061] 1) 1 part by weight of tetramethyldivinyldisiloxane, 2 parts by weight of vinyl-terminated polydimethylsiloxane (viscosity of 100000mPa·s), 1 part by weight of methyl-vinylsiloxane, 5 parts by weight of n-butyl acrylate, 5 parts by weight of ethyl acrylate, 15 parts by weight of isobutyl acrylate, 5 parts by weight of methyl methacrylate, 2 parts by weight of vinyl acetate, 2 parts by weight of styrene, 0.5 parts by weight of methyl Mix acrylic acid evenly, add 0.9 parts by weight of sodium lauryl sulfate, 1.8 parts by weight of isomeric tridecyl alcohol polyoxyethylene ether (EO number is 8), 27 parts by weight of deionized water, stir, and heat up to 50-60 °C , emulsified for 30 minutes to obtain 68.2 parts by weight of pre-emulsion A;

[0062] 2) 0.5 parts by weight of ditrimethylolpropane tetraacrylate, 5.4 parts by weight of deionized water, 0.3 parts by weight of sodium lauryl sulfate, 0.6 parts by weight of isomeric tridecyl alcohol polyoxyethylene ether (EO numb...

Embodiment 2

[0067] 1) 2 parts by weight of vinyl tris(trimethylsiloxane) silane, 3 parts by weight of vinyl terminated polydimethylsiloxane (viscosity of 100000mPa·s), 13 parts by weight of isooctyl acrylate, 5 parts by weight of ethyl acrylate, 5 parts by weight of lauryl acrylate, 5 parts by weight of methyl methacrylate, 2 parts by weight of vinyl acetate, 2 parts by weight of acrylonitrile, 0.5 parts by weight of styrene benzene sulfonic acid, mixed evenly, adding 1.2 parts by weight Parts of sodium secondary alkyl sulfonate, 2.4 parts by weight of fatty alcohol polyoxyethylene ether (AEO-9), 26.5 parts by weight of deionized water, stirred, heated to 50-60°C, and emulsified for 30 minutes to obtain 67.6 parts by weight of pre-emulsion A ;

[0068] 2) Mix 0.5 parts by weight of pentaerythritol tetraacrylate, 5.3 parts by weight of deionized water, 0.4 parts by weight of sodium secondary alkyl sulfonate, and 0.8 parts by weight of fatty alcohol polyoxyethylene ether (AEO-9), stir and e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an imitated activated pigment printing adhesive copolymer and a preparation method thereof. The copolymer is prepared from 5-25 wt% of organosilicone copolymerization units containing unsaturated carbon-carbon double bonds, 15-35 wt% of hard monomer copolymerization units containing unsaturated carbon-carbon double bonds, 45-70 wt% of soft monomer copolymerization units containing unsaturated carbon-carbon double bonds, 0.5-5 wt% of crosslinking monomer copolymerization units, 0.5-5 wt% of functional monomer copolymerization units capable of being bonded with cellulose and 0.5-5 wt% of organic carboxylic acid copolymerization units containing unsaturated carbon-carbon double bonds based on the total weight of the imitated activated pigment printing adhesive copolymer. The adhesive product is not likely to be hydrolyzed and good in stability, has excellent crockfastness and hand feeling and achieves an imitated activated pigment printing effect.

Description

technical field [0001] The invention belongs to the technical field of textile auxiliaries, and in particular relates to an environmental-friendly imitation active pigment printing adhesive copolymer and a preparation method thereof. Background technique [0002] Pigment printing refers to the process of using adhesives to adhere paint that has no affinity and reactivity to fabrics on fabrics. Pigment printing only needs to fix the color without washing, which can significantly shorten the process flow, save energy and reduce emissions. Therefore This process is widely adopted by the printing and dyeing industry. [0003] Polyacrylate emulsion is cheap and easy to obtain, and has excellent coating performance, and has been widely used in the field of pigment printing. However, the heat resistance, solvent resistance and weather resistance of the polyacrylate coating film are poor, and there are disadvantages such as high hardness, cold and brittle hot stickiness, etc. The f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/12C08F220/18C08F230/08C08F220/14C08F218/08C08F212/08C08F220/06C08F222/20C08F220/32C08F222/14C08F220/46C08F2/26C08F2/30D06P1/52D06P1/38
CPCD06P1/38D06P1/5257C08F2/26C08F2/30C08F220/18C08F283/124C08F220/1804C08F220/1808C08F212/08C08F222/205C08F220/14C08F220/1806C08F230/08
Inventor 姬海涛李正雄
Owner SHANGHAI ARGUS NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap