A method for preparing tetrabasic lead sulfate

A tetrabasic lead sulfate and concentrated sulfuric acid technology, applied in lead sulfate, lead-acid batteries, final product manufacturing, etc., can solve the problems of large crystal particles, shortened preparation reaction time, unevenness, etc., and achieves high preparation rate and shortening Agitation mixing time, smaller and uniform effect of particle size

Active Publication Date: 2018-10-30
ZHEJIANG DOULAN INTELLIGENT EQUIP CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the existing defects of the above-mentioned tetrabasic lead sulfate preparation method, provide a kind of method for preparing tetrabasic lead sulfate, adopt the method that the lead material after premixing is directly reacted with sulfuric acid, make full use of concentrated sulfuric acid The heat generated by the exothermic reaction makes the reaction kettle heat up rapidly, thereby shortening the preparation reaction time. The reaction product is rapidly cooled by compressed air, which further effectively inhibits the growth of 4BS crystal particles, and the formed 4BS particle size is small and uniform and controllable, which effectively solves the problem. In the prior art, due to the high reaction temperature and long reaction time in the preparation of tetrabasic lead sulfate, the technical problems of the reaction product crystal particles are large and uneven

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing tetrabasic lead sulfate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0034] Embodiments of the invention are described in detail below, examples of which are illustrated in the accompanying drawings. The embodiments described below by referring to the figures are exemplary and are intended to explain the present invention and should not be construed as limiting the present invention.

[0035] In the present invention, unless otherwise specified, the raw materials used can be purchased from the market or commonly used in the field. The processes in the following examples are conventional methods in the field unless otherwise specified.

[0036] Refer to the attached figure 1 A method for preparing tetrabasic lead sulfate in this embodiment is described. Accurately weigh the lead powder raw material, wherein the lead powder raw material in the present invention is one or more of lead powder, lead oxide, and lead sulfate for lead-acid storage battery production, and calculate lead oxide and free lead according to the oxidation degree of lead powd...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing tetrabasic lead sulfate, which comprises the following steps: A. Prepare the reaction, send the pre-mixed lead material into the reaction kettle, and carry out internal circulation stirring while adding sulfuric acid solution into the reaction kettle After uniformity, feed compressed air into the reaction kettle to cool the lead slime; B. Ball milling reaction, transport the lead slime in step A to a drying ball milling device, and perform drying and ball milling simultaneously to obtain a tetrabasic lead sulfate product. The present invention adopts the method of directly reacting the premixed lead material with sulfuric acid, makes full use of the heat generated by the exothermic reaction of concentrated sulfuric acid to rapidly heat up the reactor, thereby shortening the preparation reaction time, and the reaction product is rapidly cooled by compressed air, further Effectively inhibit the 4BS crystal particles from becoming larger, and the formed 4BS has a small and uniform particle size, which effectively solves the problem in the prior art that the reaction product crystal particles are large and uneven due to the high reaction temperature and long reaction time for the preparation of tetrabasic lead sulfate. technical problem.

Description

technical field [0001] The invention relates to the field of preparation of lead-acid battery materials, in particular to a method for preparing tetrabasic lead sulfate. Background technique [0002] Recently, in the production of lead-acid batteries, in order to prolong the cycle life of the battery, one of the most effective measures is to use a lead paste with a high content of tetrabasic lead sulfate, and the abbreviation of tetrabasic lead sulfate is 4BS, and 4BS as the crystal nucleus The addition of 4BS can control the amount and grain size of the formed 4BS, which overcomes the problem of high-content and large-grain 4BS plate formation, and the battery has excellent discharge performance. [0003] Chinese invention patent 201310281747.4 discloses a preparation method of tetrabasic lead sulfate, including the following steps: A. Weighing the sample, B. Hydrothermal reaction, C. Ball milling, D. Vacuum drying, E. Post-treatment and other steps. The present invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G21/20H01M10/12
CPCC01G21/20H01M10/12Y02E60/10Y02P70/50
Inventor 钱顺荣法俊卿钱梦飞
Owner ZHEJIANG DOULAN INTELLIGENT EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com